Strain hardening behavior of high performance FBDP, TRIP and TWIP steels

Based on n-value differential equation and microstructural observation, strain hardening behaviors of FBDP, TRIP, and TWIP steels during uniaxial tension were investigated. TRIP steel exhibits both superior strength and ductility than FBDP steel, and TWIP steel displays much higher total and uniform elongations in comparison to FBDP and TRIP steels. The instantaneous n values of FBDP and TRIP steels increase at small strains, reach a maximum value, smoothly decrease at higher strains, and then rapidly drop up to the specimen rupture. The strain hardening of TRIP steel persists at higher strains where that of FBDP steel begins to diminish. TWIP steel exhibits gradually increased instantaneous n values over the whole uniform plastic deformation, implying that TWIP steel shows a much larger strain hardening capability than FBDP and TRIP steels.

Characterization of microstructures and tensile properties of TRIP-aided steels with different matrix microstructure

Three different heat treatment processes have been proposed as a fundamental method to produce three kinds of TRIP-aided steels with polygonal ferritic matrix (F-TRIP), bainitic matrix (B-TRIP) and martensitic matrix (M-TRIP) in a newly designed low alloy carbon steel. By means of dilatometry study and detailed characterization, the relationships among transformation, microstructure and the resulting mechanical behavior were compared and analyzed for the three cases. The work hardening of the samples was evaluated by calculating the instantaneous n value as a function of strain. The M-TRIP sample exhibits the highest strength with the highest work hardening rate at low strains and subsequent rapid descending at high strains. In contrast, the B-TRIP sample has relatively high continuously constant work hardening behavior over strain levels greater than 0.067. The difference in work hardening behavior corresponds directly to the rate of the retained austenite-martensitic transformation during straining, which can be attributed to the carbon content, the morphology of the retained austenite and the matrix microstructure in the respective TRIP-aided samples. © 2014 Elsevier B.V.