Phase dissolution of γ-Mg17Al12 during homogenization of As-Cast AZ80 magnesium alloy and its effect on room temperature mechanical properties

As-cast AZ80 Mg alloy contains α-Mg, partially divorce eutectic of α and γ (Mg 17Al 12), fully divorce eutectic of α and γ, and lamellar eutectic of α and γ phases. During homogenization, second phase (γ-Mg 17Al 12) gets dissolved can change the mechanical properties. Therefore, the aim of the present work is to bring out the kinetics of dissolution of γ phase and evaluate its effect on mechanical properties. Microstructure evolution during homogenization was investigated as a function of time for 0.5 to 100 h and at the temperatures of 400° and 439°C. In as-cast state, this material was found to contain 70% α-Mg and 30% eutectic phase. With increasing homogenization time, dissolution of lamellar eutectic occurs first which is followed by dissolution of fully divorce eutectic and partially divorce eutectic. The dissolution kinetics of γ phase was analyzed based on the decrease in its volume fraction as a function of time. The time exponent for dissolution was found to be 0.38 and the activation energy for the dissolution of γ phase was found to be 84.1 kJ/mol. This dissolution of γ phase leads to decrease in hardness and tensile strength with increase in homogenization time.

On low temperature bainite transformation characteristics using in-situ neutron diffraction and atom probe tomography

In-situ neutron diffraction was employed to monitor the evolution of nano-bainitic ferrite during low temperature isothermal heat treatment of austenite. The first 10 peaks (austenite, γ and ferrite, α) were monitored during austenization, homogenization, rapid cooling and isothermal holding at 573 K. Changes in the α-110 and γ-111 peaks were analysed to determine the volume fraction changes and hence the kinetics of the phase transformation. Asymmetry and broadening in the α-200 and γ-200 peaks were quantified to lattice parameter changes due to carbon redistribution as well as the effects of size and dislocation density. Atom Probe Tomography was used to confirm that, despite the presence of 1.5 mass % Si, carbide formation was evident. This carbide formation is the cause of poor ductility, which is lower than expected in such steels.

Kinetics of γ-Mg17Al12 phase dissolution and its effect on room temperature tensile properties in as-cast AZ80 magnesium alloy

As-cast AZ80 magnesium alloy consists of α-Mg, eutectic product of α-Mg and γ-Mg17Al12, with the latter present in the form of partially and fully divorce eutectic. There occurs dissolution of harder γ-Mg17Al12 phase during homogenization treatment at 400 ° and 439 °C. The proportion of the α-Mg and γ-Mg17Al12 phase was varied by solutionizing the alloy for various lengths of time at these temperatures, in order to investigate the kinetics of phase transformation and to evaluate the effect of phase proportion, size and morphology on room temperature tensile properties. It was found that the yield strength decreases with the increase in solutionizing temperature from 400° to 439 °C and at the same time, ductility in general increases with the increasing solutionizing temperature. The variation in tensile properties and the nature of fractographs were analyzed in terms of the effects of microstructure. © (2014) Trans Tech Publications, Switzerland.