Focused ion beam milling as a universal template technique for patterned growth of carbon nanotubes

Focused ion beam (FIB) milling system has been used to create nanosized patterns as the template for patterned growth of carbon nanotubes on Si substrate surface without predeposition of metal catalysts. Carbon nanotubes only nucleate and grow on the template under controlled pyrolysis of iron phthalocyanine at 1000 °C. The size, growth direction, and density of the patterned nanotubes can be controlled under different growth conditions and template sizes. Atomic force microscopy and electron microscopy analyses reveal that the selective growth on the FIB template is due to its special surface morphology and crystalline structure.

Synthesis of ZnO nanowires using ball-milling and annealing method

Nanowires represent a new class of ZnO morphologies with many exiting new properties and applications. The research in the synthesis and characterization of ZnO nanowires has received enormous attention in recent years. However, most synthesis methods using vapor deposition process can only produce small amount of sample, mass production has not been achieved yet. Large-quantity production of ZnO nanowires needs to be realized for large-scale property and application studies. One of the promising approaches to the large scale synthesis is a ball-milling and annealing method. This paper first introduces several common synthesis methods of ZnO nanowires and then summarizes the one dimensional nanomaterials produced by the ball milling and annealing method. Finally, some preliminary results of ZnO nanowire synthesis are presented.

Conical boron nitride nanorods synthesized via the ball-milling and annealing method

A boron nitride (BN) nanostructure, conical BN nanorod, has been synthesized in a large quantity on Si substrates for the first time via the ball-milling and annealing method. Nitridation of milled boron carbide (B₄C) powders was performed in nitrogen gas at 1300°C on the surface of the substrates to form the BN nanorods. The highly crystallized nanorods consist of conical BN basal layers stacked along the nanorod axis. Ball milling of the B₄C powders can significantly enhance the nitridation of the powders and thus facilitate the formation of nanorods during the annealing process.

Efficient production of ZnO nanowires by a ball milling and annealing method

ZnO powder was mechanically milled in a ball mill. This procedure was found to greatly increase its evaporation ability. The anomalous evaporation behaviour was caused by the disordered structure of the milled material and was not related to the increase in its surface area after milling. ZnO nanowires were synthesized by evaporation of this milled precursor. Nanowires with smooth and rough surfaces were present in the sample; the latter morphology was dominant. A green emission band centred at 510 nm was dominant in the cathodoluminescence spectrum of the nanowires.

One-dimensional nanomaterials synthesized using high-energy ball milling and annealing process

One-dimensional (1D) nanomaterials including nanotubes, nanowires and nanorods have many new properties, functionalities and a large range of promising applications. A major challenge for these future industrial applications is the large-quantity production. We report that the ball milling and annealing process has the potential to achieve the mass production. Several examples including C, BN nanotubes and SiC, Zn nanowires are presented to demonstrate such capability. In addition, both size and structure of 1D nanomaterials can be controlled by varying processing conditions. New growth mechanisms involved in the process have been investigated and the high-energy ball milling has an important role in the formation of these 1D nanomaterials.

Rapid synthesis of TiC–Fe3C composite by electric discharge assisted mechanical milling of ilmenite (FeTiO3) with graphite

Carbo-thermic reduction of ilmenite (FeTiO₃) to TiO₂ and/or TiC is traditionally carried out by a high temperature annealing treatment at  _~1500 °C. In this work, electric discharge assisted mechanical milling (EDAMM) has been used to synthesise TiC + Fe₃C from FeTiO₃ in 5 min. In this study we report of the reduction of FeTiO₃ with C that does not require an additional high temperature annealing treatment.

Rapid synthesis of Bi and Sb sulfides using electric discharge assisted mechanical milling

Group V–VI binary sulfides are semiconductors, and find application in a number of commercial devices. Synthesis of these metal sulfides is problematic, and traditional synthesis techniques utilizing thermal and chemical means have disadvantages such as a long process time, contamination, and the use of toxic substances. In this work, the novel synthesis technique of electric discharge assisted mechanical milling (EDAMM) has been used to rapidly synthesize Bi₂S₃ and Sb₂S₃ powders from elemental S and Sb/Bi powders. This technique is shown to be both rapid and successful, and produces crystalline metal sulfide powders with a particle size of approximately 2 μm.

Fabrication of ultrafine powder from eri silk through attritor and jet milling

Fibroin protein derived from silk fibres has been extensively studied with exciting outcomes for a number of potential advanced biomaterial applications. However, one of the major challenges in applications lies in engineering fibroin into a  desired form using a convenient production technology. In this paper, fabrication of ultrafine powder from eri silk is reported. The silk cocoons were degummed and the extracted silk fibres were then chopped into snippets prior to attritor and air jet milling. Effects of process control agents, material load and material to water ratio during attritor milling were studied. Compared to dry and dry–wet attritor milling, wet process emerged as the preferred option as it caused less colour change and facilitated easy handling. Ultrafine silk powder with a volume based particle size d(0.5) of around 700 nm could be prepared following the sequence of chopping ➔ wet attritor milling ➔ spray drying ➔ air jet milling. Unlike most reported powder production methods, this method could fabricate silk particles in a short time without any pre-treatment on degummed fibre. Moreover, the size range obtained is much smaller than that previously produced using standard milling devices. Reduction in fibre tenacity either shortened the milling time even further or helped bypassing media milling to produce fine powder directly through jet milling. However, such reduction in fibre strength did not help in increasing the ultimate particle fineness. The study also revealed that particle density and particle morphology could be manipulated through appropriate changes in the degumming process.

Graphical Abstract:  Fabrication of eri silk powder using attritor and jet milling is reported. Volume based particle size d(0.5) of around 700 nm could be prepared following the sequence chopping ➔ wet attritor milling ➔ spray drying ➔ air jet milling. No pre-treatments were used and the particle size range obtained is much smaller than that previously produced using standard milling devices. Particle density morphology could be manipulated through appropriate changes of cocoon degumming conditions.

Changes in the Australian Commonwealth departmental machinery of government 1928-1982

The Commonwealth departmental machinery of government is changed by using Orders in Council to create, abolish or change the name of departments. Since 1906 governments have utilised a particular form of Order in Council, the Administrative Arrangements Order (AAO), as the means to reallocate functions between departments for administration. After 1928 successive governments from Scullin to Fraser gradually streamlined and increasingly used the formal processes for the executive to change departmental arrangements and the practical role of Parliament, in the process of change, virtually disappeared. From 1929 to 1982, 105 separate departments were brought into being, as new departments or through merger, and 91 were abolished, following the merger of their functions in one way or another with other departments. These figures exclude 6 situations where the change was simply that of name alone. Several hundred less substantial transfers of responsibilities were also made between departments. This dissertation describes, documents and analyses all these changes. The above changes can be distilled down to 79 events termed primary decisions. Measures of the magnitude of change arising from the decisions are developed with 157.25 units of change identified as occurring during the period, most being in the Whitlam and Fraser periods. The reasons for the changes were assessed and classified as occurring for reasons of policy, administrative logic or cabinet comfort. 47.2% of the units of change were attributed to policy, 34.9% to administrative logic, 17% to cabinet comfort. Further conclusions are drawn from more detailed analysis of the change and the reasons for the changes.

Role of water and surfactant in the solvent milling of wool

Unlike other fibres, wool felts readily when agitated in the presence of water. For this reason, only the minimum necessary quantity of water is used when the garments are drycleaned. However, wool fibres are often deliberately felted to obtain a warm bulky handle by controlled addition of water to the solvent. This process is known as solvent milling and recently, it has become a popular alternative to the traditional milling in water alone. Although the factors which influence milling in solvent are known, the relationships between them are not well defined. A comprehensive study of the relationship between water distribution and milling shrinkage during agitation of wool in perchloroethylene has been carried out in this thesis. The Karl Fischer method of determination was used throughout to establish the distribution of water between the wool fibre and the solvent liquor. The emphasis was placed on practical production variables. The role of surfactant in affecting milling shrinkage through its effect on the transport of water to the fibre from the solvent was examined. The ability of a suitable surfactant in promoting even and rapid sorption of water by the fibre was related to the colloidal properties of the milling liquor.

Reactive ball milling to produce nanocrystalline ZnO

Ball milling of zinc powders in oxygen atmosphere leads to nanocrystalline ZnO. The average grain size has a value of 9 nm. The zinc oxidation proceeds gradually. It is compared with the combustion oxidation reactions of metals (Zr, Ti, Fe and Sn) reported previously. We propose a new parameter ΔH/C_p(metal) instead of simplified adiabatic temperature to judge if the mechanochemical oxidation of a particular metal happens via gradual or combustion reaction.