Structure and mechanical property variations in Mg-Gd-Y-Zn-Zr alloy depending on its composition and processing conditions

An effect of alloying element content on mechanical properties and precipitate formation in Mg-RE alloys was studied for Mg-8Gd-4Y- 1Zn-0.4Zr (wt%) and Mg-10Gd-5Y-1.8Zn-0.4Zr (wt%). It is shown that small variations in the alloying element concentration can be used to manipulate the alloy microstructure and precipitate formation towards eliminating the asymmetry (tension/compression) and anisotropy of yield stress.

Compositional effects on the restoration behaviour in Mg-Zn-Re alloys

Additions of rare earth elements to magnesium alloys are qualitatively reported in the literature to retard recrystallisation. However, their effect in the presence of other (non-rare earth) alloy additions has not been systematically shown nor has the effect been quantified. The microstructural restoration following the hot deformation of Mg-xZn-yRE (x = 2.5 and 5 wt.%, y = 0 and 1 wt.%, and RE = Gd and Y) alloys has been studied using double hit compression testing and microscopy. It was found that, in the absence of rare earth additions, increases in zinc level had a negligible influence on the kinetics of restoration and the microstructure developed both during extrusion and throughout double hit testing. Adding rare earth elements to Mg-Zn alloys was found to retard restoration of the microstructure and maintain finer recrystallised grains. However, in the Mg-Zn-RE alloys, increasing the zinc concentration from 2.5 wt.% to 5 wt.% accelerated the restoration process, most likely due to a depletion of rare earth elements from solid solution and modification of the particles present in the matrix.

The effect of strain rate on the deformation mechanisms and the strain rate sensitivity of an ultra-fine-grained Al alloy

An ultra-fine-grained Al alloy was subjected to compression tests at different strain rates. The strain rate sensitivity of the flow stress was estimated. A strong effect of the baseline strain rate on the mechanisms of plastic deformation was found. It is suggested that a decrease of strain rate results in activation of micro shear banding due to grain boundary sliding. A connection between the strain rate, strain rate sensitivity, and the prevalent deformation mechanism was established.

Solid state recycling of 5083 Al alloy by hot extrusion

The machined chips of 5083 Al alloy were recycled by hot extrusion at 723 K with an extrusion ratio of 44:1 in air. Corrosion and mechanical properties of the recycled specimens have been compared with those of a virgin extrusion which was processed from the ingot block. As a result of salt immersion tests, mass loss of the recycled specimen was not less than twice of that of the virgin extrusion. The deterioration in corrosion properties for the recycled specimen was attributed to the excessive contamination of Fe which promoted galvanic corrosion. As a result of tensile tests, the recycled specimen exhibited a good combination of high strength and high elongation to failure at room temperature. The excellent mechanical properties for the recycled specimen were attributed to the refined microstructure. However, the elongation to failure of the recycled specimen at elevated temperatures more than 573 K was lower than that of the virgin extrusion. The contamination of oxide particles is likely to be responsible for the lower elongation in the solid recycled specimen.

Deformation mechanisms in an ultra-fine grained Al alloy

This work focuses on the deformation behavior of an ultra-fine grained Al-Mg-Si alloy processed by equal channel angular pressing over a wide range of temperatures and strain rates. The effect of temperature and strain rate on the homogeneity of plastic deformation, the evolution of microstructure, the strain rate sensitivity and the underlying deformation mechanisms are investigated. It is demonstrated that the localization of plastic deformation at the micro scale is triggered by grain boundary sliding due to grain boundary sliding due to grain boundary diffusion. The contributions of different deformation mechanisms during the plastic deformation of the material are discussed.

Biodegradable Mg-Ca and Mg-Ca-Y alloys for regenerative medicine

In this study, Mg-xCa (x = 0.5, 1.0, 2.0, 5.0, 10.0, 15.0 and 20.0 %, wt.%, hereafter) and Mg-1Ca-1Y alloys were investigated as new biodegradable bone implant materials. The compressive strength, ultimate strength and hardness of the Mg-Ca alloys increased, whilst the corrosion rate and biocompatibility decreased, with the increase of the Ca content in the Mg-Ca alloys; higher Ca content caused the Mg-Ca alloy to become brittle. Solutions of simulated body fluid (SBF) and modified minimum essential media (MMEM) with the immersion of Mg-xCa and Mg-1Ca-1Y alloys showed strong alkalisation. The yttrium addition to the Mg-Ca alloys does not improve the corrosion resistance of the Mg-1Ca-1Y alloy as expected compared to the Mg-1Ca alloy. It is suggested that Mg-Ca alloys with Ca additions less than 1.0 wt.% exhibited good biocompatibility and low corrosion rate.

Effect of alloying and extrusion temperature on the microstructure and mechanical properties of Mg-Zn and Mg-Zn-RE alloys

Extruded Mg-Zn-RE alloys have been shown to exhibit excellent combinations of yield strength and ductility, but it is not completely clear how adding rare earth metals to Mg-Zn alters the microstructure and affects the mechanical properties. Microstructural changes and the resulting mechanical properties from changes in composition and extrusion temperature have been investigated for Mg-. x Zn-. y RE (. x=2.5 and 5. wt.%, y=0 and 1. wt. %, and RE=Gd and Y) alloys. Adding RE to Mg-Zn increased the strength and reduced the ductility, while increasing the zinc concentration in the Mg-Zn-RE alloys had the reverse effect.

Precipitation processes in Al-Cu-Mg-Sn and Al-Cu-Mg-Sn-Ag

Microalloying trace elements into aluminum alloys have been shown to improve mechanical properties by altering the precipitation process. Here, trace amounts of Sn and (Sn + Ag) have been added to Al-1.1Cu-1.7Mg (at.%) and the effects have been investigated by a combination of hardness testing and transmission electron microscopy (TEM). Hardness testing shows that the addition of Sn increases the hardness throughout the ageing process, and in combination with Ag, further increases the hardness and shortens the time to reach the peak hardness. The increase in hardness via Sn microalloying is attributed to the homogeneous distribution of S phase (Al2CuMg) precipitates. In the alloy microalloyed with both Sn and Ag, the microstructure is dominated by homogeneously distributed Ω phase (Al2Cu) precipitates in the peak strengthened condition. Given that neither spherical β-Sn precipitates, nor any other obvious nucleation sites for the Ω phase precipitates were observed using TEM, the mechanism for development of such homogeneous precipitation remains to be determined.

Effect of Zn concentration and grain size on prismatic slip in Mg-Zn binary alloys

Mg-Zn binary alloys with concentrations between 0 and 2.8wt% Zn have been prepared and processed via hot rolling and annealing to produce specimens with a strong basal texture and a range of grain sizes. These have been deformed in tension, a condition in which the deformation is dominated by prismatic slip. This data has been used to assess the Hall-Petch parameter as a function of Zn concentration for deformation dominated by prismatic slip. Pure magnesium showed non-linear Hall-Petch behaviour at large grain sizes, and this is compared to the values for prismatic slip measured on single crystals. The differences between critical resolved shear stress measurements made through single crystal, polycrystal and mathematical modelling techniques are also discussed.

Microstructural development and mechanical properties in wrought Mg-Zn-RE alloys

Magnesium-zinc alloys with and without rare earth metals were examined. Particles form when rare earth metals are present and these affect the development of the internal structures in the alloys. Finer, more numerous and more uniformly distributed particles result in alloys with the best combination of high strength and ductility.

Na partitioning during thermomechanical processing of an Mg-Sn-Zn-Na alloy

Microstructural characterization was used to examine the changes that occur in an Mg-6Sn-5Zn-0.3Na alloy from casting to extrusion at either 623 K or 723 K (350 _C or 450 _C) followed by artificial aging at 473 K (200 _C). In particular, the partitioning of Na was examined at each step using STEM-EDS mapping. Na atoms were found to preferentially partition to the Mg-Zn phase when present. After extrusion, when no Mg-Zn was observed, the spherical Mg2Sn particles were found to be enriched in Na, particularly at the higher extrusion temperature. Artificial aging following extrusion resulted in a change in Na partitioning, and a coarse distribution of Mg-Zn precipitate rods. Na microadditions led to a high as-extruded hardness, but a significant tension–compression yield asymmetry was still observed at room temperature. The compressive yield strength was found to decrease significantly after 1000 hours of aging.

A Mg-Al-Nd alloy produced via a powder metallurgical route

A Mg-5 wt.%Al-2 wt.%Nd alloy has been prepared by a powder metallurgical route using a blend of two dissimilar alloy powders. The initial consolidation of the powders was achieved through a single equal channel angular extrusion pass at 150 °C. After heat treatment at temperatures between 420 °C and 530 °C, it was possible to produce a microstructure that consisted of a uniform distribution of Al3Nd and Al11Nd3 precipitates in a magnesium matrix. These precipitates displayed distinct orientation relationships with the matrix. The size and shape of the precipitates depended on the heat treatment temperature and time. © 2009 Elsevier B.V. All rights reserved.