Optimization of alloy design and hot rolling conditions for shape memory in Fe–Mn–Si-based alloys

The effect of composition and hot rolling conditions on the shape memory effect (SME) in the Fe–Mn–Si-based system has been studied to obtain improved shape memory without the need to rely on “training”. It has been found that the texture is not markedly affected by rolling conditions, and texture is therefore not a major factor in explaining variations in SME with processing conditions. Decreasing the pre-deformation temperature to below the Ms was found to have a beneficial effect on shape memory. It was found that the best SME was achieved in an alloy that had Ms just above room temperature, and had been processed by hot rolling followed by recovery annealing. Alloys of different compositions exhibited different optimum rolling temperatures for maximum shape memory performance.

Re-examination of the effect of NbC precipitation on shape memory in Fe-Mn-Si-based alloys

Current literature pertaining to the shape memory effect in the Fe–Mn–Si-based system is critically discussed. It is argued that the
enhanced shape memory previously attributed to NbC precipitation is mainly due to the associated thermo-mechanical treatments.
It is concluded that the thermo-mechanical processing of the alloy is the dominant factor that determines the shape memory effect in
this alloy system.

Effect of second-phase particles on shape memory in Fe-Mn-Si-based alloys

The shape memory behaviour of two Fe–Mn–Si-based alloys has been investigated. One alloy was a reference alloy, and the other alloy was
similar in composition except that it contained 0.55 wt% Ti. Following solution treatment and quenching, strip samples were subjected to three types
of treatments; isothermal holding, cold rolling followed by isothermal holding, and hot rolling followed by isothermal holding. These treatments
resulted in the formation of intermetallic precipitates in the Ti-containing alloy, while the reference alloy remained precipitate-free. In comparing
the shape memory of the reference and the particle-containing alloy after identical heat treatments, it was found that the formation of precipitates
had a beneficial effect on the shape memory in all cases. In general, the larger precipitates caused a larger increase in the shape memory. The effect
of particle size on shape memory has been analysed using the current data and published results for a range of precipitate types.

Study on microstructure characteristics of steel in two-body abrasive wear.

This study was focussed on understanding the abrasive wear mechanism occurring in mining and mineral processing industries. The outcome of this research will aim to produce better ferrous alloys to combat abrasion, thereby bringing down the financial losses.

Thermo-mechanical processing and the shape memory effect in an Fe–Mn–Si-based shape memory alloy

The effect of cold rolling and annealing on the shape memory effect (SME) in an Fe–Mn–Si-based alloy has been studied. It has been found
that the SME in these alloys can be significantly increased by the appropriate thermo-mechanical processing (TMP). The optimum conditions
were found to be 15% cold rolling followed by annealing at 800 ◦C for 15 min. This produced a total strain recovery of 4.5%. TEM showed that
this processing schedule produces a microstructure of evenly spaced, and well defined stacking faults throughout the parent phase. It is shown for
the first time that samples processed in this way produce a larger fraction of martensite compared to samples in the as-austenitized condition. It
is concluded that the stacking faults induced by TMP act as nucleation sites for martensite formation during deformation. The SME is improved
primarily as a result of the increased amount of martensite that is formed in this condition.

Performance of wrought aluminium and magnesium alloy tubes in three-point bending

This present work examines the load carrying capacity, energy absorption and fracture characteristics of wrought magnesium and aluminium alloy tubes in three-point bending. Magnesium alloy AZ31, and aluminium alloys 6063 and 7075, were extruded into cylindrical tubes of both equivalent thickness and mass. A strong thickness effect was present meaning that the AZ31 tube had significantly higher load and energy absorption performance than an equivalent mass 6063 tube, albeit not as high as the 7075 tube. Hinge formation and maximum load was delayed for the magnesium alloy, meaning that a high energy absorption rate persisted to higher deformation displacements than the aluminium alloys. It was also found that fracture during deformation was dependent on the indenter diameter, tube thickness and lower support separation.

Recrystallization during and following hot working of magnesium alloy AZ31

The microstructures of magnesium AZ31 are examined following hot compression testing and annealing. The grain size, fraction dynamically recrystallized and, in a couple of cases, the crystallographic texture are reported. It was found that the progress of dynamic recrystallization is strongly sensitive to processing conditions but that the dynamically
recrystallized grain size was less sensitive to stress than in other metals. It was also found that, for structures containing between 80 and 95 % dynamic recrystallization, abnormal grain growth occurs during annealing. The crystallographic texture produced is also sensitive to the deformation conditions.

Fabrication of novel metal alloy foams for biomedical applications

Degeneration of the weight bearing bones of the ageing population often requires the inception of metallic biomaterials. Research in this area is receiving increased attention globally. However, most of today's artificial bone materials are dense and suffer from problems of adverse reaction, biomechanical mismatch and lack of appropriate space for the regeneration of new bone tissues. In the present study, novel ZrTi alloy foams with a porous structure and mechanical properties that are very close to those of bone were fabricated. These ZrTi alloy foams are biocompatible, and display a porous structure permitting the ingrowth of new bone tissues.

The influence of twinning on the hot working flow stress and microstructural evolution of magnesium alloy AZ31

The microstructural evolution during compression (at 350°C and a strain rate of 0.01s-1) was examined for magnesium alloy AZ31 received in the "as-cast" condition. It was revealed that at low strains, many twins are produced and dynamically recrystallized (DRX) grains form as a necklace along pre-existing grain boundaries. At higher strains, DRX stagnates, most likely due to the accommodation of deformation in the DRX fraction of the material. It was also observed that twin boundaries act as sites for the nucleation of DRX grains. The analysis was repeated for samples pre-compressed to a strain of 0.15 at room temperature prior to the hot deformation step. The idea of these additional tests was to increase the degree of twinning and therefore the density of sites for the nucleation of DRX. It was found that statically recrystallized (SRX) grains developed at the twins during heating to the test temperature. When these samples were deformed, the peak flow stress was reduced by approximately 20% and the development of DRX was enhanced. This can be attributed to the accelerated nucleation of DRX in the refined SRX structure.

Mapping the hot deformation microstructure of Ni-30Fe alloy

The evolution of structure during the hot working of an austenitic Ni-30%Fe alloy is studied using EBSD analysis of samples tested in torsion. A microstructural map in temperature-strain space that plots grain size, cell size, fracture and dynamic recrystallization is presented.

Fabrication of novel TiZr alloy foams for biomedical applications

Bone injuries and failures often require the inception of implant biomaterial. Research in this area has received increasing attention recently. In particular, porous metals are attractive due to its unique physical, mechanical, and new bone tissue ingrowth properties. In the present study, TiZr alloy powders were prepared using mechanical alloying. Novel TiZr alloy foams with relative densities of approximately 0.3 were fabricated by a powder metallurgical process. The TiZr alloy foams displayed an interconnected porous structure resembling bone and the pore size ranged from 200 to 500 μm. The compressive plateau stress and the Young’s modulus of the TiZr foam were 78.4 MPa and 15.3 GPa, respectively. Both the porous structure and the mechanical properties of the TiZr foam were very close to those of natural bone.

A semianalytical Sachs model for the flow stress of a magnesium alloy

A semianalytical Sachs-type equation for the flow stress of magnesium-base alloys is developed using the Schmid law, power law hardening, and a sigmoidal increase in the twinning volume fraction with strain. Average Schmid factors were estimated from electron backscattered diffraction (EBSD) data. With these, the equation provides a reasonable description of the flow curves obtained in compression and tension for samples of Mg-3Al-1Zn cut in different orientations from rolled plate. The model illustrates the general importance of basal slip and twinning in magnesium alloys. The significance of prismatic slip in room temperature tension testing is also highlighted. This is supported with EBSD slip line trace analysis and rationalized in terms of a possible sensitivity of the critical resolved shear stress for prismatic (cross) slip to the stress on the basal plane.

Theoretical investigation of wear-resistance mechanism of superelastic shape memory alloy NiTi

Recent experimental research indicates that superelastic shape memory alloy nickel–titanium (NiTi) is superior to stainless steel against wear and could be applied in tribological engineering. It is believed that the super wear resistance of shape memory alloys is mainly due to the recovery of the superelastic deformation. Our recent wear study indicates that wear rate is very sensitive to the maximum contact pressure. In the present investigation, which involves applying Hertz contact theory and the finite element method, the wear behaviour of shape memory alloys is examined against that of stainless steels through analyzing the maximum contact pressure and the plastic deformation. Our investigation indicates that the contribution of superelasticity to the high wear resistance of NiTi is directly linked to the low transformation stress and the large recoverable transformation strain. Furthermore, the low Young's modulus of this alloy also plays an important role to reduce the maximum contact pressure and therefore reduce the wear rate. Additionally, the high plastic yield strength of transformed martensite NiTi enhances its wear resistance further.