One-Step synthesis of the pine-shaped nanostructure of aluminum nitride and its photoluminescence properties

An array of pine-shaped nanostructures of aluminum nitride (AlN) was synthesized through direct reaction between Al vapor and nitrogen gas in direct current (DC) arc discharge plasma without any catalyst or template. The as-prepared nanostructure consists of many pine-needle-shaped leaves with conical shape tips. The structure, morphology, and optical property of the nanostructure have been characterized by X-ray powder diffraction, energy-dispersive X-ray spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, Raman spectroscopy, and photoluminescence. A possible growth mechanism of the pine-shaped nanostructure was discussed. Two factors were found to be essential for branched nanostructure growth, i.e., the reaction time and N2 pressure. The photoluminescence spectrum of the nanostructure of AlN revealed an intense emission band, suggesting that there may be potential applications in electronic and optoelectronic nanodevices.

Three-dimensional AlN microroses and their enhanced photoluminescence properties

Novel three-dimensional AlN microroses, for the first time, have been synthesized via direct reaction between Al and N2 in arc plasma without any catalyst and template.

Hydrothermal synthesis of V0.13Mo0.87O2.935 nanowires with strong blue photoluminescence

Hexagonal V0.13Mo0.87O2.935 nanowires were hydrothermally synthesized at 220 °C for the first time. X-ray diffraction and field-emission scanning electron microscopy were utilized to characterize the phase and morphology of the nanowires, respectively. Transmission electron microscopy and selected area electron diffraction indicate that the nanowires are single crystalline, growing along the [001] direction. Interestingly, the nanowires easily become amorphous under the electron irradiation. The comparative hydrothermal experiments show that the molar ratio between the starting reagents of Mo and NH4VO3 plays a vital role in the anisotropic growth of nanowires. The photoluminescence measurement demonstrates that these nanowires exhibit two strong emission peaks at 420 and 438 nm, which are probably related to the intrinsic oxygen vacancies.