Dynamic recrystallization of austenite in Ni-30 Pct Fe model alloy : microstructure and texture evolution

The microstructure and crystallographic texture development in an austenitic Ni-30 pct Fe model alloy was investigated within the dynamic recrystallization (DRX) regime using hot torsion testing. The prominent DRX nucleation mechanism was strain-induced grain boundary migration accompanied by the formation of large-angle sub-boundaries and annealing twins. The increase in DRX volume fraction occurred through the formation of multiple twinning chains. With increasing strain, the pre-existing Σ3 twin boundaries became gradually converted to general boundaries capable of acting as potent DRX nucleation sites. The texture characteristics of deformed grains resulted from the preferred consumption of high Taylor factor components by new recrystallized grains. Similarly, the texture of DRX grains was dominated by low Taylor factor components as a result of their lower consumption rate during the DRX process. The substructure of deformed grains was characterized by “organized,” banded subgrain arrangements, while that of the DRX grains displayed “random,” more equiaxed subgrain/cell configurations.

The microstructure evolution and softening processes during high-temperature deformation of a 21Cr-10Ni-3Mo duplex stainless steel

The austenite and ferrite microstructure evolution and softening mechanisms have been investigated in a 21Cr-10Ni-3Mo duplex stainless steel, containing about 60% austenite, deformed in torsion at 1200°C using a strain rate of 0.7 s-1. The above experimental conditions led to the formation of a small volume fraction of new austenite grains through discontinuous dynamic recrystallization (DDRX), which could not account for the observed large softening on the flow curve. DDRX grains mainly formed through the strain-induced migration of the pre-existing austenite grain boundaries, known to dominate in single-phase austenite, complemented by subgrain growth in the interface regions with ferrite. A significant portion of austenite dynamic softening has been attributed to the large-scale subgrain coalescence, the extent of which increased with strain, which seems to have contributed substantially to the observed flow stress decrease. The above process thus appears to represent an alternative mode of austenite dynamic softening to the classical DDRX in the duplex austenite/ferrite microstructure, characterised by limited availability of the pre-existing austenite/austenite high-angle boundaries, deformed at a high temperature. The softening mechanism within ferrite has been classified as "continuous DRX", characterised by a gradual increase in misorientations between neighbouring subgrains with strain and resulting in the progressive conversion of subgrains into "crystallites" bounded partly by low-angle and partly by large-angle boundaries.

Dynamic softening of ferrite during large strain warm deformation of a plain-carbon steel

The evolution of dynamic ferrite softening in a plain-carbon steel was investigated by torsion tests during warm deformation at 810 °C, in the two-phase (ferrite + austenite) region, and strain rate of 0.1 s−1 with different strains up to 50. The warm flow behaviour and ferrite microstructural parameters, such as grain size, misorientation angle across ferrite/ferrite boundaries, and the fraction of high-angle and low-angle grain/subgrain boundaries were quantified using electron back scatter diffraction. The results show that with increasing strain up to not, vert, similar2, the ferrite grain size and fraction of high-angle boundaries rapidly decrease and the fraction of low-angle boundaries increases. However, these parameters remain approximately unchanged with increasing strain from not, vert, similar2 to 50. The dynamic softening mechanism observed during large strain ferritic deformation is explained by dynamic recovery and continuous dynamic recrystallization.

Characterization on ferrite microstructure evolution during large strain warm torsion testing of plain low carbon steel

Ferrite grain/subgrain structures evolution during the extended dynamic softening of a plain low carbon steel was investigated throughout the large strain warm deformation by hot torsion. Microstructural analysis with electron back-scattering diffraction (EBSD) scanning electron microscope (FEG/SEM) was carried out on the ferrite microstructural parameters. The results showed that the warm flow stress–strain curves are similar to those affected only by dynamic softening and an extended warm flow softening is seen during large strain deformation up to 30. Furthermore, with an increase in strain up to ~ vert, similar1 the grain size of ferrite, misorientation angle and fraction of high-angle boundaries gradually decrease and fraction of low-angle boundaries increases. With a further increase in the strain beyond ~, vert, similar2, these parameters remain approximately unchanged. No evidence of discontinuous dynamic recrystallisation involving nucleation and growth of new grains was found within ferrite. Therefore, the dynamic softening mechanism observed during large strain ferritic deformation is explained by continuous dynamic recrystallization (CDRX).