Assessment of delamination in composite beams using shear horizontal (SH) wave mode

Interaction of Lamb waves with structural damage can lead to wave mode conversion. In this study, the shear horizontal (SH) wave, from the mode conversion of the fundamental symmetric Lamb wave (S0), was used for quantitative identification of delamination in composite beams, based on advanced signal processing using an inverse approach. SH wave propagation under various delamination conditions in CF/EP beams made of orthotropic plain woven fabrics was simulated, and signal characteristics were extracted in terms of the concept of digital damage fingerprints (DDF). With the aid of an artificial neural algorithm, the relation between the DDF of delamination-scattered SH mode and damage parameters was calibrated, whereby the occurrence, location and size of delamination in the composite beams were assessed. The approach was experimentally validated, and the results demonstrate the effectiveness of SH mode for quantitative damage evaluation of composite structures.

Mode II delamination toughness of Z-pinned laminates

Mode II delamination toughness of z-pin reinforced composite laminates is investigated using finite element (FE) method. The z-pin pullout process is simulated by the deformation and breakage of non-linear springs. A critical shear stress criterion based on linear elastic fracture mechanics is used to simulate crack growth in an end-notched-flexure (ENF) beam made of z-pinned laminates. The mode II toughness is quantified by the potential energy release rate calculated using the contour integral method. This FE model is verified for an unpinned ENF composite beam. Numerical results obtained indicate that z-pins can significantly increase the mode II delamination toughness of composite laminate. The effects of design variables on the toughness enhancement of z-pinned laminates are also studied, which provides an important technological base and useful data to optimize and improve the z-pinning technique.

Melding: a new alternative to adhesive bonding

Melding, a novel method for joining composites is examined in this paper. The method uses Quickstep ™ technology to retain partially cured areas of a composite laminate, enabling subsequent bonding operations. The effect of melding on the mechanical properties of the composite has been investigated. Flexural testing of HexPly 914 indicates consistent properties throughout a melded section. Flexural strength values of 1.36±O.03 GPa compared to 1.35±O.03 GPa for a standard laminate were recorded. In order to achieve sufficient bond strength, the portion of the composite to be joined must have a significant proportion of uncured matrix. The ability of Hexply 914 prepreg to retain sufficient bonding potential to form a strong joint was also investigated. HexPly 914 Lap Shear results indicated no significant variation in strength values between co-cured and melded joins, with a recorded
strength value of 15.0±0. 7 MPa.

A family of simple and robust finite elements for linear and geometrically nonlinear analysis of laminated composite plates

A family of simple, displacement-based and shear-flexible triangular and quadrilateral flat plate/shell elements for linear and geometrically nonlinear analysis of thin to moderately thick laminate composite plates are introduced and summarized in this paper.

The developed elements are based on the first-order shear deformation theory (FSDT) and von-Karman’s large deflection theory, and total Lagrangian approach is employed to formulate the element for geometrically nonlinear analysis. The deflection and rotation functions of the element boundary are obtained from Timoshenko’s laminated composite beam functions, thus convergence can be ensured theoretically for very thin laminates and shear-locking problem is avoided naturally.

The flat triangular plate/shell element is of 3-node, 18-degree-of-freedom, and the plane displacement interpolation functions of the Allman’s triangular membrane element with drilling degrees of freedom are taken as the in-plane displacements of the element. The flat quadrilateral plate/shell element is of 4-node, 24-degree-of-freedom, and the linear displacement interpolation functions of a quadrilateral plane element with drilling degrees of freedom are taken as the in-plane displacements.

The developed elements are simple in formulation, free from shear-locking, and include conventional engineering degrees of freedom. Numerical examples demonstrate that the elements are convergent, not sensitive to mesh distortion, accurate and efficient for linear and geometric nonlinear analysis of thin to moderately thick laminates.

Effect of manufacturing method and aging environment on painted automotive carbon fibre composite surfaces

In this paper, the effect of various aging environments on the painted surface finish of unidirectional carbon fibre composite laminates, manufactured by autoclave and a novel out-of-autoclave technique was investigated. Laminates were exposed to water immersion, 95 % relative humidity and cyclic environments for 552 h and the surface finish was evaluated using visual and wave-scan distinctness of image (DOI) techniques. It was found that the laminate surface finish was dependent on the amount of moisture in the aging test. Minor surface waviness occurred on the laminates exposed to the cyclic test, whereas, surface waviness, print through and DOI values were all significantly higher as the laminates absorbed larger quantities of moisture from the hygrothermal and hydrothermal tests. The water immersion test, which was the most detrimental to the surface finish of the painted laminates, produced dense blistering on the autoclave manufactured laminate surface whereas the out-of-autoclave laminate surface produced only a few. It was found that the out-of-autoclave laminate had high substrate surface roughness which resulted in improved paint adhesion and, therefore, prevented the formation of surface blistering with aging. © 2012 Springer Science+Business Media Dordrecht.

Hygrothermal effects on painted carbon fibre composite surfaces

In this article, the effect of hygrothermal aging on the painted surface finish of unidirectional and fabric carbon fibre composite laminates, with and without surfacing film was investigated. The results highlighted the importance of ensuring that the composite surface directly beneath the paint layer is made from a uniform material with a consistent thickness in order to minimise surface defects from occurring during aging. The surfacing film was found to minimise the print through development on the painted unidirectional and twill composite surfaces. However, the surfacing film layer was found to intermingle with the carbon fibre plies during cure, which resulted in an uneven film thickness that caused increased levels of orange peel. The twill laminate painted surface produced high levels of print through and surface waviness that was caused by the large resin rich regions located within the tow intersections at the surface which enlarged due to thermal expansion and swelling of the matrix with hygrothermal aging. It was also noted that the small resin rich regions between the individual carbon fibres on the unidirectional composite surface were sufficiently large to print through the painted surface.

Rapidly cured out-of-autoclave laminates: understanding and controlling the effect of voids on laminate fracture toughness

Voids are one of the most significant defects found within composites and have been demonstrated to reduce the performance of composite structures. The understanding of the impact of the size and distribution of voids on laminate properties is still limited because voids have proven difficult to deliberately control. This study aims to understand the mechanisms by which voids are generated within out-of-autoclave cured laminates. In this study, a process of prepreg conditioning was developed to control the level of voids within test laminates. Non-conditioned laminates highlighted signs of void growth (1.5%), while conditioned laminates showed consistently low levels of voids (<0.3%). Mass spectrometry indicated higher levels of aqueous and solvent volatiles within the non-conditioned prepreg. Finally, Mode II fracture testing revealed a 21% improvement in toughness for the non-voided laminates. A model on the effect of voids within the Mode II stress state has also been proposed.

Rapidly cured epoxy/anhydride composites: effect of residual stress on laminate shear strength

The drive towards rapid cure thermosetting composites requires a better understanding of the residual stresses that develop during curing. This study investigates the impact of residual stresses on the interlaminar shear strength of resin-infused epoxy/anhydride carbon-fibre laminates. The magnitude of the residual stress was varied by changing the initial injection cure temperature between 75 °C and 145 °C. The corresponding cycle times and the final glass transition temperature of the resin were also measured. The experimentally measured chemical shrinkage and thermal expansion properties of the resin after vitrification were used as inputs to a finite element analysis to calculate the peak residual stresses in the composite. An increase in the initial cure temperature from 85 to 135 °C resulted in an increase of 25% in the residual stress, which led to an experimentally measured reduction in the composite's short beam shear strength of approximately 16% (8 MPa), in good agreement with model prediction.