Dynamic softening of ferrite during large strain warm deformation of a plain-carbon steel

The evolution of dynamic ferrite softening in a plain-carbon steel was investigated by torsion tests during warm deformation at 810 °C, in the two-phase (ferrite + austenite) region, and strain rate of 0.1 s−1 with different strains up to 50. The warm flow behaviour and ferrite microstructural parameters, such as grain size, misorientation angle across ferrite/ferrite boundaries, and the fraction of high-angle and low-angle grain/subgrain boundaries were quantified using electron back scatter diffraction. The results show that with increasing strain up to not, vert, similar2, the ferrite grain size and fraction of high-angle boundaries rapidly decrease and the fraction of low-angle boundaries increases. However, these parameters remain approximately unchanged with increasing strain from not, vert, similar2 to 50. The dynamic softening mechanism observed during large strain ferritic deformation is explained by dynamic recovery and continuous dynamic recrystallization.

Texture and substructure development during post-dynamic softening in Ni-30%Fe austenite

The texture and substructure development during post-dynamic annealing of an austenitic Ni-30%Fe model alloy after complete dynamic recrystallization was investigated using electron back-scattered diffraction (EBSD) and transmission electron microscopy (TEM). A novel mechanism of metadynamic softening is proposed based on the experimental investigation of the grain structure, crystallographic texture and dislocation substructure evolution. The initial softening stage involved rapid growth of the dynamically formed nuclei and migration of the mobile boundaries. The subboundaries within DRX grains progressively disintegrated through dislocation climb and dislocation annihilation, which ultimately led to the formation of dislocation-free grains, while the grain boundary migration gradually became slower. As a result, the DRX texture was largely preserved throughout the annealing process.

The mechanism of metadynamic softening in austenite after complete dynamic recrystallization

A novel mechanism of post-dynamic softening during annealing of a fully dynamically recrystallized (DRX) austenitic Ni–30Fe alloy is proposed. The initial softening stage involves rapid growth of the dynamically formed nuclei and migration of the mobile boundaries. The sub-boundaries within DRX grains progressively disintegrate through dislocation climb and dislocation annihilation, which ultimately leads to the formation of dislocation-free grains, and the grain boundary migration gradually becomes slower. As a result, the DRX texture largely remains preserved throughout the annealing process.

A mechanical approach to quantify dynamic recrystallization in polycrystalline metals

A new method is proposed to quantify progress of dynamic recrystallization in polycrystalline metals during deformation. This approach utilises the stress–strain curve of the material to quantify the progress of dynamic softening. The outcome of this method showed a good agreement with experimental results for alloys of this study.

Microstructure evolution and softening processes occurring during annealing of hot deformed Ni-30Fe austenite

The current work investigates the microstructure evolution and softening processes that take place during annealing of an austenitic Ni-30Fe model alloy subjected to hot deformation in the dynamic recrystallization (DRX) regime. The substructure of the deformed matrix grains largely comprised organized microband arrays, though that of the DRX grains consisted of more random, complex subgrain/cell arrangements. This substructure disparity was also reflected by the distinct difference in the mechanism of post-deformation softening taking place during annealing of the deformed matrix and DRX grains. In the former, the recrystallization process took place through nucleation and growth of new grains fully replacing the deformed structure, as expected for the classical static recrystallization (SRX). The corresponding texture was essentially random, in contrast to that of the DRX grains dominated by low Taylor factor components. The microbands originally present within the deformed matrix grains displayed some tendency to disintegrate during annealing, nonetheless, they remained largely preserved even at prolonged holding times. During annealing of the fully DRX microstructure, a novel softening mechanism was revealed. The initial post-dynamic softening stage involved rapid growth of the dynamically formed nuclei and migration of the mobile boundaries in correspondence with the well-established metadynamic recrystallization (MDRX) mechanism. However, in contrast to the deformed matrix, SRX was not observed and the sub-boundaries within DRX grains rapidly disintegrated through dislocation climb and dislocation annihilation, which led to the formation of dislocation-free grains already at short holding times. Consequently, the DRX texture initially became slightly weakened and then remained largely preserved throughout the annealing process.

Texture evolution and softening processes in an austenitic Ni-30Fe alloy subjected to hot deformation and subsequent annealing

The current work has investigated the texture development in an austenitic Ni-30Fe model alloy during deformation within the dynamic recrystallization (DRX) regime and after post-deformation annealing. Both the deformed matrix and DRX texture displayed the expected FCC shear components, the latter being dominated by the low Taylor factor grains, which was presumably caused by their lower consumption rate during DRX. The deformed matrix grains were largely characterized by organized, microband structures, while the DRX grains showed more random, complex subgrains/cell arrangements. The latter substructure type proved to be significantly less stable during post-deformation annealing. The recrystallization of the deformed matrix occurred through nucleation and growth of new grains fully replacing the deformed structure, as expected for the classical static recrystallization (SRX). Unlike the DRX grains, the SRX texture was essentially random. By contrast, a novel softening mechanism was revealed during annealing of the fully DRX microstructure. The initial post-dynamic softening stage involved rapid growth of the dynamically formed nuclei and migration of the mobile boundaries in line with the well-established metadynamic recrystallization (MDRX) mechanism, which weakened the starting DRX texture. However, in parallel, the sub-boundaries within the deformed DRX grains progressively disintegrated through dislocation climb and dislocation annihilation, which ultimately led to the formation of dislocation-free grains. Consequently, the weakened DRX texture largely remained preserved throughout the annealing process.

Hyaluronic acid–collagen network interactions during the dynamic compression and recovery of cartilage

A compression cell designed to fit inside an NMR spectrometer was used to investigate (i) the in situ dynamic strain response and structural changes of the internal pore network, and (ii) the diffusion and flow of interstitial water, in full thickness cartilage samples as they were mechanically deformed under a constant compressive load (pressure) and then allowed to recover (swell again) when the load was removed. Selective enzymatic digestion of the collagen fibril network and the glycopolysaccharide hyaluronic acid (HA) was performed to mimic some of the structural and compositional changes associated with osteoarthritis. Digestion of collagen gave rise to mechanical ‘dynamic softening’ and—perhaps more importantly—nearly complete loss in the ability to recover through swelling, both effects due to the disruption of the hierarchical structure and fibril interconnectivity in the collagen network which adversely affects its ability to deform reversibly and to properly regulate the pressurization and resulting rate and direction of interstitial fluid flow. In contrast, digestion of HA inside the collagen pore network caused the cartilage to ‘dynamically stiffen’ which is attributed to the decrease in the osmotic (entropic) pressure of the digested HA molecules confined in the cartilage pores that causes the network to contract and thereby become less permeable to flow. These digestioninduced changes in cartilage’s properties reveal a complex relationship between the molecular weight and concentration of the HA in the interstitial fluid, and the structure and properties of the collagen fibril pore network, and provide new insights into how changes in either could influence the onset and progression of osteoarthritis.

The microstructure evolution and softening processes during high-temperature deformation of a 21Cr-10Ni-3Mo duplex stainless steel

The austenite and ferrite microstructure evolution and softening mechanisms have been investigated in a 21Cr-10Ni-3Mo duplex stainless steel, containing about 60% austenite, deformed in torsion at 1200°C using a strain rate of 0.7 s-1. The above experimental conditions led to the formation of a small volume fraction of new austenite grains through discontinuous dynamic recrystallization (DDRX), which could not account for the observed large softening on the flow curve. DDRX grains mainly formed through the strain-induced migration of the pre-existing austenite grain boundaries, known to dominate in single-phase austenite, complemented by subgrain growth in the interface regions with ferrite. A significant portion of austenite dynamic softening has been attributed to the large-scale subgrain coalescence, the extent of which increased with strain, which seems to have contributed substantially to the observed flow stress decrease. The above process thus appears to represent an alternative mode of austenite dynamic softening to the classical DDRX in the duplex austenite/ferrite microstructure, characterised by limited availability of the pre-existing austenite/austenite high-angle boundaries, deformed at a high temperature. The softening mechanism within ferrite has been classified as "continuous DRX", characterised by a gradual increase in misorientations between neighbouring subgrains with strain and resulting in the progressive conversion of subgrains into "crystallites" bounded partly by low-angle and partly by large-angle boundaries.

Characterization on ferrite microstructure evolution during large strain warm torsion testing of plain low carbon steel

Ferrite grain/subgrain structures evolution during the extended dynamic softening of a plain low carbon steel was investigated throughout the large strain warm deformation by hot torsion. Microstructural analysis with electron back-scattering diffraction (EBSD) scanning electron microscope (FEG/SEM) was carried out on the ferrite microstructural parameters. The results showed that the warm flow stress–strain curves are similar to those affected only by dynamic softening and an extended warm flow softening is seen during large strain deformation up to 30. Furthermore, with an increase in strain up to ~ vert, similar1 the grain size of ferrite, misorientation angle and fraction of high-angle boundaries gradually decrease and fraction of low-angle boundaries increases. With a further increase in the strain beyond ~, vert, similar2, these parameters remain approximately unchanged. No evidence of discontinuous dynamic recrystallisation involving nucleation and growth of new grains was found within ferrite. Therefore, the dynamic softening mechanism observed during large strain ferritic deformation is explained by continuous dynamic recrystallization (CDRX).

Substructure and texture development in austenite through thermomechanical processing

The data collection was performed using EBSD and TEM techniques. The objective was to characterise the substructure and crystallographic texture development during dynamic and post-dynamic deformation. The work reveals the role of the initial dislocation structure and texture on the softening characteristics in austenite and how these evolve during softening. It is also shown that the differences in the deformation dislocation structures between the dynamically recrystallized and deformed regions play a major role in determining the extent of recovery. An enhanced static recovery can be seen during post dynamic softening.

The static, dynamic and metadynamic recrystallisation of a medium carbon steel

Grain refinement during and after hot isothermal deformation of a medium carbon steel has been investigated. The average austenite grain size decreased with an increase in strain for the hot deformed and recrystallised material, with refinement extending beyond the strain for the peak stress. A window of strain that corresponds to transition from classical static to metadynamic recrystallisation was observed in respect to the recrystallised material. Within this post-dynamic transition window the strain at which strain independent softening occurs was different for different volume fractions of the recrystallised material. This led to a new terminology corresponding to initiation of strain independent softening. For the alloy of this study, strain independent softening for the start of post-deformation recrystallisation occurred near the strain to the peak stress. The strain corresponding to complete metadynamic recrystallisation, which was defined as when all levels of recrystallisation were strain independent, was much greater than the strain for the peak stress.

An analysis of the transition between strain dependent and independent softening in austenite

The post-deformation softening behaviour of austenite has been studied for various compositions and deformation conditions. The strain at which the transition from strain dependent to strain independent post-deformation softening behaviour occurs (ε*) has been found to coincide closely with the strain to the peak stress (εp) under certain conditions but not under others. It has been proposed that the relationship between ε* and εp may be described geometrically using the initial grain size and the dynamically recrystallised grain size.

Correlation between the deformation and post-deformation softening behaviours in hot worked Austenite

The relation between the deformation and post-deformation softening behaviours of austenite is examined in a 304 stainless steel. This correlation has been exploited in the modelling of hot rolling and it is argued here that the key to this understanding lies in the deformation structure. The latter is characterized in the present work by the fraction of dynamic recrystallization. The value of this fraction at the peak in the flow stress curve is found to decrease with increasing stress (i.e. with decreasing temperature and increasing strain rate). By contrast, the fraction of dynamic  recrystallization at the strain corresponding to the point where  post-deformation softening becomes strain independent is found to be constant. These observations are used to explain the nature of the important difference between the flow curve peak and the onset of strain independent post-deformation softening.

Softening mechanisms in two duplex stainless steels deformed in hot torsion

The aim of the present work was to undertake a detailed investigation of the softening mechanisms during hot deformation of a 21Cr-10Ni-3Mo (steel A) and a 21Cr-8Ni-3Mo (steel B) austenite/ferrite duplex stainless steels containing about 60% and 30% of austenite, respectively. The steels were subjected to hot deformation in torsion performed at 900 ºC and 1200 ºC using a strain rate of 0.7 s-1 to several strain levels. Quantitative optical and transmission electron microscopy were used in the investigation. Austenite was observed to soften via dynamic recovery (DRV) and dynamic recrystallisation (DRX) accompanied by DRV for the deformation temperatures of 900 °C and 1200 °C, respectively, for the both steels studied. DRX of austenite largely occurred through strain-induced grain boundary migration, complemented by (multiple) twinning, and developed significantly faster in steel A than in steel B, indicating that considerably larger strains partitioned into austenite in the former steel during deformation at 1200 °C. The above softening mechanism was accompanied by the formation of DRX grains from subgrains along the austenite/ferrite interface and by large-scale subgrain coalescence. At 900°C, stressassisted phase transitions between austenite and ferrite were observed, characterised by dissolution of the primary austenite, formation of Widmanstätten secondary austenite and gradual globularisation of the microstructure with increasing strain. These processes appeared to be significantly more widespread in steel B. The softening mechanism within ferrite for the both steels studied was classified as “continuous DRX”, characterised by a gradual increase in misorientations between neighbouring subgrains with strain, for the both deformation temperatures.