Effect of substructure characteristics on the dislocation annihilation process during post-deformation annealing

Two distinct substructures were produced in a Ni-30Fe austenitic model alloy by different thermomechanical processing routes. The first substructure largely displayed organized, banded subgrain arrangements with alternating misorientations, resulting from the deformation at a strain just before the initiation of dynamic recrystallization (DRX). By contrast, the second substructure was more random in character and exhibited complex subgrain/cell arrangements characterized by local accumulation of misorientations, formed through DRX. During the post-deformation annealing, the latter substructure revealed a rapid disintegration of dislocation boundaries leading to the formation of dislocation-free grains within a short holding time, though the former largely preserved its characteristics till becoming replaced by growing statically recrystallized grains.

Effect of crystallization on corrosion resistance of Cu52.5Ti30Zr11.5Ni6 bulk amorphous alloy

The effects of crystallization on the corrosion resistance of a  Cu52.5Ti30Zr11.5Ni6 bulk amorphous alloy in 1 mol/L HCl, and 6 mol/L NaOH solutions were studied. The amorphous alloy was identified by  differential thermal analysis(DSC) and by X-ray diffraction(XRD). The partially and fully crystallized alloys were prepared by controlling the annealing  temperatures at 738 and 873 K for 1 and 12 min, respectively, and the corrosion resistances of those annealed alloys were compared with that of the amorphous alloy by immersion test and potentiodynamic measurements in 1 mol/L HCl and 6 mol/L NaOH solutions. The results show that the  partially crystallized alloy exhibits high corrosion resistance, whereas full crystallization results in deteriorated corrosion resistance compared with that of the as-cast amorphous alloy.

Effect of relaxation on pressure sensitivity index in a Zr-based metallic glass

Shear-banding features of as-cast and annealed Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5 bulk metallic glass were investigated through Rockwell indentation tests. Isothermal annealing of the as-cast samples was conducted at temperatures below its glass transition temperature, Tg. The exothermal enthalpy during continuous heating below Tg decreases with increasing annealing temperature, indicating the gradual reduction of free-volume upon annealing. The observation on the morphology of shear-banding pattern around the indents implies a reduced shear bands activity in the annealed samples. The included angles (2θ) between two families of shear bands emanating from the edge of Rockwell indent decrease from 88° for the as-cast sample to 79° for the sample annealed at 633 K for 1 h, indicating a pressure sensitive plasticity. By Mohr–Coulomb criterion, the pressure sensitive index can be obtained on the basis of the measured 2θ, which increases with increasing annealing temperature, indicating an increase of “atomistic friction” due to the reduction of the free volume upon annealing.

Effect of initial processing on the microstructure-property relationships in bake-hardened C-Mn-Si TRIP steels

The effect of pre-straining (PS) and bake-hardening (BH) on the microstructure and mechanical properties has been studied in C-Mn-Si TRansformation Induced Plasticity (TRIP) steels after: (i) thermomechanically processing (TMP) and (ii) intercritical annealing. The steels were characterised before and after PS/BH by transmission electron microscopy (TEM), X-ray diffraction (XRD), and tensile tests. The main microstructural differences were the higher volume fraction of bainite and more stable retained austenite in the TMP steel. This led to a difference in the strain-hardening behavior before and after BH treatment. The higher dislocation density in ferrite and formation of microbands in the TMP steel after PS and the formation of Fe3C carbides between the bainitic ferrite laths during BH for both steels also affected the strain-hardening behavior. However, both steels after PS/BH treatment demonstrated an increase in the yield and tensile strength.

Effect of grain size on deformation twinning behaviour of high MN steel

The effect of grain size on the mechanical properties and deformation twinning behaviour in high manganese steel was investigated. In order to generate different grain sizes, the samples were subjected to hot rolling, cold rolling and annealing. Room temperature tensile testing of the steel with different grain sizes (5-50 µm) indicated the occurrence of twinning induced plasticity (TWIP) in all the samples. Also, changes in work-hardening behaviour accompanied changes in the grain size. The results are discussed in terms of the enhanced sensitivity of twinning to the grain size.

Effect of pre-straining and bake hardening on the microstructure and mechanical properties of CMnSi trip steels

The effects of pre-straining and bake hardening on the mechanical behaviour and microstructural changes were studied in two CMnSi TRansformation-Induced Plasticity (TRIP) steels with different microstructures after intercritical annealing. The TRIP steels before and after pre-straining and bake hardening were characterised by X-ray diffraction, optical microscopy, transmission electron microscopy, three dimensional atom probe and tensile tests. Both steels exhibited discontinuous yielding behaviour and a significant strength increase with some reduction in ductility after pre-straining and bake hardening treatment. The following main microstructural changes are responsible for the observed mechanical behaviours: a decrease in the volume fl:action of retained austenite, a increase in the dislocation density and the formation of cell substructure in the polygonal ferrite, higher localized dislocation density in the polygonal ferrite regions adjacent to martensite or retained austenite, and the precipitation of fine iron carbides in bainite and martensite. The mechanism for the observed yield point phenomenon in both steels after treatment was analysed.

Effect of bake-hardening on the structure-property relationship of multiphase steels for the automotive industry

The effect of a bake-hardening (BH) treatment on the microstructure and mechanical properties has been studied in C-Mn-Si TRansformation Induced Plasticity (TRIP) and Dual Phase (DP) steels after: (i) thermomechanical processing (TMP) and (ii) intercritical annealing (IA). The steels were characterized using X-ray diffraction, transmission electron microscopy (TEM) and three-dimensional atom probe tomography (APT). All steels showed high BH response. however, the DP and trip steels after IA/BH showed the appearance of upper and lower yield points, while the stress-strain behavior of the trip steel after TMP/BH was still continuous. This was due to the higher volume fraction of bainite and more stable retained austenite in the TMP/BH steel, the formation of plastic deformation zones with high dislocation density around the "as-quenched” martensite and “TRIP” martensite in the IA/BH DP steel and IA/BH TRIP steel, respectively.

Effect of structure relaxation on the plastic deformation behaviour in a Zr-based BMG under indenter

Vickers and nano indentations were performed on a structurally relaxed Zr₄₁Ti₁₄Cu_12.5Ni₁₀Be_22.5 bulk metallic glass (BMG), and the evolution of the shear bands in the relaxed BMG was investigated and compared to that in the as-cast alloy. Results indicate that the plastic deformation in the BMG with structure relaxation is accommodated by the semicircular (primary) and radial (secondary) as well as tertiary shear bands. Quantitatively, the shear band density in the relaxed alloy was much lower than that in the as-cast alloy. The annihilation of free volume caused by the annealing was responsible for the embrittlement of the sample with structure relaxation.

Effect of pre-straining and bake hardening on the microstructure and mechanical properties of CMnSi trip steels

The effects of pre-straining and bake hardening on the mechanical behaviour and microstructural changes were studied in two CMnSi TRansformation-Induced Plasticity (TRIP) steels with different microstructures after intercritical annealing. The TRIP steels before and after pre-straining and bake hardening were characterised by X-ray diffraction, optical microscopy, transmission electron microscopy, three dimensional atom probe and tensile tests. Both steels exhibited discontinuous yielding behaviour and a significant strength increase with some reduction in ductility after pre-straining and bake hardening treatment. The following main microstructural changes are responsible for the observed mechanical behaviours: a decrease in the volume fraction of retained austenite, an increase in the dislocation density and the formation of cell substructure in the polygonal ferrite, higher localized dislocation density in the polygonal ferrite regions adjacent to martensite or retained austenite, and the precipitation of fine iron carbides in bainite and martensite. The mechanism for the observed yield point phenomenon in both steels after treatment was analysed.

Effect of orientation stability on recrystallization textures of deformed aluminium single crystals

High purity Al single crystals of the Cube (0 0 1)[1 0 0] and rotated Cube (0 1 1)[0 1 ¯ 1] orientations have been deformed in plane strain compression in a channel die. Deformation was carried out at temperatures between 25 and 600 8C up to strains of 1.2. The as-deformed microstructure has been characterised using electron microscopy and electron backscattered diffraction (EBSD).
Annealing was carried out for various times and temperatures. The recrystallized microstructure has been studied using electron microscopy, and the orientation of recrystallized grains determined using EBSD. After cold deformation and annealing both orientations exhibited a random recrystallization texture component. After hot deformation both orientations retained a similar annealing texture to their starting deformation texture. The annealing texture of deformed single crystals was found to be more sensitive to the temperature of deformation than the stability of the orientation.

Thermo-mechanical processing and the shape memory effect in an Fe–Mn–Si-based shape memory alloy

The effect of cold rolling and annealing on the shape memory effect (SME) in an Fe–Mn–Si-based alloy has been studied. It has been found
that the SME in these alloys can be significantly increased by the appropriate thermo-mechanical processing (TMP). The optimum conditions
were found to be 15% cold rolling followed by annealing at 800 ◦C for 15 min. This produced a total strain recovery of 4.5%. TEM showed that
this processing schedule produces a microstructure of evenly spaced, and well defined stacking faults throughout the parent phase. It is shown for
the first time that samples processed in this way produce a larger fraction of martensite compared to samples in the as-austenitized condition. It
is concluded that the stacking faults induced by TMP act as nucleation sites for martensite formation during deformation. The SME is improved
primarily as a result of the increased amount of martensite that is formed in this condition.

Effect of NbC and TiC precipitation on shape memory in an iron-based alloy

This paper examines the effects of TiC and NbC precipitation and prior cold rolling on the shape memory behaviour of an iron-based alloy. A precipitate-free alloy was used as a reference to investigate the relative contributions of prior-deformation and precipitation on shape memory. Heat treatment of the Nb- and Ti-containing alloys at 700 °C and 800 °C resulted in carbide precipitates between 120 nm and 220 nm in diameter. Bend testing of these samples showed a marginal increase in shape memory compared to the precipitate-free alloy. Under these conditions TiC precipitation exhibited slightly better shape memory than for NbC. However, this small increase was over-shadowed by the marked increase in shape memory that can be produced by subjecting the alloys to cold rolling followed by recovery annealing. When processed in this way, fine carbides are formed in the Ti- and Nb-containing alloys during the heat treatment. For particles >25 nm in diameter the shape memory is unaffected, but, it was found that small <5 nm particles have a detrimental effect on shape memory due to pinning of the martensite plates, thereby inhibiting their reversion to austenite. The optimum shape memory was observed in the precipitate-free alloy after cold rolling and recovery annealing.

Martensite/particle interactions and the shape memory effect in an Fe–Mn–Si-based alloy

The effect of carbide precipitates with a size range of 30–300 nm on the austenite to martensite transformation has been studied. Such particles are known to enhance shape memory, and it was the aim of this work to clarify how the particles exert a favourable effect on shape memory. Differential scanning calorimetry revealed that the presence of particles increases the amount of thermally induced martensite. X-ray diffraction showed that the presence of particles increases the amount of stress-induced martensite also. Surface-relief produced on a pre-polished surface by bending deformation showed that the particle-containing samples exhibited a more complex and highly tilted surface-relief indicative of the formation of a larger volume fraction of martensite. The reversion characteristics of the particle-containing and solution-treated samples were similar: both showed co-reversion of multiple variants of martensite within the same volume of microstructure. However, a higher volume fraction of martensite reverted for the particle-containing sample on recovery annealing. The increased density of nucleation sites for martensite formation and a higher volume fraction of stress-induced martensite for a given strain are therefore considered to be the main contributions of relatively coarse carbide particles to the improvement of shape memory performance.

Effect of isothermal dissolution and re-precipitation of austenite on the mechanical properties of duplex structures

The hot deformation behaviour of a duplex ferritic/austenitic stainless steel was studied after different deformation conditions. The results showed a strange and interesting behaviour in the strength of the material during post-deformation studies. For most deformation conditions, the flow stress of the material was un-expectedly increased after annealing of deformed structures. This phenomenon implied that microstructural hardening occurred in the material during the interpass annealing rather than the expected softening. Also, an interesting change was observed where the morphology of the austenite phase changed from stringers or layers of austenite to a widmanstätten structure. The microstructural studies suggest that the austenite was dissolved and re-precipitated during the annealing process and the hardening was mostly associated with the change in the morphology of austenite.