Crystallographic analysis of nano-structured bainitic steels

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200 and 350°C bainitic transformation temperatures. The microstructure was consisted of bainitic ferrite lath and retained austenite for both heat treatment conditions. The crystallographic analysis revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with their parent austenite. The isothermal bainite transformation temperature has a significant effect on the retained austenite characteristics and the variant selection of the bainitic ferrite laths. In general, a decrease in the isothennal bainite transformation temperature refined the bainitic structure and weakened the variant selection.

Understanding of the bainite transformation in a nano-structured bainitic steel

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200°C for 10 days to form a nano-scale bainitic microstructure consisting of nanobainitic ferrite laths with high dislocation density and retained austenite films. The crystallographic analysis using TEM and EBSD revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with the parent austenite. There was only one type of packet identified in a given transformed austenite grain. Each packet consisted of two different blocks having variants with the same habit plane, but different crystallographic orientations. The presence of fine C-rich clusters and Fe-C carbides with a wide range of compositions in bainitic ferrite was revealed by Three-dimensional Atom Probe Tomography (APT). The high carbon content of bainitic ferrite compared to the para-equilibrium level of carbon in ferrite, absence of segregation of carbon to the austenite/bainitic ferrite interface and absence of partitioning of substitutional elements between the retained austenite and bainitic ferrite were also found using APT.

Sex reversal in Nile tilapia (Oreochromis niloticus Linnaeus) by androgen immersion

Two experiments were conducted to investigate the efficacy of three androgens applied through immersion treatments on the sex ratio of Nile tilapia (Oreochromis niloticus L.) fry. In experiment 1, 14 days post-hatching (DPH) larvae were exposed to a single immersion treatment in 17α-methyltestosterone (MT), 17α-methyldihydrotestosterone (MDHT) or 17α-ethynyltestosterone (ET) at 200, 600 and 1800 μg L⁻¹ over 4 h (130 larvae per treatment). In experiment 2, Nile tilapia larvae were exposed to the higher androgen concentration (1800 μg L⁻¹) applied as either a single immersion (14 DPH) or double immersion (10 and 14 DPH) over 4 h (125 larvae per treatment). Change in sex proportion within each experiment as well as between experiments was analysed by the chi-square test. In experiment 1, MT, MDHT and ET were equally effective in significantly increasing the proportion of males when applied at 1800 μg L⁻¹ (86.0%, 90.0% and 86.7% respectively). At 200 μg L⁻¹ none of the androgens altered sex ratio. At 600 μg L⁻¹, only MDHT slightly, but significantly skewed the sex ratio towards males (73.0%). In experiment 2, a single immersion treatment at 14 DPH (1800 μg L⁻¹) significantly increased the proportion of males, but at this time the response was significantly hormone dependent (MDHT, 100.0%; MT, 91.6%; ET, 76.9%). When compared with a single immersion, two-immersion treatments significantly increased the proportion of males in the MT-treated group (from 91.6% to 98.3%), decreased the proportion of males in the MDHT group (from 100.0% to 93.4%) and had no significant effect the ET-treated group (change from 76.9% to 82.5%). The overall comparison of the sex ratio among same treatments from different experiments (a single immersion in 1800 μg L⁻¹) was not significantly different.

Validation of the aceto-carmine technique for evaluating phenotypic sex in Nile tilapia (Oreochromis niloticus) fry

In this study a method for evaluating phenotypic sex in Nile tilapia was validated. A technique that uses aceto-carmine squash mounts to stain the entire gonadal tissue for microscopic examination (Method 2- squash mounts) was compared with a technique based on traditional histology. Approximately 2600 Nile tilapia fry weighing and measuring, respectively, between 0.25-2.50g and 26-53mm, aged 35 to 60 days after hatch (DAH), were sexed using this methodology. In situ microscopic examination on the gonads was also performed. A reliable sexing using squash mount was possible with fish weighing more than 0.500g, 45-47 DAH. Results from microscopic observation using the aceto-carmine stain coincided 100% with the histological examination. Male gonadal tissue was characterized by the presence of cysts containing spermatogonia and spermatocytes, while females were easily identified by the presence of oocytes at the perinucleolar stage. The technique proved to be efficient not only in terms of evaluating sex proportion in fish but also because it allows immediate evaluation of gonadal sex and demands less time and labour.

Characterization of nano-structured bainitic steel

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200°C for 10 days to produce a nano-structured bainitic steel. The microstructure consisted of nanobainitic ferrite laths with a high dislocation density and retained austenite films having extensive twins. The crystallographic analysis using TEM and EBSD revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with their parent austenite. There was only one type of packet identified in a given transformed austenite grain. Each packet consisted of two different blocks having variants with the same habit plane, but different crystallographic orientations. Atom Probe Tomography (APT) revealed that the carbon content of nanobainitic ferrite laths was much higher than expected from the para-equilibrium level. This was explained due to the long heat treatment time, which led to the formation of fine Fe-C clusters on areas with high dislocation densities in bainitic ferrite laths.