Microstructural analysis of pre-strained TRIP steel after fatigue testing

The widespread introduction of multiphase sheet steels in the automotive industry has led to considerable interest in the fatigue properties of these materials. The different microstructural phases within matelials such as TRIP steels can influence the fatigue behaviour due to the manner in which the cyclic strain is accommodated within these phases. In this study fully reversed straincontrolled fatigue tests were perfonnrmed on a commercially-produced uncoated TRIP 780 steel both in the as-received and 20 % prestrained condition. The pre-strained TRIP steel showed significant cyclic softening at higher strain amplitudes, whereas some initial work hardening was observed at lower strain amplitudes before cyclic softening. The cyclic stabilised strength of the pre-strained TRIP steel was independent of strain amplitude, while the cyclic stabilised strength of the as-received TRIP steel increased with strain amplitude. Transmission Electron Microscopy TEM was used to examine the effect of the cyclic deformation on the microstructure of the different conditions, with the differences in fatigue behaviour explained based on the differences in the deformation structure formed within the steel (i.e. dislocation density and sub-structure and microband formation).

Cyclic deformation of advanced high-strength steels : mechanical behavior and microstructural analysis

The fatigue properties of multiphase steels are an important consideration in the automotive industry. The different microstructural phases present in these steels can influence the strain life and cyclic stabilized strength of the material due to the way in which these phases accommodate the applied cyclic strain. Fully reversed strain-controlled low-cycle fatigue tests have been used to determine the mechanical fatigue performance of a dual-phase (DP) 590 and transformation-induced plasticity (TRIP) 780 steel, with transmission electron microscopy (TEM) used to examine the deformed microstructures. It is shown that the higher strain life and cyclic stabilized strength of the TRIP steel can be attributed to an increased yield strength. Despite the presence of significant levels of retained austenite in the TRIP steel, both steels exhibited similar cyclic softening behavior at a range of strain amplitudes due to comparable ferrite volume fractions and yielding characteristics. Both steels formed low-energy dislocation structures in the ferrite during cyclic straining.

The effect of low cycle fatigue, ratcheting and mean stress relaxation on stress-strain response and microstructural development in a dual phase steel

This study examines the cyclic plastic deformation behavior and microstructural development of a dual phase steel in both symmetric and asymmetric cycling in strain and stress control modes. The low-cycle fatigue (LCF) and mean stress relaxation (MSR) tests show very similar fatigue lifetimes. However, fatigue lifetimes reduce and prominent accumulation of directional strain was observed in ratcheting. A microstructural analysis has revealed that the type of cyclic test carried out has a noticeable impact on the substructural development, and this has been correlated with differences in accumulated tensile strain. Electron backscatter diffraction investigation has shown larger in-grain misorientation for ratcheting specimen in comparison with LCF and MSR specimens. The orientation of ferrite grains was found to have very little effect on their substructural development, and strain localization commonly occurred in the ferrite at the ferrite/martensite interface.

Constitutive analysis of hot deformation behavior of a Ti6Al4V alloy using physical based model

The effect of deformation parameters on the flow behavior of a Ti6Al4V alloy has been studied to understand the deformation mechanisms during hot compression. Cylindrical samples with partially equiaxed grains were deformed in the α+β phase region at different thermo-mechanical conditions. To develop components with tailored properties, the physically based Estrin and Mecking (EM) model for the work hardening/dynamic recovery combined with the Avrami equation for dynamic recrystallization was used to predict the flow stress at varying process conditions. The EM model revealed good predictability up to the peak strain, however, at strain rates below 0.01s^-1, a higher B value was observed due to the reduced density of dislocation tangles. In contrast, the flow softening model revealed higher value of constants a and b at high strain rates due to the reduction in the volume fraction of dynamic recrystallization and larger peak strain. The predicted flow stress using the combined EM+Avrami model revealed good agreement with the measured flow stress resulted in very low average absolute relative error value. The microstructural analysis of the samples suggests the formation of coarse equiaxed grains together with the increased β phase fraction at low strain rate leads to a higher flow softening.

Characterization on ferrite microstructure evolution during large strain warm torsion testing of plain low carbon steel

Ferrite grain/subgrain structures evolution during the extended dynamic softening of a plain low carbon steel was investigated throughout the large strain warm deformation by hot torsion. Microstructural analysis with electron back-scattering diffraction (EBSD) scanning electron microscope (FEG/SEM) was carried out on the ferrite microstructural parameters. The results showed that the warm flow stress–strain curves are similar to those affected only by dynamic softening and an extended warm flow softening is seen during large strain deformation up to 30. Furthermore, with an increase in strain up to ~ vert, similar1 the grain size of ferrite, misorientation angle and fraction of high-angle boundaries gradually decrease and fraction of low-angle boundaries increases. With a further increase in the strain beyond ~, vert, similar2, these parameters remain approximately unchanged. No evidence of discontinuous dynamic recrystallisation involving nucleation and growth of new grains was found within ferrite. Therefore, the dynamic softening mechanism observed during large strain ferritic deformation is explained by continuous dynamic recrystallization (CDRX).

Microstructure and properties of a C-Mn steel subjected to heavy plastic deformation

In the present paper an effect of severe plastic deformation (SPD) on the microstructural evolution and properties of a plain C-Mn steel was investigated. The SPD was accomplished by the MaxStrain system which deforms material along two perpendicular axes while the deformation along the third axis is fully constrained. The applied amounts of true strains were 5 and 20 in total. Deformation was conducted at room and 500°C temperatures. Some samples deformed at room temperature were subsequently annealed at 500°C. A microstructural analysis by SEM/EBSD was used for recognition the low- and high-angle grain boundaries. It was found that the collective effect of severe plastic deformation (true strain of 20) and further annealing promotes the formation of high-angle grain boundaries and uniform fine grained microstructure. The refinement of ferrite microstructure results in a significant increase in strength and hardness.

Effect of cooling rate on phase transformations in a high-strength low-alloy steel studied from the liquid phase

The phase transformation and precipitation in a high-strength low-alloy steel have been studied over a large range of cooling rates, and a continuous cooling transformation (CCT) diagram has been produced. These experiments are unique because the measurements were made from samples cooled directly from the melt, rather than in homogenized and re-heated billets. The purpose of this experimental design was to examine conditions pertinent to direct strip casting. At the highest cooling rates which simulate strip casting, the microstructure was fully bainitic with small regions of pearlite. At lower cooling rates, the fraction of polygonal ferrite increased and the pearlite regions became larger. The CCT diagram and the microstructural analysis showed that the precipitation of NbC is suppressed at high cooling rates, and is likely to be incomplete at intermediate cooling rates.

Microstructural and surface texture analysis due to machining in Super Austenitic Stainless Steel

Inferior surface quality is a significant problem faced by machinist. The purpose of this study is to present a surface texture analysis undertaken as part of machinability assessment of Super Austenitic Stainless Steel alloy-AL6XN. The surface texture analysis includes measuring the surface roughness and investigating the microstructural behaviour of the machined surfaces. Eight milling trials were conducted using combination of cutting parameters under wet machining. An optical profilometer (non-contact), was used to evaluate the surface texture at three positions. The surface texture was represented using the parameter, average surface roughness. Scanning Electron Microscope was utilised to inspect the machined surface microstructure and co relate with the surface roughness results. Results showed that maximum roughness values recorded at the three positions in the longitudinal direction (perpendicular to the machining grooves) were 1.21 μm (trial 1), 1.63 μm (trial 6) and 1.68 μm (trial 7) respectively whereas the roughness values were greatly reduced in the lateral direction. Also, results showed that the feed rate parameter significantly influences the roughness values compared to the other cutting parameters. The microstructure of the machined surfaces was distorted by the existence of cracks, deformed edges and bands and wear deposition due to machining process.

The influence of twinning on the hot working flow stress and microstructural evolution of magnesium alloy AZ31

The microstructural evolution during compression (at 350°C and a strain rate of 0.01s-1) was examined for magnesium alloy AZ31 received in the "as-cast" condition. It was revealed that at low strains, many twins are produced and dynamically recrystallized (DRX) grains form as a necklace along pre-existing grain boundaries. At higher strains, DRX stagnates, most likely due to the accommodation of deformation in the DRX fraction of the material. It was also observed that twin boundaries act as sites for the nucleation of DRX grains. The analysis was repeated for samples pre-compressed to a strain of 0.15 at room temperature prior to the hot deformation step. The idea of these additional tests was to increase the degree of twinning and therefore the density of sites for the nucleation of DRX. It was found that statically recrystallized (SRX) grains developed at the twins during heating to the test temperature. When these samples were deformed, the peak flow stress was reduced by approximately 20% and the development of DRX was enhanced. This can be attributed to the accelerated nucleation of DRX in the refined SRX structure.

Microstructural features of rolled mg-3Al-1Zn

The microstructures of hot- and cold-rolled Mg-3Al-1Zn (AZ31) are examined using scanning electron and optical microscopy. It is shown that the microstructures following multipass hot rolling and annealing are more uniform than those formed by heavy single pass rolling and annealing. The importance of twins in producing intragranular recrystallization is evident, although the most dominant nucleation site is grain boundaries. The cold-rolled structure after a rolling reduction of 15 pct is dominated by the presence of deformation twins. Twin trace analysis suggests that approximately two thirds of the twins are a form of “c-axis compression” twin. A number of “c-axis tension” twins were also observed and additional in-situ scanning electron microscopy experiments were performed to confirm earlier observations that suggest these twins can form after deformation, during unloading.

Microstructural development in Al/MgAl2O4 in situ metal matrix composite using value-added silica sources

Al/MgAl2O4 in situ metal matrix composites have been synthesized using value-added silica sources (microsilica and rice husk ash) containing ~97% SiO2 in Al-5 wt.% Mg alloy. The thermodynamics and kinetics of MgAl2O4 formation are discussed in detail. The MgO and MgAl2O4 phases were found to dominate in microsilica (MS) and rice husk ash (RHA) value-added composites, respectively, during the initial stage of holding the composites at 750 °C. A transition phase between MgO and MgAl2O4 was detected by the scanning electron microscopy and energy-dispersive spectroscopy (SEM–EDS) analysis of the particles extracted from the composite using 25% NaOH solution. This confirms that MgO is gradually transformed to MgAl2O4 by the reaction 3SiO2(s)+2MgO(s)+4Al(l)→2MgAl2O4(s)+3Si(l). The stoichiometry of MgAl2O4, n, computed by a new methodology is between 0.79 and 1.18. The reaction between the silica sources and the molten metal stopped after 55% of the silica source was consumed. A gradual increase in mean MgAl2O4 crystallite size, D, from 24 to 36 nm was observed in the samples held for 10 h.

Microstructural characterization and mechanical properties of Mg-Zr-Ca alloys prepared by hot-extrusion for biomedical applications

This paper investigated the microstructural characterization and mechanical properties of Mg-Zr-Ca alloys prepared by hot-extrusion for potential use in biomedical applications. Mg-Zr-Ca alloys were fabricated by commercial pure Mg (99.9%), Ca (99.9%), and master Mg-33% Zr alloy (mass%). The microstructural characterization of the hot-extruded Mg-Zr-Ca alloys was examined by X-ray diffraction analysis and optical microscopy, and the mechanical properties were determined from tensile tests. The experimental results indicate that the hot-extruded Mg-Zr-Ca alloys with 1 mass% Ca are composed of one single phase and those alloys with 2 mass% Ca consist of both Mg2Ca and α phase. The hot-extruded Mg-Zr-Ca alloys exhibit equiaxed granular microstructures and the hot-extrusion process can effectively increase both the tensile strength and ductility of Mg-Zr-Ca alloys. The hot-extruded Mg-1Zr-1Ca alloy (mass%) exhibits the highest strength and best ductility among all the alloys, and has much higher strength than the human bone, suggesting that it has a great potential to be a good candidate for biomedical application.

A genre analysis of reprint request emails written by EFL and physics professionals

The present study aimed to analyze reprint request e-mail messages written by postgraduates (MA students) of two fields of study, namely Physics and EFL, to realize the differences and similarities between the two email types. The results showed that the two corpora were much alike at the level of move schemata while there were some differences concerning strategies and microstructural features. The results showed that the two corpora were much alike at the level of move schemata while there were some differences concerning strategies and microstructural features. The email writers within each discipline were affected by their previously learned texts and the physics group was affected by the conventions of Persian letter writing. The email writers within each discipline were affected by their previously learned texts and the physics group was affected by the conventions of Persian letter writing

Solidification behaviour and microstructural development of ironbased alloys under conditions pertinent to strip casting - 200 series stainless steels

The castability and microstructures produced from strip casting simulations of three compositions in the 200 series stainless steels have been examined. The nucleation density was similar for all three compositions.The as-cast microstructure showed very fine austenite grains of 10–20 μm in width. Retained delta ferrite was observed in the inter-dendritic regions, and was likely to be stabilised by the segregation of Cr into these regions. An analysis of the crystallography expected of different solidification sequences is presented, but a strict adherence to the Kurdjumov-Sachs orientation relationship was not found in these samples.