Influence of surface mechanical attrition treatment attrition media on the surface contamination and corrosion of magnesium

Surface mechanical attrition treatment (SMAT) is a mechanical peening process used to generate ultrafine grain surfaces on a metal. SMAT was carried out on pure magnesium using different attrition media (zirconia [ZiO2], alumina [Al2O3], and steel balls) to observe the effect on microstructure, surface residual stress, surface composition, and corrosion. Surface contamination from SMAT was characterized using glow discharge optical emission spectroscopy (GDOES). The SMAT process produced a refined grain structure on the surface of Mg but resulted in a region of elemental contamination extending ~10 μm into the substrate, regardless of the media used. Consequently, SMAT-treated surfaces showed an increased corrosion rate compared to untreated Mg, primarily through increased cathodic kinetics. This study highlights the issue of contamination resulting from the SMAT process, which is a penalty that accompanies the significant grain refinement of the surface produced by SMAT. This must be considered if attempting to exploit grain refinement for improving corrosion resistance.

Tailoring the surface chemistry of carbon fiber and E-glass composites for improved adhesion

The main challenges in the manufacture of composite materials are low surface energy and the presence of silicon-containing contaminants, both of which greatly reduce surface adhesive strength. In this study, carbon fiber (CF) and E-glass epoxy resin composites were surface treated with the Accelerated Thermo-molecular adhesion Process (ATmaP). ATmaP is a multiaction surface treatment process where tailored nitrogen and oxygen functionalities are generated on the surface of the sample through the vaporization and atomization of n-methylpyrrolidone solution, injected via specially designed flame-treatment equipment. The treated surfaces of the polymer composites were analyzed using XPS, time of flight secondary ion mass spectrometry (ToF-SIMS), contact angle (CA) analysis and direct adhesion measurements. ATmaP treatment increased the surface concentration of polar functional groups while reducing surface contamination, resulting in increased adhesion strength. XPS and ToF-SIMS showed a significant decrease in silicon-containing species on the surface after ATmaP treatment. E-glass composite showed higher adhesion strength than CF composite, correlating with higher surface energy, higher concentrations of nitrogen and CO functional groups (from XPS) and higher concentrations of oxygen and nitrogen-containing functional groups (particularly C₂H₃O⁺ and C₂H₅NO⁺ molecular ions, from ToF-SIMS).

Premature thermal fatigue failure of aluminium injection dies with duplex surface treatment

The premature failure of an aluminium injection die with a duplex surface treatment (plasma nitriding and physical vapor deposition coating) was investigated, in an effort to identify the causes of such premature failure of the component. The manufacturing and the operating conditions were documented. Analytical tools were used, including scanning electron microscopy with energy dispersive X-ray capability, X-ray diffraction, and instrumented microhardness testing. Preliminary observations showed a microstructure of coarse tempered martensite, and a considerably rough surface with porosity and cracks. A detailed analysis of crack initiation sites identified sulfur inclusions in the subsurface, underneath the coating. A further revision of the processing conditions revealed that a sulfur-impregnated grinding stone had been used to polish the die. The chemical composition of such grinding stone matched that of the inclusions found in the subsurface of the failed component. Thus, searched causes of premature failure could be discussed on the lights of the present findings.

Arsenic contamination in Bangladesh groundwater: a major environmental and social disaster

In attempting to eliminate disease caused by drinking polluted surface water, millions of shallow surface wells were drilled into the Ganges delta alluvium in Bangladesh. The latest statistics indicate that 80% of Bangladesh and an estimated 40 million people are at risk of arsenic poisoning-related diseases because the ground water in these wells is contaminated with arsenic. The clinical manifestations of arsenic poisoning are myriad, and the correct diagnosis depends largely on awareness of the problem. Patients with melanosis, leuco-melanosis, keratosis, hyperkeratosis, dorsum, non-petting edema, gangrene and skin cancer have been identified. The present article reviews the current arsenic contamination of ground water, hydrological systems, groundwater potential and utilization and environmental pollution in Bangladesh. This paper concludes by clarifying the main actions required to ensure the sustainable development of water resources in Bangladesh

The inhibitory effect of stevioside on bacillus cereus growth in milk: validation and its response surface optimization

Stevioside, a glycoside present in the leaves of Stevia rebaudiana Bertoni, offers therapeutic benefits such as anti-hyperglycemic, anti-hypertensive, antiinflammatory, anti-tumor, diuretic and immune influencing properties. In this work antimicrobial activity of stevioside against Bacillus cereus, a major source of milk contamination was investigated. The isolate was confirmed by various biochemical and 16S rRNA gene sequencing. The effect of temperature, incubation time and concentration of stevioside was optimized from a central composite response surface design. The standard plate count (SPC) of pasteurized milk was drastically reduced in comparison to toned and fresh milk. The optimal temperature, incubation time and stevioside concentration were observed to be 60.23°C, 21 h, and 275 μg/ mL respectively. The synergism of stevioside with the external factors (temperature and time) against B. cereus was observed. Our studies showed that addition of stevioside in fresh as well as pasteurised milk would control growth of B. cereus in milk.