Using titania photocatalysts to degrade toluene in a combined adsorption and photocatalysis process

Three types of titania supported materials including titanium dioxide and silicon dioxide composite, titania-coated activated carbon and titania-coated glass beads were prepared and used as photocatalysts to remove toluene from an air stream. Their surface areas were analysed. TEM image reveals titania-silica composites were nanostructured aggregates. XRD was used to determine their crystalline phase which was 100% anatase for the titania component. A fixed bed reactor was designed and built in the laboratory, the toluene with initial concentration of 300 ppm (1149 mg/m³) was fed into the reactor, the destruction efficiencies of toluene were determined by the gas analyser. It was also found that TiO₂-SiO₂ aggregates with high surface area (421.1 m²/g) achieved high destruction efficiencies. The combined effects of adsorption and photocatalysis were further studied by comparing the performance of pure activated carbon (surface area of 932.4 m²/g) and TiO₂ coated activated carbon with BET surface area of 848.4 m²/g. It was found that the TiO₂ coated activated carbon demonstrated comparable results to pure activated carbon, and most importantly, the TiO₂-coated activated carbon can be effectively regenerated by UV irradiation, and was reused as adsorbent. The experimental result of titania-coated glass beads demonstrated a steady degradation efficiency of 15% after a period of 17 hours. It helped to understand that photocatalysis degradation ability of the TiO₂ was constant regardless of the adsorption capacity of the catalysts. This photocatalytic property can be used to degrade the adsorbed toluene and regenerate the catalyst. This study revealed that if the experiments were designed to use adsorption to remove toluene and followed by regeneration of adsorbent using photocatalysis, it could achieve a very high removal efficiency of toluene and reduce the regeneration cost of saturated adsorbent.

Synthesis and characterization of silver nanoparticles and titanium oxide nanofibers : toward multifibrous nanocomposites

A new method was investigated to produce new multiscale fibrous nanocomposites comprised of titanium oxide (TiO₂) nanofibers and silver (Ag) nanoparticles (NPs). The process involved electrospinning TiO₂ precursor solution containing colloidal solution of Ag NPs, and organic solvent (dimethyl-n′n-formamide) to fabricate a porous, nonwoven, free-standing nanofiber mesh. Postprocess heating of the electrospun nanofibers entailed calcination in air environment at 500°C for 3 h. Microemulsion processing was used to generate NPs of Ag in a monodispersed distribution throughout the colloidal solution. X-ray diffraction data were consistent with the anatase phase of TiO2, while transmission electron microscopy and hydrogen desorption measurements revealed a very porous microstructure. It was demonstrated that NP colloidal stability is solvent dependent. It is anticipated that incorporation of metal particles in nanofibers will lead to enhanced photocurrent generation, when used in functional devices.

Nanocrystalline titanium to mesoporous anatase with high bioactivity

In present study, the formation of bioactive anatase on bulk titanium (Ti) by hybrid surface mechanical attrition treatment (SMAT) is reported. A commercial pure Ti plate first underwent SMAT in a vacuum for 1 h to produce a nanocrystalline layer with a thickness of about 30 µm, and then the nanocrystalline Ti (30 nm) was transformed into mesoporous anatase with a grain size 10 nm by chemical oxidation and calcination. The mesoporous anatase showed excellent bioactivity while being soaked in simulated body fluid, which could be attributed to the unique nanostructure on the SMAT Ti surface.

Morphology evolution during annealing and electrical conductivity of titania nanotube films

Titania nanotube films were produced by anodization of titanium foil. The titania nanotube films were annealed at different temperatures. Morphology evolution, phase transformation and electrical conductivity of the titania nanotubes were studied. Results showed that the nanotube walls became rough, porous and even collapsed after annealed at 400, 500 and 600°C respectively. Titania anatase phase formed after annealed at 400°C; the amount of anatase phase increased as the annealing temperature increased. The conductivity of the nanotube film annealed at 400°C was improved greatly compared with the conductivity of the as-anodized nanotube film. However, the conductivity of the nanotube films annealed at higher temperatures decreased. The effect of the morphology on the electronic conductivity of the titania nanotube films was discussed.

Photocatalytic degradation of phenanthrene on soil surfaces in the presence of nanometer anatase TiO2 under UV-light

The effect of nanometer anatase TiO2 was investigated on the photocatalytic degradation of phenanthrene on soil surfaces under a variety of conditions. After being spiked with phenanthrene, soil samples loaded with different amounts of TiO2 (0 wt.%, 1 wt.%, 2 wt.%, 3 wt.%, and 4 wt.%) were exposed to UV-light irradiation for 25 hr. The results indicated that the photocatalytic degradation of phenanthrene followed the pseudo first-order kinetics. TiO2 significantly accelerated the degradation of phenanthrene with the half-life reduced from 45.90 to 31.36 hr for TiO2 loading of 0 wt.% and 4 wt.%, respectively. In addition, the effects of H2O2, light intensity and humic acid on the degradation of phenanthrene were investigated. The degradation of phenanthrene increased with the concentration of H2O2, light intensity and the concentration of humic acids. It has been demonstrated that the photocatalytic method in the presence of nanometer anatase TiO2 was a very promising technology for the treatments of soil polluted with organic substances in the future.