LiI-doped N,N-Dimethyl-Pyrrolidinium iodide, an archetypal rotator-phase ionic conductor

N,N-Dimethyl-pyrrolidinium iodide, and the effect of doping with LiI, has been investigated using DSC, NMR, and impedance spectroscopy. It was found that the addition of a small amount of LiI enhances the ionic conductivity by up to 3 orders of magnitude for this ionic solid. Furthermore, a slight decrease in phase transition onset temperatures, as well as the appearance of a superimposed narrow line in the ¹H NMR spectra with dopant, suggest that the LiI facilitates the mobility of the matrix material, possibly by the introduction of vacancies within the lattice. ⁷Li NMR line width measurements reveal a narrow Li line width, decreasing in width and increasing in intensity with temperature, indicating mobile Li ions.

Plastic crystal behaviour in tetraethylammonium dicyanamide

The plastic crystal tetraethylammonium dicyanamide ([N_2,2,2,2][dca]) has been investigated with an emphasis on structure and dynamics in the plastic phase. It was found that almost all of the volume expansion occurs at the II → I transition, with no volume expansion at the melt transition (as normally observed for crystals). The conductivity of this material shows a rapid increase at temperatures below the II → I transition, reaching values ~ 10^{− 3} S/cm in Phase I, and 0.1 S/cm in the melt. The NMR measurements show that there is a sudden onset of rotational motions of the cations at the plastic transition; below this temperature the cations appear static. The rotational motion of the cation in Phase I has been discussed in terms of isotropic tumbling.

N-methyl-N-alkylpyrrolidinium bis(perfluoroethylsulfonyl)amide ([NPf2]–) and tris(trifluoromethanesulfonyl)methide ([CTf3]–) salts : synthesis and characterization

Novel salts based the pyrrolidinium cation [C_nmpyr]⁺ (where n denote the number of carbons in the straight alkyl chain) and either the [NPf₂]^– or [CTf₃]^– anions have been synthesized and characterized to determine their thermal behaviour, stability, and conductivity. [C₁mpyr][NPf₂], [C₂mpyr][NPf₂], and [C₁mpyr][CTf₃] exhibit behaviour indicative of a plastic crystal phase. Both [C₃mpyr][NPf₂] and [C₄mpyr][NPf₂] are RTILs, while all of the [CTf₃]^– salts, have melting points above 60°C. [C₃mpyr][NPf₂] exhibited the widest electrochemical window of 5.5 V. The [NPf2]– salt exhibited similar reductive limits to the [NTf₂]^– anion, –3.2 V versus Fc⁺|Fc, while [CTf₃]^– had lower reductive stability. The [CTf₃]^– salts were more stable towards oxidation, +2.5 V versus Fc⁺|Fc, compared to the [NPf₂]^– and [NTf₂]^– salts.

Unusual phase behaviour of the organic ionic plastic crystal N,N-dimethylpyrrolidinium tetrafluoroborate

Analysis of N,N-dimethylpyrrolidinium tetrafluoroborate by ¹H and ¹¹B NMR, Raman spectroscopy and powder XRD shows that this organic ionic plastic crystal material exhibits unusual phase behaviour. ¹H NMR analysis indicates that the mobility of the pyrrolidinium cation decreases when the material is heated into phase I, while the X-ray diffraction pattern changes from a simple, one peak structure in phase II to a more complex pattern in phase I. The possible origins of these unusual transitions are discussed.