Sol-gel derived HA/TiO2 double coatings on Ti scaffolds for orthopaedic applications

Hydroxyapatite/titania (HA/TiO₂) double layers were coated onto Ti scaffolds throughout for orthopaedic applications by sol-gel method. Differential scanning calorimetry (DSC), thermogravimetric analysis (TG) and X-ray diffractometry (XRD) were used for the characterisation of the phase transformations of the dried gels and coated surface structures. Scanning electron microscope (SEM) equipped with energy dispersive spectrometry (EDS) was used for the observation and evaluation of the morphology and phases of the surface layers and for the assessment of the in vitro tests. The in vitro assessments were performed by soaking the HA/TiO₂ double coated samples into the simulated body fluid (SBF) for various periods. The TiO₂ layer was coated by a dipping-coating method at a speed of 12 cm/min, followed by a heat treatment at 600 °C for 20 min. The HA layer was subsequently dipping-coated on the outer surface at the same speed and then heat-treated at difference temperatures. The results indicat that the HA phase begins to crystallize after a heat treatment at 560 °C. The crystallinity increases obviously at 760 °C. SEM observations find no delamination or crack at the interfaces of HA/TiO₂ and TiO₂/Ti. The HA/TiO₂ coated Ti scaffolds displays excellent bone-like apatite forming ability when it is soaked into SBF. Ti scaffolds after HA/TiO₂ double coatings can be anticipated as promising implant materials for orthopaedic applications

11B nuclear magnetic resonance study of boron nitride nanotubes prepared by mechano-thermal method

We reported ¹¹B nuclear magnetic resonance studies of boron nitride (BN) nanotubes prepared by mechano-thermal route. The NMR lineshape obtained at 192.493 MHz (14.7 T) was fitted with two Gaussian functions, and the ¹¹B nuclear magnetization relaxations were satisfied with the stretched–exponential function, exp[-(tlT₁)^(D+1)/6] (D: space dimension) at all temperatures. In addition, the temperature dependence of spin–lattice relaxation rates was well described by T_i^-1 = aT (a: constant, T: temperature) and could be understood in terms of direct phonon process. All the 11BNMR results were explained by considering the inhomogeneous distribution of the paramagnetic metal catalysts, such as α-Fe, Fe–N, and Fe₂ B, that were incorporated during the process of high-energy ball milling of boron powder and be synthesized during subsequent thermal annealing. X-ray powder diffraction as well as electron paramagnetic resonance (EPR) on BN nanotubes were also conducted and the results obtained supported these conclusions.

Catástrofes naturales y seguro en Australia: ¿Ha llegado la hora de un sistema nacional de seguros de desastres naturales?

This article examines the legal and regulatory framework for insurance in Australia and the concrete measures taken to manage property damage from natural disasters. Doing so will examine how recent reports have recommended the need for a specific solution for insurance against natural disasters.