Microstructural analysis of pre-strained TRIP steel after fatigue testing

The widespread introduction of multiphase sheet steels in the automotive industry has led to considerable interest in the fatigue properties of these materials. The different microstructural phases within matelials such as TRIP steels can influence the fatigue behaviour due to the manner in which the cyclic strain is accommodated within these phases. In this study fully reversed straincontrolled fatigue tests were perfonnrmed on a commercially-produced uncoated TRIP 780 steel both in the as-received and 20 % prestrained condition. The pre-strained TRIP steel showed significant cyclic softening at higher strain amplitudes, whereas some initial work hardening was observed at lower strain amplitudes before cyclic softening. The cyclic stabilised strength of the pre-strained TRIP steel was independent of strain amplitude, while the cyclic stabilised strength of the as-received TRIP steel increased with strain amplitude. Transmission Electron Microscopy TEM was used to examine the effect of the cyclic deformation on the microstructure of the different conditions, with the differences in fatigue behaviour explained based on the differences in the deformation structure formed within the steel (i.e. dislocation density and sub-structure and microband formation).

Warm deformation and annealing behaviour of iron-silicon-(carbon) steel sheets

Single pass warm rolling and compression experiments were carried out from ambient to 800°C for ultra-low carbon (ULC) steel with ∼100 ppm carbon and interstitial free (IF) steels, both with two levels of silicon. Subsequently, annealing was done in order to recrystallize the deformed specimens. The main purpose of this study was to understand the effects of rolling temperature and silicon on stress responses and textures. This study comprises two main themes: flow stress and strain rate sensitivity during compression and shear banding and textures in warm rolled specimens. The effects of deformation temperature on in-grain shear bands were different between ULC-Si and IF-Si steels. As in previous work with more conventional steels, in-grain shear bands in the IF grade had low sensitivity to rolling temperature, while those in the ULC grade depended significantly on the deformation temperature. However, the temperature profile of shear banding in the ULC grade was approximately 150°C higher than in previous work. Deformation and recrystallisation textures for both IF and ULC grades depended on their rolling temperatures. The variation of both grain size and texture after annealing can be explained by the rise and fall of in-grain shear banding activity which is related to the strain rate sensitivity.

Ultrafine grained ferrite formed by interrupted hot torsion deformation of plain carbon steel

A plain carbon steel was deformed using a hot torsion deformation simulator. A schedule known to produce strain-induced ferrite was used with the strain interrupted for increasing intervals of time to determine the effect of an isothermal hold on the final microstructure. Microscopy and electron back-scattered diffraction (EBSD) were used to analyse the changes that occurred in the partially transformed microstructure during the hold and the subsequent applied strain. The strain-induced ferrite coarsened during the hold and this coarsened ferrite was refined during the second deformation. These results were compared to those obtained for a different plain carbon steel deformed in single pass rolling close to the Ar3 temperature.

Fragmentation of orientation within grains of a cold-rolled interstitial-free steel

The formation of a favourable recrystallization texture in interstitial-free (IF) steels depends on the availability and activation of particular nucleation sites in the deformed microstructure. This paper presents a description of the deformed microstructure of a commercially cold-rolled IF steel, with particular emphasis on the microstructural inhomogeneities and short-range orientational variation that provide suitable nucleation sites during recrystallization. RD-fibre regions deform relatively homogeneously and exhibit little short-range orientational variation. ND-fibre regions are heavily banded and exhibit considerable short-range orientational variation associated with the bands. While the overall orientational spread of ND-fibre grains frequently is about the ND-axis, the short-range orientational variation often involves rotation about axes in the TD-ND plane that are nearer to the TD than the ND.

Cr(N,C) diffusion coating formation on pre-nitrocarburised H13 tool steel

The microstructural processes of Cr(N,C) coating formation by thermoreactive deposition and diffusion (TRD) on pre-nitrocarburised H13 tool steel were studied. Both nitrocarburising and TRD were performed in fluidized bed furnaces at 570 °C. During TRD, chromium was transferred from chromium powder in the fluidized bed, to the nitrocarburised substrates by gas-phase reactions initiated by reaction of HCl gas with the chromium. Addition of 30% H2 to the input inert gas was found to increase the rate of coating formation, although hydrogen reduction resulted in rapid loss of nitrogen to the surface. The reason for the increased rate of coating formation could not be established without further investigation, although several possible explanations have been proposed. It was found that porosity and the formation of an iron nitride ‘cover layer’ during nitrocarburising were the biggest influences on the microstructure of the Cr(N,C) coating. Microstructural characterization of the coatings was performed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and glow discharge optical emission spectroscopy (GDOES).

Characterisation of galvanneal coatings on strip steel

Galvanneal is a form of zinc-coated sheet steel, where steel is dipped in molten zinc, and then heat treated in a furnace to produce a complex iron-zinc coating. Many industries, such as automotive, use galvanneal for components fabricated from sheet steel. The microstructural properties of galvanneal have a significant influence on how well the sheet metal changes shape on stamping. By means of optical microscopy, scanning electron microscopy, and glow-discharge optical emission spectrometry, we present a study of the microstructure of several galvanneal samples, both stamped and unformed, relating the phases and morphology of the coatings to performance in stamping operations. Samples of galvanneal were subjected to different heat-treatment temperatures. The frequency of defects in stamped components was found to be related to the average alloy content in the coatings, which varied with furnace temperature. An increased average iron content in the coatings was related to increased powdering defects in stamping operations that use galvanneal coated sheet steel.

Influence of the geometry of an immersed steel workpiece on mass transfer coefficient in a chemical heat treatment fluidised bed

The mass transfer during carburising in a fluidised bed and in a steel workpiece has been studied experimentally in this work. This involved carburising experiment in an electrically heated fluidised bed at 900–970°C with natural gas and air as the atmosphere. A steel workpiece was designed to provide a range of carbon transfer surfaces of different geometries in the fluidised bed, and the carbon transfer coefficient was measured at these surfaces. The carbon transfer coefficient was determined from the carbon distribution within the diffusion layer of the sample. An empirical relationship of the carbon potential as a function of carburising atmosphere, bed temperature and fluidising velocity was determined, based on the understanding of the mass transfer mechanism and analysis of the experimental results.

The static and metadynamic recrystallization behaviour of an X60 Nb Microalloyed Steel

A rapid method has been developed to determine recrystallization kinetics of Nb microalloyed steels by interrupted hot torsion test. The softening behaviour was achieved as a function of different processing parameters. The method clearly identified three regions, where the strain dependency of the recrystallization rate varied. Firstly, at large strains the rate of recrystallization was not a function of strain; this is generally ascribed to metadynamic recrystallization. At lower strains the time to 50% recrystallization showed a power low relationship with strain, characteristic of static recrystallization. A further break point exists on the time for 50% softening curve when strain induced precipitation occurs in the material. The onset of strain induced precipitation was at strains below the strain to the peak stress at temperatures below 900°C. The experimental results were used to estimate the time for 50% softening and to anticipate the onset of the strain induced precipitation for the alloy of this study. Grain refinement of the recrystallized austenite continued to strains significantly beyond the peak stress and beyond the static to metadynamic recrystallization rate transition.

Local Austenite grain size distribution in hot bar rolling of AISI 4135 Steel

In this paper, the local distribution of austenite grain size (AGS) was experimentally determined by conducting single round-oval and square-diamond pass hot bar rolling experiments of AISI4135 steel. The rolling experiments were carried out using the laboratory mill. The local distribution of AGS was also determined numerically. In order to predict AGS distribution, the AGS evolution model was combined with three dimensional non-isothermal finite element analyses by adopting a modified additivity rule. AGS evolution model was experimentally determined from hot torsion test according to Hodgson's model. The predicted results were in a reasonably good agreement with experimental results.