An analysis of the transition between strain dependent and independent softening in austenite

The post-deformation softening behaviour of austenite has been studied for various compositions and deformation conditions. The strain at which the transition from strain dependent to strain independent post-deformation softening behaviour occurs (ε*) has been found to coincide closely with the strain to the peak stress (εp) under certain conditions but not under others. It has been proposed that the relationship between ε* and εp may be described geometrically using the initial grain size and the dynamically recrystallised grain size.

Dynamic softening of ferrite during large strain warm deformation of a plain-carbon steel

The evolution of dynamic ferrite softening in a plain-carbon steel was investigated by torsion tests during warm deformation at 810 °C, in the two-phase (ferrite + austenite) region, and strain rate of 0.1 s−1 with different strains up to 50. The warm flow behaviour and ferrite microstructural parameters, such as grain size, misorientation angle across ferrite/ferrite boundaries, and the fraction of high-angle and low-angle grain/subgrain boundaries were quantified using electron back scatter diffraction. The results show that with increasing strain up to not, vert, similar2, the ferrite grain size and fraction of high-angle boundaries rapidly decrease and the fraction of low-angle boundaries increases. However, these parameters remain approximately unchanged with increasing strain from not, vert, similar2 to 50. The dynamic softening mechanism observed during large strain ferritic deformation is explained by dynamic recovery and continuous dynamic recrystallization.

Blood-nourishing and hard-softening capsule costs less in the management of osteoarthriticknee pain : A randomized controlled trial

The blood-nourishing and hard-softening (BNHS) capsule is a traditional Chinese formula used in the symptomatic treatment of inflammation and pain. We conducted this randomized controlled trial to compare the efficacy of BNHS with other commonly prescribed drugs. We recruited 120 patients from two teaching hospitals; 30 patients in each hospital were randomly assigned to receive BNHS. In one hospital, the 30 controls were given another traditional Chinese drug; whereas a Western medicine (chondroprotection drug/Viartril-s) was used as the control in the other hospital. Intervention was carried out over a period of 4 weeks. Primary outcome measures included self-reported pain level, and changes in stiffness and functional ability as measured by the Western Ontario McMaster Universities Osteoarthritis (WOMAC) index. Mixed models were used for statistical analysis. Substantial improvements in disease-specific symptoms were observed, after 4 weeks of treatment, in patients taking BNHS capsules. As assessed by the WOMAC index, pain level of the BNHS group decreased by 57% [95% confidence interval (CI) = 50, 63], stiffness by 63% (95% CI = 55, 71) and functional ability increased by 56% (95% CI = 50, 63). No significant differences were found in any of the outcome measures between the BNHS group and either of the comparison groups. No severe adverse effects were reported. However, this study lacked a placebo group; therefore, we conclude that BNHS appears to be as effective as commonly prescribed medicines for the relief of pain and dysfunction in knee osteoarthritis patients, but costs a lot less than other Western and herbal drugs in the study.

Correlation between the deformation and post-deformation softening behaviours in hot worked Austenite

The relation between the deformation and post-deformation softening behaviours of austenite is examined in a 304 stainless steel. This correlation has been exploited in the modelling of hot rolling and it is argued here that the key to this understanding lies in the deformation structure. The latter is characterized in the present work by the fraction of dynamic recrystallization. The value of this fraction at the peak in the flow stress curve is found to decrease with increasing stress (i.e. with decreasing temperature and increasing strain rate). By contrast, the fraction of dynamic  recrystallization at the strain corresponding to the point where  post-deformation softening becomes strain independent is found to be constant. These observations are used to explain the nature of the important difference between the flow curve peak and the onset of strain independent post-deformation softening.

The mechanism of metadynamic softening in austenite after complete dynamic recrystallization

A novel mechanism of post-dynamic softening during annealing of a fully dynamically recrystallized (DRX) austenitic Ni–30Fe alloy is proposed. The initial softening stage involves rapid growth of the dynamically formed nuclei and migration of the mobile boundaries. The sub-boundaries within DRX grains progressively disintegrate through dislocation climb and dislocation annihilation, which ultimately leads to the formation of dislocation-free grains, and the grain boundary migration gradually becomes slower. As a result, the DRX texture largely remains preserved throughout the annealing process.

Softening mechanisms in two duplex stainless steels deformed in hot torsion

The aim of the present work was to undertake a detailed investigation of the softening mechanisms during hot deformation of a 21Cr-10Ni-3Mo (steel A) and a 21Cr-8Ni-3Mo (steel B) austenite/ferrite duplex stainless steels containing about 60% and 30% of austenite, respectively. The steels were subjected to hot deformation in torsion performed at 900 ºC and 1200 ºC using a strain rate of 0.7 s-1 to several strain levels. Quantitative optical and transmission electron microscopy were used in the investigation. Austenite was observed to soften via dynamic recovery (DRV) and dynamic recrystallisation (DRX) accompanied by DRV for the deformation temperatures of 900 °C and 1200 °C, respectively, for the both steels studied. DRX of austenite largely occurred through strain-induced grain boundary migration, complemented by (multiple) twinning, and developed significantly faster in steel A than in steel B, indicating that considerably larger strains partitioned into austenite in the former steel during deformation at 1200 °C. The above softening mechanism was accompanied by the formation of DRX grains from subgrains along the austenite/ferrite interface and by large-scale subgrain coalescence. At 900°C, stressassisted phase transitions between austenite and ferrite were observed, characterised by dissolution of the primary austenite, formation of Widmanstätten secondary austenite and gradual globularisation of the microstructure with increasing strain. These processes appeared to be significantly more widespread in steel B. The softening mechanism within ferrite for the both steels studied was classified as “continuous DRX”, characterised by a gradual increase in misorientations between neighbouring subgrains with strain, for the both deformation temperatures.

Softening during the hot deformation of steel

The behaviour of steel undergoing hot deformation was examined with the aim of better understanding the softening mechanisms operating during industrial hot strip rolling. These softening mechanisms can significantly influence the deformation force required to attain a given reduction in thickness, and this work answered a number of questions with regard to the transition between softening mechanisms.

Texture and substructure development during post-dynamic softening in Ni-30%Fe austenite

The texture and substructure development during post-dynamic annealing of an austenitic Ni-30%Fe model alloy after complete dynamic recrystallization was investigated using electron back-scattered diffraction (EBSD) and transmission electron microscopy (TEM). A novel mechanism of metadynamic softening is proposed based on the experimental investigation of the grain structure, crystallographic texture and dislocation substructure evolution. The initial softening stage involved rapid growth of the dynamically formed nuclei and migration of the mobile boundaries. The subboundaries within DRX grains progressively disintegrated through dislocation climb and dislocation annihilation, which ultimately led to the formation of dislocation-free grains, while the grain boundary migration gradually became slower. As a result, the DRX texture was largely preserved throughout the annealing process.

Microstructure evolution and softening processes occurring during annealing of hot deformed Ni-30Fe austenite

The current work investigates the microstructure evolution and softening processes that take place during annealing of an austenitic Ni-30Fe model alloy subjected to hot deformation in the dynamic recrystallization (DRX) regime. The substructure of the deformed matrix grains largely comprised organized microband arrays, though that of the DRX grains consisted of more random, complex subgrain/cell arrangements. This substructure disparity was also reflected by the distinct difference in the mechanism of post-deformation softening taking place during annealing of the deformed matrix and DRX grains. In the former, the recrystallization process took place through nucleation and growth of new grains fully replacing the deformed structure, as expected for the classical static recrystallization (SRX). The corresponding texture was essentially random, in contrast to that of the DRX grains dominated by low Taylor factor components. The microbands originally present within the deformed matrix grains displayed some tendency to disintegrate during annealing, nonetheless, they remained largely preserved even at prolonged holding times. During annealing of the fully DRX microstructure, a novel softening mechanism was revealed. The initial post-dynamic softening stage involved rapid growth of the dynamically formed nuclei and migration of the mobile boundaries in correspondence with the well-established metadynamic recrystallization (MDRX) mechanism. However, in contrast to the deformed matrix, SRX was not observed and the sub-boundaries within DRX grains rapidly disintegrated through dislocation climb and dislocation annihilation, which led to the formation of dislocation-free grains already at short holding times. Consequently, the DRX texture initially became slightly weakened and then remained largely preserved throughout the annealing process.

Texture evolution and softening processes in an austenitic Ni-30Fe alloy subjected to hot deformation and subsequent annealing

The current work has investigated the texture development in an austenitic Ni-30Fe model alloy during deformation within the dynamic recrystallization (DRX) regime and after post-deformation annealing. Both the deformed matrix and DRX texture displayed the expected FCC shear components, the latter being dominated by the low Taylor factor grains, which was presumably caused by their lower consumption rate during DRX. The deformed matrix grains were largely characterized by organized, microband structures, while the DRX grains showed more random, complex subgrains/cell arrangements. The latter substructure type proved to be significantly less stable during post-deformation annealing. The recrystallization of the deformed matrix occurred through nucleation and growth of new grains fully replacing the deformed structure, as expected for the classical static recrystallization (SRX). Unlike the DRX grains, the SRX texture was essentially random. By contrast, a novel softening mechanism was revealed during annealing of the fully DRX microstructure. The initial post-dynamic softening stage involved rapid growth of the dynamically formed nuclei and migration of the mobile boundaries in line with the well-established metadynamic recrystallization (MDRX) mechanism, which weakened the starting DRX texture. However, in parallel, the sub-boundaries within the deformed DRX grains progressively disintegrated through dislocation climb and dislocation annihilation, which ultimately led to the formation of dislocation-free grains. Consequently, the weakened DRX texture largely remained preserved throughout the annealing process.

Microstructure evolution and softening processes in hot deformed austenitic and duplex stainless steels

The microstructure evolution and softening processes occurring in 22Cr-19Ni-3Mo austenitic and 21Cr-10Ni-3Mo duplex stainless steels deformed in torsion at 900 and 1200 °C were studied in the present work. Austenite was observed to soften in both steels via dynamic recovery (DRV) and dynamic recrystallisation (DRX) for the low and high deformation temperatures, respectively. At 900 °C, an "organised", self-screening austenite deformation substructure largely comprising microbands, locally accompanied by micro-shear bands, was formed. By contrast, a "random", accommodating austenite deformation substructure composed of equiaxed subgrains formed at 1200 °C. In the single-phase steel, DRX of austenite largely occurred through straininduced grain boundary migration accompanied by (multiple) twinning. In the duplex steel, this softening mechanism was complemented by the formation of DRX grains through subgrain growth in the austenite/ferrite interface regions and by large-scale subgrain coalescence. At 900 °C, the duplex steel displayed limited stress-assisted phase transformations between austenite and ferrite, characterised by the dissolution of the primary austenite, formation of Widmanstätten secondary austenite and gradual globularisation of the transformed regions with strain. The softening process within ferrite was classified as "extended DRV", characterised by a continuous increase in misorientations across the sub-boundaries with strain, for both deformation temperatures.