The effect of hydrogenation on the ECAP compaction of Ti–6Al–4V powder and the mechanical properties of compacts

The effect of hydrogen content on the compaction of Ti–6Al–4V powder at low temperatures, namely 500 °C, using equal channel angular pressing (ECAP) with back pressure has been investigated. The properties of the compacts before and after a heat treatment and de-hydrogenation cycle have been determined. Compaction of powder by ECAP (500 °C and 260 MPa) has shown maximum levels of relative density of 99.3% and 99.4% when charged with 0.05–0.1 wt.% and 0.61–0.85 wt.% of hydrogen, respectively. After the de-hydrogenation heat treatment the diffusion bonding between individual powder particles was completed and the microstructure was altered, depending on the level of hydrogen content. Two local maxima of 99.2% and 98.1% were observed in the measured density of consolidated compacts for hydrogen contents between 0.05 wt.% and 0.1 wt.% and between 0.61 wt.% and 0.85 wt.%, respectively. However, the mechanical properties of the compacts within these two ranges of hydrogen content were significantly different due to a difference in the observed microstructure. An exceptionally high ductility of 29%, in combination with a relatively high strength of ~560 MPa, was measured in a shear punch test on specimens which had a prior hydrogen level of 0.05 wt.% before the heat treatment. It was shown that material consolidated from powder hydrogenated to low levels of hydrogen before compaction has the potential to offer substantial improvements in mechanical properties after a suitable heat treatment.

Novel sphene coatings on Ti–6Al–4V for orthopedic implants using sol–gel method

Hydroxyapatite (HAp) is commonly used to coat titanium alloys (Ti–6Al–4V) for orthopedic implants. However, their poor adhesion strength and insufficient long-term stability limit their application. Novel sphene (CaTiSiO₅) ceramics possess excellent chemical stability and cytocompatibility. The aim of this study is to use the novel sphene ceramics as coatings for Ti–6Al–4V. The sol–gel method was used to produce the coatings and the thermal properties, phase composition, microstructure, thickness, surface roughness and adhesion strength of sphene coatings were analyzed by differential thermal analysis–thermal gravity (DTA–TG), X-ray diffraction (XRD), scanning electron microscopy (SEM), atom force microscopy (AFM) and scratch test, respectively. DTA analysis confirmed that the temperature of the sphene phase formation is 875 °C and XRD analysis indicated pure sphene coatings were obtained. A uniform structure of the sphene coating was found across the Ti–6Al–4V surface, with a thickness and surface roughness of the coating of about 0.5–1 μm and 0.38 μm, respectively. Sphene-coated Ti–6Al–4V possessed a significantly improved adhesion strength compared to that for HAp coating and their chemical stability was evaluated by testing the profile element distribution and the dissolution kinetics of calcium (Ca) ions after soaking the sphene-coated Ti–6Al–4V in Tris–HCl solution. Sphene coatings had a significantly improved chemical stability compared to the HAp coatings. A layer of apatite formed on the sphene-coated Ti–6Al–4V after they were soaked in simulated body fluids (SBF). Our results indicate that sol–gel coating of novel sphene onto Ti–6Al–4V possessed improved adhesion strength and chemical stability, compared to HAp-coated Ti–6Al–4V prepared under the same conditions, suggesting their potential application as coatings for orthopedic implants.

Constitutive analysis of hot deformation behavior of a Ti6Al4V alloy using physical based model

The effect of deformation parameters on the flow behavior of a Ti6Al4V alloy has been studied to understand the deformation mechanisms during hot compression. Cylindrical samples with partially equiaxed grains were deformed in the α+β phase region at different thermo-mechanical conditions. To develop components with tailored properties, the physically based Estrin and Mecking (EM) model for the work hardening/dynamic recovery combined with the Avrami equation for dynamic recrystallization was used to predict the flow stress at varying process conditions. The EM model revealed good predictability up to the peak strain, however, at strain rates below 0.01s^-1, a higher B value was observed due to the reduced density of dislocation tangles. In contrast, the flow softening model revealed higher value of constants a and b at high strain rates due to the reduction in the volume fraction of dynamic recrystallization and larger peak strain. The predicted flow stress using the combined EM+Avrami model revealed good agreement with the measured flow stress resulted in very low average absolute relative error value. The microstructural analysis of the samples suggests the formation of coarse equiaxed grains together with the increased β phase fraction at low strain rate leads to a higher flow softening.

Softening behavior of Ti6Al4V alloy during hot deformation

The effect of strain rate and strain on the hot compression behavior of Ti6Al4V has been analysed to understand the microstructural evolution and restoration behavior. Cylindrical samples with partially equiaxed grains were deformed in the α+β region at different thermo-mechanical conditions. EBSD has been used to study the microstructural evolution and the flow softening mechanisms. The microstructural evolution showed a complex restoration behaviour, where both fragmentation and nucleation of new grains have been observed. The volume fraction of the equiaxed grains increased with an increase in the strain, but decreased with the strain rate. At the same time, the average grain size of the equiaxed grains decreased with an increase in both the strain and strain rate. The measured activation energy for deformation revealed a good agreement with reported values in the literature.

An improved static model for tool deflection in machining of Ti–6Al–4V acetabular shell produced by selective laser melting

Tool deflection during milling operation leads to dimensional error, decreasing surface quality and increasing rejection rate. In this study, tool deflection during the milling of the inner surfaces of Ti–6Al–4V prosthetic acetabular shell produced by selective laser melting (SLM) was modelled. The first purpose of this research is to provide a general static cutting tool deflection model for ball nose cutters where deviation of machine components and tool holder are so small as to be considered negligible. This is because the values of machine component and tool holder deflection were lower than standard tolerances (10 μm) and found to be lower than 1/15 of tool deflection. The second and third objectives of this work involve calculating contact surfaces by determining workpiece and tool geometry and choosing second moment of inertia using a novel cross section method (CSM). Static models for three quasi-analytical methods (QAM) that are simple cantilever beam model (SCBM), two-section model (TWSM) and our three section model (THSM) are presented. THSM showed high accuracy which was validated by 3D finite element method (FEM3D) and experimental measurements. The accuracy of tool deflection calculation using THSM by computing, shank, flute and ball head deflection and also utilizing CSM to determine second moment of inertia showed notable improvements.

Improvement of the biomedical properties of titanium using SMAT and thermal oxidation

Titanium and its alloys are excellent candidates for biomedical implant. However, they exhibit relatively poor tribological properties. In this study, a two-step treatment including surface mechanical attrition treatment (SMAT) combined with thermal oxidation process has been developed to improve the tribological properties and biocompatibility of Ti. Ti after two-step treatment shows excellent wear-resistance and biocompatibility among all Ti samples, which can be ascribed to the highest surface energy, well crystallinity of rutile layer on its surface. Overall, the two-step treatment is a prospective method to produce excellent biomedical Ti materials.

Materials machining study of titanium alloy using a high speed camera

The research aim is to study and analyze the shear zone by application of merchant circle during machining of titanium alloy (Ti6Al4V). The thermo-mechanical reaction during machining plays an important role in defining machinability of titanium alloys. The scientific community is concerned about machining of titanium alloy due to problems occurring in the shear zone that affect tool life. Studying the cutting action contributes to understanding and addressing these problems effectively. For this purpose, an experimental setup, utilizing a high speed camera will be used to study the shear zone. The shear zone characteristics are studied by analyzing the images captured by a high speed camera placed near to the shear zone during machining. The experimental design consists of conducting a series of turning trials using combination of cutting parameters namely constant spindle speed (n) 770 rpm; feed rate (f) of 2 and 4 mm/rev; and depth of cut (d) of 1 and 2 mm. The length of cut (L) of 10 mm remains constant and no coolant is used for all trials. The images obtained from the camera are analyzed against the theory of orthogonal cutting using merchants circle.