Static and metadynamic recrystallization of interstitial free steels during hot deformation

A rapid method was used to identify kinetics of the recrystallization for two IF (Interstitial Free) steels which have different phosphorous and boron contents. The static and metadynamic softening behaviour of the materials for a range of strain rates and temperatures were quantified. The critical strain for initiation of strain independent softening was estimated for the IF steels in respect to the time for 50 percent softening after deformation. The results showed that the strain for the initiation of strain independent softening (often referred to as metadynamic recrystallization) varies with the Zener Hollomon parameter. Classic static recrystallization was observed at strains below the strain independent softening for all processing conditions and the strain rate had a strong effect on the time for strain independent softening. Results also revealed that static and metadynamic recrystallization was delayed owing to the phosphorous and boron alloying elements. Hence, the large strain at above no-recrystallization temperature may be required for the early stage of Finishing Stands Unit (FSU) in hot strip rolling mills to initiate austenite grain refinement of phosphorous and boron added IF steels.

Mapping the hot deformation microstructure of Ni-30Fe alloy

The evolution of structure during the hot working of an austenitic Ni-30%Fe alloy is studied using EBSD analysis of samples tested in torsion. A microstructural map in temperature-strain space that plots grain size, cell size, fracture and dynamic recrystallization is presented.

Microstructural evolution during hot deformation of duplex stainless steel

The microstructure evolution during hot deformation of a 23Cr-5Ni-3Mo duplex stainless steel was investigated in torsion. The presence of a soft δ ferrite phase in the vicinity of austenite caused strain partitioning, with accommodation of more strain in the δ ferrite. Furthermore, owing to the limited number of austenite/austenite grain boundaries, the kinetics of dynamic recrystallisation (DRX) in austenite was very slow. The first DRX grains in the austenite phase formed at a strain beyond the peak and proceeded to <15% of the microstructure at the rupture strain of the sample. On the other hand, the microstructure evolution in δ ferrite started by formation of low angle grain boundaries at low strains and the density of these boundaries increased with increasing strain. There was clear evidence of continuous dynamic recrystallisation in this phase at strains beyond the peak. However, in the δ ferrite phase at high strains, most grains consisted of δ/δ and δ/γ boundaries.

Feasibility study of partial recrystallisation in multi-pass hot deformation process and application to calculation of mean flow stress

A feasibility study for handling the partial recrystallisation in multi-pass hot deformation where the heterogeneity of microstructure of deformed austenite is inherently accompanied is presented. The proposed model is based on modification of the conventional model in which the microstructure of deformed austenite at each pass is simply taken as being homogeneous during the multi-pass deformation. The usefulness of the modified model has been demonstrated by applying it to a four-pass oval–round (or round–oval) rod rolling sequence. The recrystallised fraction, austenite grain size (AGS) and mean flow stress at each pass computed from the modified model has been compared with those from the conventional model. The result showed that the recrystallisation behaviour and evolution of AGS at a given pass were dependent on the modelling method of the partial recrystallisation in the multi-pass rolling for the case studied. As the rolling speed increased, the difference between the mean flow stresses calculated by the conventional model and the proposed model was gradually larger in accordance with the contribution of partial recrystallisation.

Application of identification techniques to determine effect of carbon content in steels on rheological parameters during hot deformation

The objective of the present work is searching for the correlation between the carbon content in steels and the parameters of the rheological models, which are used to describe the materials behavior during hot plastic deformation. This correlation can be expected in the internal variable models, which are based on physical phenomena occurring in the material. Such a model, based on the dislocation density as the internal variable, is investigated in this work. The experiments including hot torsion tests are used for the analysis.
The procedure is composed of three parts. Plastometric tests were performed for steels with various carbon content. Optimization techniques were applied next to determine the coefficients in the internal variable rheological model for these steels. Two versions of the model are considered. One is based on the average dislocation density and the second accounts for the distribution of dislocation densities. Evaluation of correlation between carbon content and such coefficients in the models as activation energy for self diffusion, activation energy for recrystallization, grain boundary mobility, recovery coefficient etc. was the main objective of the work. In consequence, the model which may be used for simulation of hot forming processes for steels with various chemical compositions, is proposed.

Recrystallization in AISI 304 austenitic stainless steel during and after hot deformation

In order to improve the understanding of the dynamic and post-dynamic recrystallization behaviours of AISI 304 austenitic stainless steel, a series of hot torsion test have been performed under a range of deformation conditions. The mechanical and microstructural features of dynamic recrystallization (DRX) were characterized to compare and contrast them with those of the post-dynamic recrystallization. A necklace type of dynamically recrystallized microstructure was observed during hot deformation at 900 °C and at a strain rate of 0.01 s⁻¹. Following deformation, the dependency of time for 50% recrystallization, t₅₀, changed from “strain dependent” to “strain independent” at a transition strain (ε^*), which is significantly beyond the peak. This transition strain was clearly linked to the strain for 50% dynamic recrystallization during deformation. The interrelations between the fraction of dynamically recrystallized microstructure, the evolution of post-dynamically recrystallized microstructure and the final grain size have been established. The results also showed an important role of grain growth on softening of deformed austenite.

Hot deformation and recrystallization of austenitic stainless steel: Part 11. post-deformation recrystallization

The postdeformation recrystallization behavior of a hot-deformed austenitic stainless steel was investigated based on the first part of this study, in which the microstructure development during hot deformation and, in particular, the evolution of dynamic recrystallization (DRX), was studied. The effect of different parameters such as strain, strain rate, and temperature were examined. The dependency of the time for 50 pct softening, t 50, changed from “strain dependent” to “strain independent” at a transition strain (ε*) that was in the steady-state area of the hot deformation flow curve. The fully recrystallized microstructure showed a similar transition in strain sensitivity. However, this occurred at stains greater than ε*. A mathematical model was developed to predict the transition strain under different deformation conditions. Microstructural measurements show that the transition strain corresponds to approximately 50 pct DRX in the deformed structure at the point of unloading.

Hot deformation and recrystallization of austenitic stainless steel: part 1. dynamic recrystallization

The hot deformation behavior of a 304 austenitic stainless steel was investigated to characterize the evolution of the dynamically recrystallized structure as a starting point for studies of the postdeformation  recrystallization behavior. The effect of different deformation parameters such as strain, strain rate, and temperature were investigated. The flow curves showed typical signs of dynamic recrystallization (DRX) over a wide range of temperatures and strain rates (i.e., different Zener–Hollomon (Z) values). However, under very high or very low Z values, the flow curves’ shapes changed toward those of the dynamic recovery and multiple peaks, respectively. The results showed that while DRX starts at a strain as low as 60 pct of the peak strain, a fully DRX microstructure needs a high strain of almost 4.5 times the initiation strain. The DRX average grain size showed power-law functions with both the Zener–Hollomon parameter and the peak stress, although power-law breakdown was observed at high Z values.

Fine structure of shear bands formed during hot deformation of two austenitic steels

Shear bands formed during both cold and hot plastic deformation have been linked with several proposed mechanisms for the formation of ultrafine grains. The aim of the present work was to undertake a detailed investigation of the microstructural and crystallographic characteristics of the shear bands formed during hot deformation of a 22Cr-19Ni-3Mo (mass%) austenitic stainless steel and a Fe-30 mass%Ni based austenitic model alloy. These alloys were subjected to deformation in torsion and plane strain compression (PSC), respectively, at temperatures of 900°C and 950°C and strain rates of 0.7s_-1 and 10s_-1, respectively. Transmission electron microscopy and electron backscatter diffraction in conjunction with scanning electron microscopy were employed in the investigation. It has been observed that shear bands already started to form at moderate strains in a matrix of pre-existing microbands and were composed of fine, slightly elongated subgrains (fragments). These bands propagated along a similar macroscopic path and the subgrains, present within their substructure, were rotated relative to the surrounding matrix about axes approximately parallel to the sample radial and transverse directions for deformation in torsion and PSC, respectively. The subgrain boundaries were largely observed to be non-crystallographic, suggesting that the subgrains generally formed via multiple slip processes. Shear bands appeared to form through a co-operative nucleation of originally isolated subgrains that gradually interconnected with the others to form long, thin bands that subsequently thickened via the formation of new subgrains. The observed small dimensions of the subgrains present within shear bands and their large misorientations clearly indicate that these subgrains can serve as potent nucleation sites for the formation of ultrafine grain structures during both subsequent recrystallisation, as observed during the present PSC experiments, and phase transformation.

EBSD and TEM investigation of the hot deformation substructure characteristics of a type 316L austenitic stainless steel

The evolution of crystallographic texture and deformation substructure was studied in a type 316L austenitic stainless steel, deformed in rolling at 900 °C to true strain levels of about 0.3 and 0.7. Electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) were used in the investigation and a comparison of the substructural characteristics obtained by these techniques was made. At the lower strain level, the deformation substructure observed by EBSD appeared to be rather poorly developed. There was considerable evidence of a rotation of the pre-existing twin boundaries from their original orientation relationship, as well as the formation of highly distorted grain boundary regions. In TEM, at this strain level, the substructure was more clearly revealed, although it appeared rather inhomogeneously developed from grain to grain. The subgrains were frequently elongated and their boundaries often approximated to traces of {111} slip planes. The corresponding misorientations were small and largely displayed a non-cumulative character. At the larger strain, the substructure within most grains became well developed and the corresponding misorientations increased. This resulted in better detection of sub-boundaries by EBSD, although the percentage of indexing slightly decreased. TEM revealed splitting of some sub-boundaries to form fine microbands, as well as the localized formation of microshear bands. The substructural characteristics observed by EBSD, in particular at the larger strain, generally appeared to compare well with those obtained using TEM. With increased strain level, the mean subgrain size became finer, the corresponding mean misorientation angle increased and both these characteristics became less dependent on a particular grain orientation. The statistically representative data obtained will assist in the development of physically based models of microstructural evolution during thermomechanical processing of austenitic stainless steels.

EBSD study of the orientation dependence of substructure characteristics in a model Fe-30wt%Ni alloy subjected to hot deformation

The aim of the present investigation was to determine the orientation dependence of substructure characteristics in an austenitic Fe−30wt%Ni model alloy subjected to hot plane strain compression. Deformation was carried out at a temperature of 950 °C using a strain rate of 10 s^₋₁ to equivalent strain levels of approximately 0.2, 0.4, 0.6 and 0.8. The specimens obtained were analysed using a fully automatic electron backscatter diffraction technique. The crystallographic texture was characterized for all the strain levels studied and the subgrain structure was quantified in detail at a strain of 0.4. The substructure characteristics displayed pronounced orientation dependence. The major texture components, namely the copper, S, brass, Goss and rotated Goss, generally contained one or two prominent families of parallel larger-angle extended subboundaries, the traces of which on the longitudinal viewing plane appeared systematically aligned along the {111} slip plane traces, bounding long microbands subdivided into slightly elongated subgrains by short lower-angle transverse subboundaries. Relatively rare cube-orientated grains displayed pronounced subdivision into coarse deformation bands containing large, low-misorientated subgrains. The misorientation vectors across subboundaries largely showed a tendency to cluster around the sample transverse direction. Apart from the rotated Goss texture component, the stored energy levels for the remaining components were principally consistent with the corresponding Taylor factor values.

Softening during the hot deformation of steel

The behaviour of steel undergoing hot deformation was examined with the aim of better understanding the softening mechanisms operating during industrial hot strip rolling. These softening mechanisms can significantly influence the deformation force required to attain a given reduction in thickness, and this work answered a number of questions with regard to the transition between softening mechanisms.