The kinetics of two-stage formation of TiAl3 in multilayered Ti/Al foils prepared by accumulative roll bonding

The solid-state reactions of Ti/Al multilayered samples produced by Accumulative Roll Bonding (ARB) have been investigated using differential scanning calorimetry, X-ray diffraction and scanning electron microscopy. The kinetics of the formation of the intermetallic compound TiAl3 was highlighted. Experimental evidence and analysis of the data shows that, there was a two-stage process in the formation of TiAl₃ in the ARB Ti/Al reactive multilayered samples. Calorimetric and microstructural analyses also suggest that the interdiffusion of Al and Ti which led to solid solutions preceded the formation of intermetallic compounds. Despite the apparent chaos in the thickness of the ARB multilayered samples, the distribution of layer spacing did not become broad enough to lose the main features of the double exothermal behaviour. Isothermal DSC shows a larger Avarami constant in ARB Ti/Al multilayered structures than was found in Ti/Al thin films. A modified model based on thin films was set up to describe the kinetic characteristics of the formation of the intermetallic compound TiAl₃ in ARB samples.

Bimetallic copper-aluminium tube by severe plastic deformation

A new process of joining tubes from different materials to a bimetallic tube based on a combination of large shear and high hydrostatic pressure is proposed. It results in improved mechanical locking of surface asperities, along with enhanced diffusivity owing to the ultrafine-grained microstructure produced. This is augmented by a temperature increase due to heat release associated with mechanical work. Electron microscopy characterization of the interface and the adjacent regions supports the hypothesis of enhanced interdiffusion.

Asymmetric accumulative roll bonding of aluminium-titanium composite sheets

Aluminium-titanium (Al/Ti) composite sheets were fabricated via asymmetric accumulative roll bonding (AARB), which capitalises on additional shear to enhance plastic deformation. Multi-layers of Al alloy (AA1050) and commercially-pure Ti sheets were alternatively stacked and rolled-bonded with varied roll diameter ratios (dr) ranging from 1 to 2, for up to four passes. Annealing of selected composite sheets was subsequently carried out at 600°C for 24h to compare the rates of solid-state diffusion reactions between Al and Ti components. Mechanical tests revealed that both tensile strength and ductility of the sheets increase systematically with dr. The microstructures and the Al/Ti interfaces of the sheets were analysed in detail using TEM, SEM and FIB techniques. It is shown that not only does AARB lead to a more refined grain size of the Al matrix but also it promotes the development of a nanostructured surface layer on Ti that comprises crystallites of 50-100nm in size, which is otherwise absent in the case of symmetric ARB (i.e. dr=1). The AARB-processed sheets exhibit a larger thickness of the interdiffusion layer at the Al/Ti interfaces than the counterparts processed via the symmetric ARB route, the difference being in excess of 15%. The effects and the implications of AARB processing on mechanical behaviour and diffusion kinetics are discussed with respect to the microstructural evolutions.

Multicomponent materials from machining chips compacted by equal-channel angular pressing

Al and Mg machining chip blends were compacted by equal-channel angular pressing with back pressure. By varying the weight fraction of the constituent materials, temperature and processing route, as well as employing subsequent heat treatment, the microstructure and the mechanical properties of the compact were varied. The width of the interdiffusion zone and the formation of intermetallic phases near the interfaces between the two metals were studied by energy-dispersive X-ray spectroscopy and nanoindentation. It was shown that substantial improvement of mechanical properties, such as an increase of strength, strain-hardening capability and ductility, can be obtained. This is achieved by changing the processing parameters of equal-channel angular pressing and the annealing temperature, as well as by optimising the weight fraction of the constituent metals. © 2013 Springer Science+Business Media New York.