Gamma-irradiated carbon nanotube yarn as substrate for high-performance fiber supercapacitors

As an electrical double layer capacitor, dry-spun carbon nanotube yarn possesses relatively low specific capacitance. This can be significantly increased as a result of the pseudocapacitance of functional groups on the carbon nanotubes developed by oxidation using a gamma irradiation treatment in the presence of air. When coated with high-performance polyaniline nanowires, the gamma-irradiated carbon nanotube yarn acts as a high-strength reinforcement and a high-efficiency current collector in two-ply yarn supercapacitors for transporting charges generated along the long electrodes. The resulting supercapacitors demonstrate excellent electrochemical performance, cycle stability, and resistance to folding-unfolding that are required in wearable electronic textiles.

The effect of laser power density on the fatigue life of laser-shock-peened 7050 aluminium alloy

Laser shock peening (LSP) is an innovative surface treatment method that can result in significant improvement in the fatigue life of many metallic components. The process produces very little or no surface profile modification while producing a considerably deeper compressive residual stress layer than traditional shot peening operations. The work discussed here was designed to: (a) quantify the fatigue life improvement achieved by LSP in a typical high strength aircraft aluminium alloy and (b) identify any technological risks associated with its use. It is shown that when LSP conditions are optimal for the material and specimen configuration, a —three to four times increase in fatigue life over the as-machined specimens could be achieved for a representative fighter aircraft loading spectrum when applied at a representative load level. However, if the process parameters are not optimal for the material investigated here, fatigue lives of LSP treated specimens may be reduced instead of increased due to the occurrence of internal cracking. This paper details the effect of laser power density on fatigue life of 7050-T7451 aluminium alloy by experimental and numerical analysis.