The effect of hydrogenation on the ECAP compaction of Ti–6Al–4V powder and the mechanical properties of compacts

The effect of hydrogen content on the compaction of Ti–6Al–4V powder at low temperatures, namely 500 °C, using equal channel angular pressing (ECAP) with back pressure has been investigated. The properties of the compacts before and after a heat treatment and de-hydrogenation cycle have been determined. Compaction of powder by ECAP (500 °C and 260 MPa) has shown maximum levels of relative density of 99.3% and 99.4% when charged with 0.05–0.1 wt.% and 0.61–0.85 wt.% of hydrogen, respectively. After the de-hydrogenation heat treatment the diffusion bonding between individual powder particles was completed and the microstructure was altered, depending on the level of hydrogen content. Two local maxima of 99.2% and 98.1% were observed in the measured density of consolidated compacts for hydrogen contents between 0.05 wt.% and 0.1 wt.% and between 0.61 wt.% and 0.85 wt.%, respectively. However, the mechanical properties of the compacts within these two ranges of hydrogen content were significantly different due to a difference in the observed microstructure. An exceptionally high ductility of 29%, in combination with a relatively high strength of ~560 MPa, was measured in a shear punch test on specimens which had a prior hydrogen level of 0.05 wt.% before the heat treatment. It was shown that material consolidated from powder hydrogenated to low levels of hydrogen before compaction has the potential to offer substantial improvements in mechanical properties after a suitable heat treatment.

Thermal behavior of copper processed by ECAP with and without back pressure

Samples of electrolytic tough pitch (ETP) pure copper were subjected to 12 passes of Equal-Channel Angular Pressing (ECAP) at room temperature with and without back pressure. Subsequent annealing was performed to evaluate the influence of back pressure during ECAP on the thermal behavior of ultrafine-grained copper. The microstructural and hardness changes caused by annealing were characterized by orientation imaging microscopy (OIM) and microhardness measurements. The application of back pressure resulted in an earlier drop in hardness upon annealing, which is believed to be associated with a lower critical temperature for the initiation of recrystallization and a rapid coarsening of microstructure. Regardless of whether back pressure was applied or not, structure coarsening during short-time annealing of ECAP-processed copper was governed by discontinuous static recrystallization. This is seen as a result of microstructure heterogeneity. Analysis of recrystallization kinetics was carried out based on observations of the microstructure after annealing in terms of the Avrami equation. The magnitude of the apparent activation energies for recrystallization in the absence of back pressure and in the case of back pressure of 100 MPa was estimated to be ~99 kJ/mol and ~91 kJ/mol, respectively. The reasons for reduced activation energy in the case of processing with back pressure are discussed.

Influence of backpressure during ECAP on the monotonic and cyclic deformation behavior of AA5754 and Cu99.5

Ultrafine-grained (UFG) metals produced by equal channel angular pressing (ECAP) exhibit outstanding mechanical properties. They show high strength under monotonic loading as well as strongly enhanced fatigue lives in the Wöhler S-N-plot compared to their coarse grained (CG) counterparts. It could be shown that the fatigue lives can be significantly enhanced further by applying backpressure during ECAP. Besides the positive effect of backpressure on the processability of hard to deform materials via ECAP, the hydrostatic stress induced by backpressure also influences the mechanical properties under monotonic and cyclic loading. Therefore the influence of backpressure on ECAPed Cu99.5 and on the ECAPed aluminum alloy AA5754 was investigated. It is shown that backpressure has no effect on the hardness and grain size in Cu99.5 but changes the grain boundary misorientation to higher fractions of low angle grain boundaries. Also the temperature dependency of the yield strength as well as the hardening behavior under monotonic compression is affected. The cyclic deformation behavior of Cu99.5 is not strongly influenced by backpressure, but the mean stress level changes drastically. The fatigue life increases with the application of backpressure at low plastic amplitudes due to a change in the crack initiation and propagation. Aim of this work is the investigation of the influence of backpressure during equal channel angular pressing (ECAP) on the mechanical properties under monotonic and cyclic loading. Therefore we performed hardness measurements, compression, and fatigue tests on ECAPed Cu99.5 and AA5754. The results are discussed in terms of microstructure and relevant deformation and damage mechanisms.

The influence of temporary hydrogenation on ECAP formability and low cycle fatigue life of CP titanium

It is generally believed that thermo-hydrogen processing has a beneficial effect on tensile ductility and fatigue properties of titanium. This study was concerned with investigating whether this also applies to titanium of commercial purity (CP) with an ultrafine-grained structure obtained by equal-channel angular pressing (ECAP). It was shown that despite the possibility to manipulate the microstructure of titanium the thermo-hydrogen processing offers, temporary hydrogenation was not able to improve ductility and low cycle fatigue life of CP titanium over the levels achievable by straight ECAP.

Equal channel angular pressing of metal matrix composites: effect on particle distribution and fracture toughness

An Al6061-20%Al₂O₃ powder metallurgy (PM) metal matrix composite (MMC) with a strongly clustered particle distribution is subjected to equal channel angular pressing (ECAP) at a temperature of 370 °C. The evolution of the homogeneity of the particle distribution in the material during ECAP is investigated by the quadrat method. The model proposed by Tan and Zhang [Mater Sci Eng 1998;244:80] for estimating the critical particle size which is required for a homogeneous particle distribution in PM MMCs is extended to the case of a combination of extrusion and ECAP. The applicability of the model to predict a homogeneity of the particle distribution after extrusion and ECAP is discussed. It is shown that ECAP leads to an increase of the  uniformity of the particle distribution and the fracture toughness.

Multi equal channel angular pressing with rotational dies

The recent successful development of the equal channel angular pressing (ECAP) process in metals provides a feasible solution to produce ultra-fine or nano-grained bulk: materials with tailored material properties. However, ECAP is difficult to scale up commercially due to excessive load requirements. In this paper, a new Multi-ECAP process with die rotation is considered to obtain ultra-fine grain structured materials under a moderate deformation force. It is shown that an addition of torsion results in a reduction in the pressing force and an increase in severity of plastic deformation. An analysis using the upper bound method is found to be useful in predicting the pressing load and flow pattern of ECAP with and without rotational dies. Solutions are obtained for different inclined channel angles under different angular velocities of dies. Relative pressures are presented and some computed solutions are compared with those found by FEM simulation. The theoretical predictions of the pressing load are in good agreement with the simulation results. The amount of plastic deformation is determined by the inclined angle between the two intersecting channels, and the velocity ratio between the angular velocity of dies and the normal component of the punch velocity.

Enhanced tensile ductility of an ultra-fine-grained aluminium alloy

Aluminum alloy 6082 was subjected to equal-channel angular pressing (ECAP), which resulted in an ultra-fine-grained (UFG) microstructure with an average grain size of 0.2–0.4 μm. There was a pronounced effect of the grain refinement on the strain-rate sensitivity and tensile ductility. The Hart criterion of tensile necking fails to explain the observed ductility of the UFG material at low strain rates. A correlation between the observed stronger-than-expected ductility and a tendency to microshear band formation at low strain rates was established.

T-Shaped equi-channel angular pressing of Pb-Sn eutectic and its tensile properties

Equi-channel angular pressing (ECAP) of a Pb–Sn eutectic alloy up to six passes in a T-shaped die, rather than a conventional L-shaped die, was studied for grain refinement. The effect of ECAP on the hardness and tensile properties was studied. Microstructure predominately changed in the early part of the ECAP process and became equiaxed and uniformly distributed in both the longitudinal and the transverse sections after four passes. There occurred substantial softening over the first two passes—hardness of 10 Hv, yield strength of 14.2 MPa and tensile strength of 16.3 MPa in the as-cast condition decreased upon two passes to 6 Hv, 9.7 MPa and 13.0 MPa, respectively. The ductility (% elongation) increased drastically from <50% in the as-cast condition to 150% upon two passes, and further increased to 230% after four passes. Various tensile properties and concurrent microstructural evolution were used to develop a mutual relationship among them.

Deep drawing behaviour of ultrafine grained copper : modelling and experiment

Ultrafine grained materials produced by severe plastic deformation methods possess attractive mechanical properties such as high strength compared with traditional coarse grained counterparts and reasonable ductility. Between existing severe plastic deformation methods the Equal Channel Angular Pressing is the most promising for future industrial applications and can produce a variety of ultrafine grained microstructures in materials depending on route, temperature and number of passes during processing. Driven by a rising trend of miniaturisation of parts these materials are promising candidates for microforming processes. Considering that bi-axial deformation of sheet (foil) is the major operation in microforming, the investigation of the influence of the number of ECAP passes on the bi-axial ductility in micro deep drawing test has been examined by experiments and FE simulation in this study. The experiments have showed that high force was required for drawing of the samples processed by ECAP compare to coarse grained materials. The limit drawing ratio of ultrafine grained samples was in the range of 1.9–2.0 with ECAP pass number changing from 1 to 16, while a higher value of 2.2 was obtained for coarse grained copper. However, the notable decrease in tensile ductility with increase in strength was not as pronounced for bi-axial ductility. The FE simulation using standard isotropic hardening model and von Mises yielding criterion confirmed these findings.

Use of residual hydrogen to produce CP-Ti powder compacts for low temperature rolling

The present work investigates the optimal level of residual hydrogen in partially de-hydrogenated powder to produce CP-Ti plate compacts using ECAP with back pressure which are subsequently rolled at low temperature. A comparative study of the compaction of two TiH₂ powders and a CP-Ti powder, with particle sizes 150 um, 50um and 45 um respectively, has been carried out. The hydride powders have also been compacted in a partially de-hydrogenated state. The optimal level of residual hydrogen with respect to the density of the resulting compact and the associated mechanical properties has been defined. ECAP at 300°C produced compacts from these partially de-hydrogenated powders of 99.5% theoretical density, while CP-Ti was compacted to almost full theoretical density under the same ECAP conditions. Therefore, the compaction of powder by ECAP does not benefit from temporary hydrogen alloying.

These compacts then were rolled at temperatures ranging from room temperature to 500°C with an 80% reduction in a single pass. Heat treatment after the rolling can modify the microstructure to improve the resulting mechanical properties and in this regard the temporary alloying with hydrogen has been observed to offer some significant benefits. It is shown the ECAP followed by low temperature rolling is a promising route to the batch production of fully dense CP-Ti wrought product from powder feedstock that avoids the need to subject the material to temperatures greater than 500°C. This low temperature route is expected to be efficient from an energy point of view and it also avoids the danger of interstitial contamination that accompanies most high temperature powder processing.

Effect of grain size on corrosion of high purity aluminium

A complete understanding of how grain refinement, grain size, and processing affect the corrosion resistance of different alloys has not yet been fully developed. Determining a definitive 'grain size-corrosion resistance' relationship, if one exists, is inherently complex as the processing needed to achieve grain refinement also imparts other changes to the microstructure (such as texture, internal stress, and impurity segregation). This work evaluates how variation in grain size and processing impact the corrosion resistance of high purity aluminium. Aluminium samples with a range of grain sizes, from ∼100 μm to ∼2000 μm, were produced using different processing routes, including cold rolling, cryo rolling, equal channel angular pressing, and surface mechanical attrition treatment. Evaluation of all the samples studied revealed a tendency for corrosion rate to decrease as grain size decreases. This suggests that a Hall-Petch type relationship may exist for corrosion rate and grain size. This phenomenon, discussed in the context of grain refinement and processing, reveals several interesting and fundamental relationships.

Mechanical response of aluminium alloy 6061-T6 after CECAP processing

The potential of new designed continues ECAP machine in intermediate industrial scale has been discussed in the present work. The improved mechanical and microstructural properties of processed materials has been investigated on commercial aluminium alloy 6061 in T6 condition. The 6061-T6 sheet was subjected to one, two, three and four passes of ECAP. The results showing the significant improvement of mechanical properties after ECAP processing.

Severe plastic deformation of TWIP steel

The severe plastic deformation of a Twinning Induced Plasticity (TWIP), 0.61C-22.3Mn-0.19Si-0.14Ni-0.27Cr (wt. %) steel by Equal Channel Angular Pressing (ECAP) at elevated temperatures was used to study the deformation mechanism as a function of accumulated strain and processing parameters. The relationship between the microstructures after different deformation schedules of ECAP at the temperatures of 200, 300 and 400oC, strain hardening behavior and mechanical properties was studied. The best balance between strength and ductility (1702 MPa and 24%) was found after 2 passes at 400oC and 300oC of ECAP. It was due to the formation of deformation microbands and twins in the microstructure. The twinning was observed after all deformation schedules except after 1 pass at 400oC. The important finding was the formation of twins in the ultrafine grains. Moreover, the stacking faults were observed in the subgrains with the size of 50nm. It is also worth mentioning the formation of nano- twins within the micro-twins at the same time. It was found that the deformation schedule affects the dislocation substructure with formation of deformation bands, cells, subgrains, two variants of twins that, in turn, influence the strain-hardening behavior and mechanical properties. Keywords: Twinning Induced Plasticity steels; Equal Channel Angular Pressing; mechanical properties; transmission electron microscopy; micro/nano twins; dislocation substructure.

Comparison of laboratory-scale and industrial-scale equal channel angular pressing of commercial purity titanium

This study contrasts the extent to which laboratory and industrial scale variants of equal channel angular pressing (ECAP) impart desirable microstructures and mechanical properties in Grades 2 and 4 titanium. Industrial-scale ECAP-Conform (ECAP-C) with post-ECAP thermo-mechanical processing (TMP) enhanced performance levels beyond those achieved with the same material processed in the laboratory by ECAP only. ECAP-C processed titanium demonstrated exceptional tensile properties and fatigue strength, superior even to conventional Ti-6Al-4V.