An electrochemical impedance study of ionic liquid film formation and aqueous corrosion of magnesium alloy ZE41

Ionic liquid surface treatments are proposed as a method of controlling corrosion processes on magnesium alloys. An important magnesium alloy, ZE41 (nominally 4% Zn and 1% rare earth), was treated with the ionic liquid trihexyl(tetradecyl)phosphonium diphenylphosphate (P₆₆₆₁₄DPP). Impedance spectra were acquired at intervals during the treatment, indicating the development of a film and allowing a measure of the film formation process to be obtained over time. Mechanically polished and electro-polished surfaces were prepared; these surfaces, treated and untreated, were subsequently exposed to 0.1 M NaCl aqueous solutions. The corrosion behavior of the prepared surfaces were assessed using impedance spectroscopy and optical microscopy. The results indicated a significant role for the method of surface preparation used and, in both cases, the ionic liquid treatment produced a more corrosion-resistant surface.

Use of electrochemical impedance spectroscopy for study of CO2 corrosion prevention by batch treatment inhibitor films

Electrochemical impedance spectroscopy (EIS) was used to study and evaluate commercial batch treatment inhibitors which are used for protecting oil wells, gas wells, and pipelines from CO2 corrosion, focusing on the evaluation of inhibitor film persistency. It was found that theformation and deterioration of batch treatment inhibitor films were accompanied by typical impedance spectral changes. During the formation of inhibitor films, electrode impedance showed a rapid increase and the Bode phase angle plots also showed a sudden change. Thus, the formation of inhibitor film was a very fast process. During the deterioration of inhibitor films, electrode impedance showed a gradual decrease and the Bode phase angle plots showed changes which characterised the three stages of the inhibitor film deterioration process. The relationships between EIS and corrosion rate are discussed, including comparisons with weight loss measurements. Based on the experimental findings in the present work, a method is suggested for estimating the persistency of inhibitor films by monitoring the characteristic changes in the Bode phase angle plots and by measuring electrochemical charge transfer resistance at the second and third stages of the inhibitor film deterioration process.

Electrochemical impedance spectroscopy and surface characterization techniques to study carbon dioxide corrosion product scales

Electrochemical impedance spectroscopy (EIS) was used to study carbon dioxide (CO2) corrosion product scales and their effects on further CO2 corrosion. Objectives were to determine the suitability of EIS for studying corrosion scales and to investigate the influence of environmental factors on scale formation. EIS provided useful information about protective abilities and electrochemical properties of corrosion scales. CO2 corrosion scales formed at high-temperature and pressure provided better protection than those formed at low-temperature and pressure. The level of protection of the scale formed at higher temperature and pressure increased with exposure time. EIS results were compared with coupon weight-loss measurements. Scales were analyzed using a combination of Fourier transform infrared (FTIR) analysis, x-ray diffraction (XRD), and electron microscopy.

Studies of CO2 corrosion product scales using electrochemical impedance spectroscopy and surface characterisation techniques

Electrochemical impedance spectroscopy (EIS) was used to study carbon dioxide (CO2) corrosion product scales and their effects on further CO2 corrosion. Objectives were to determine the suitability of EIS for studying corrosion scales and to investigate the influence of environmental factors on scale formation. EIS provided useful information about protective abilities and electrochemical properties of corrosion scales. CO2 corrosion scales formed at high-temperature and pressure provided better protection than those formed at low-temperature and pressure. The level of protection of the scale formed at higher temperature and pressure increased with exposure time. EIS results were compared with coupon weight-loss measurements. Scales were analyzed using a combination of Fourier transform infrared (FTIR) analysis, x-ray diffraction (XRD), and electron microscopy

Studying the cathodic disbondment of coatings using electrochemical impedance spectroscopy

The disbondment of protective organic coatings is a widely reported pipeline coating failure mode in the oil and gas industry. Traditional methods of evaluating cathodic disbondment of pipeline coatings are based on visual inspection of pipeline conditions, and laboratory testing of cathodic disbondment resistance (CDR) using standard methods such as ASTM G8. Although some other laboratory-based techniques, such as scanning kelvin probe and scanning acoustic microscopy have been used to study the cathodic disbondment (CD) of coatings, these are often difficult to apply in practical testing. Over the past decade, electrochemical impedance spectroscopy (EIS) has been employed as a potential method for measuring CD. This paper reports preliminary results from an EIS study designed to characterise CD behaviour of epoxy coatings under excessive cathodic protection. EIS data correlated well with the area of disbonded coating. Analysis of EIS data can provide valuable information on the initiation and rates of CD.

Electrochemical impedance spectroscopy as a tool to measure cathodic disbondment on coated steel surfaces: capabilities and limitations

The disbondment of protective organic coatings under excessive cathodic protection potentials is a widely reported coating failure mechanism. Traditional methods of evaluating cathodic disbondment are based on ex situ visual inspection of coated metal surfaces after being exposed to standard cathodic disbondment testing conditions for a long period of time. Although electrochemical impedance spectroscopy (EIS) has been employed as an effective means of evaluating various anti-corrosion properties of organic coatings; its application for assessing the cathodic disbondment resistance of coatings has not been sufficiently exploited. This paper reports an experimental study aimed at developing EIS into a tool for in situ measurement and monitoring of cathodic disbondment of coatings. A clear correlation between EIS parameters and the disbonded coating areas has been confirmed upon short term exposure of epoxy-coated steel electrodes to cathodic disbondment conditions; however the degree of this correlation was found to decrease with the extension of exposure duration. This observation suggests that EIS loses its sensitivity with the propagation of coating disbondment, and that in order to achieve quantitative determination of the coating cathodic disbondment localized EIS measurements are required to measure the parameters related to local disbonded areas.

Communication - an approach to measuring local electrochemical impedance for monitoring cathodic disbondment of coatings

An electrochemically integrated multi-electrode array has been used for monitoring and visualizing the cathodic disbondment of
defective coatings by measuring local electrochemical impedance. Compared with the conventional electrochemical impedance and
local current measurement approaches, this new approach significantly enhances the sensitivity of detecting the propagation of
coating disbondment by eliminating the effects of the dominating low impedance regions, such as those that arise at coating defects,
and thus increases the visibility of higher impedance regions deep in the disbonded coating. Furthermore, it facilitates the probing
of electrode processes and mechanisms in selected local electrode regions.

The corrosion inhibition mechanism of new rare earth cinnamate compounds — electrochemical studies

A combination of linear polarisation resistance (LPR) and cyclic potentiodynamic polarisation (CPP) measurements demonstrated that the lanthanum-4 hydroxy cinnamate compound could inhibit both the cathodic and anodic corrosion reactions on mild steel surfaces exposed to 0.01 M NaCl solutions. However, the dominating response was shown to vary with inhibitor concentration. At the concentrations for which the highest level of protection was achieved, both REM-4 hydroxy cinnamate (REM being lanthanum and mischmetal) displayed a strong anodic behaviour for mild steel and their inhibition performance, including their resistance against localised attack, improved with time.

Electrochemical impedance spectroscopy (EIS) measurements and modelling were carried out so as to propose a simple electrical model and correlate the extracted parameters to the inhibition mechanism put forward for REM-cinnamate based compounds. The results supported the high corrosion inhibition performance of the compounds as well as the build-up of a protective film with time. Based on a two-layer model the results suggested that the upper layer of the inhibitor film seemed to offer less resistance to the diffusion of electrochemically active species than the highly resistive inner layer at the film/metal interface.

Corrosion properties of plasma-polymerized methylcyclohexane films using electrochemical methods

Three types of methylcyclohexane (MCH) coating were deposited as interlayer dielectrics on copper using plasma-enhanced chemical vapor deposition (PECVD) at three different RF plasma power levels. The coating performance was then evaluated by an electrochemical im pedance spectroscopy (EIS) and a potentiodynamic polarization test in 3.5 wt.% NaCl solution. An atomic force microscopy (AFM) and Fourier transform infrared reflection (FT-IR) spectroscopy were also conducted to analyze the coatings. The MCH coatings showed a lower corrosion rate than the copper substrate in the potentiodynamic tests. The EIS results showed that the corrosion resistance of the coatings increased with an increasing plasma power. Thus, the MCH films with an increasing plasma power improved the corrosion resistance due to the formation of a low-porosity coating, the enhanced formation of C−H, C−C, and C≡C stretching configurations, and the improved smooth surfaces.

Electrochemical behavior of CrN coating for polymer electrolyte membrane fuel cell

CrN films on a bipolar plate in polymer electrolyte membrane fuel cells have several advantages owing to their excellent corrosion resistance and mechanical properties. Three CrN samples deposited at various radio frequency (RF) powers by RF magnetron sputtering were evaluated under potentiodynamic, potentiostatic and electrochemical impedance spectroscopy conditions. The electrochemical impedance spectroscopy data were monitored for 168 h in a corrosive environment at 70 °C to determine the coating performance at +600 mV_SCE under simulated cathodic conditions in a polymer electrolyte membrane fuel cell. The electrochemical behavior of the coatings increased with decreasing RF power. CrN films on the AISI 316 stainless steel substrate showed high protective efficiency and charge transfer resistance, i.e. increasing corrosion resistance with decreasing RF power. X-ray diffraction confirmed the formation of a CrN(200) preferred orientation at low RF power.

Electrochemical and physicochemical properties of small phosphonium cation ionic liquid electrolytes with high lithium salt content

Electrolytes of a room temperature ionic liquid (RTIL), trimethyl(isobutyl)phosphonium (P111i4) bis(fluorosulfonyl)imide (FSI) with a wide range of lithium bis(fluorosulfonyl)imide (LiFSI) salt concentrations (up to 3.8 mol kg−1 of salt in the RTIL) were characterised using a combination of techniques including viscosity, conductivity, differential scanning calorimetry (DSC), electrochemical impedance spectroscopy (EIS), nuclear magnetic resonance (NMR) and cyclic voltammetry (CV). We show that the FSI-based electrolyte containing a high salt concentration (e.g. 1:1 salt to IL molar ratio, equivalent to 3.2 mol kg−1 of LiFSI) displays unusual transport behavior with respect to lithium ion mobility and promising electrochemical behavior, despite an increase in viscosity. These electrolytes could compete with the more traditionally studied nitrogen-based ionic liquids (ILs) in lithium battery applications.