Effect of synthesis parameters on the electrical conductivity of polypyrrole-coated poly(ethylene terephthalate) fabrics

The effects of pyrrole, anthraquinone-2-sulphonic acid (AQSA) and iron(III) chloride (FeCl3) concentrations, reaction time and temperature on the electrical conductivity of polypyrrole (PPy) - coated poly(ethylene terephthalate) (PET) fabrics were investigated. With an increase in both the AQSA and FeCl3 concentrations, resistivity decreased to a point beyond which higher concentrations led to increased surface resistivity. Erosion of the polymer coating, in dynamic synthesis from continual abrasion, manifested as an exponential increase in the resistance of the coated textile substrate. This was not encountered in static synthesis conditions. Temperature affected the degree of surface and bulk polymerisation. The effect of polymerisation temperature on conductivity was negligible. Conductive polymer coating on textiles through chemical polymerisation enabled a smooth coherent film to encase individual fibres, which did not affect the tactile properties of the host substrate. The optimum FeCl3/pyrrole and AQSA FeCl3/pyrrole molar ratios were found to be 2.22 and 0.40 respectively.

Eri silk fibre attributes and sliver preparation

Eri silk produced by Philosamia cynthia ricini silkworm is a fibre not well-known to the silk industry, in spite of the fact that Eri silk is finer, softer, and has better mechanical and thermal properties than most animal fibres. Eri silk has a high commercial potential, as the host plants of Eri silk worms are widespread in diverse geographical locations, and the worms also have a higher degree of disease resistance than most other silk worms. Mills are often not aware of the properties of Eri for designing appropriate end products. Thus, Eri silk yarn is traditionally produced by hand spinning, and Eri silk usually ends up as material for handwoven shawls. The potential for bulk fibre processing and the development of soft luxurious novel Eri silk products is yet to be discovered. To better understand the material and its processing behaviour, Eri silk was characterised and cocoons were processed into tops through degumming, opening, and cutting filaments into different lengths, followed by a worsted spun silk processing route. Fibre properties such as fineness, crimp, strength and length at different processing stages up to combed tops were measured. The results indicate that staple Eri silk can be processed via the worsted topmaking route, using a cut length of 200 mm or 150 mm for filament sheets prepared from degummed cocoons.

Covalent immobilization of naringinase for the transformation of a flavonoid

Naringinase (EC 3.2.1.40) from Penicillium sp was immobilized by covalent binding to woodchips to improve its catalytic activity. The immobilization of naringinase on glutaraldehyde-coated woodchips (600 mg woodchips, 10 U naringinase, 45 °C, pH 4.0 and 12h) through 1% glutaraldehyde cross-linking was optimized. The pH-activity curve of the immobilized enzyme shifted toward a lower pH compared with that of the soluble enzyme. The immobilization caused a marked increase in thermal stability of the enzyme. The immobilized naringinase was stable during storage at 4 °C. No loss of activity was observed when the immobilized enzyme was used for seven consecutive cycles of operations. The efficiency of immobilization was 120%, while soluble naringinase afforded 82% efficacy for the hydrolysis of standard naringin under optimal conditions. Its applicability for debittering kinnow mandarin juice afforded 76% debittering efficiency. 

Silver sulfide as a staining agent for scanning electron microscopy of nylon 6/MXD6 blends

BACKGROUND: In transmission and scanning electron microscopy imaging, the ability to obtain sufficient contrast between the components of a blend when they are both of a similar chemical structure still remains problematic. This paper investigates the domain morphology of a polymer blend containing two polyamides, nylon 6 and the semi-aromatic polyamide poly(m-xylene adipamide) (MXD6), using scanning electron microscopy in backscattered electron imaging mode. The efficiency of three staining agents, ruthenium tetroxide, phosphotungstic acid and silver sulfide, in obtaining optimum phase contrast between the two polymers is discussed.
RESULTS: The use of silver sulfide as a staining agent was found to be a fast and reliable approach which required basic sample preparation and provided excellent compositional contrast between the phases present in the nylon 6/MXD6 blends compared to the other staining agents.
CONCLUSIONS: The technique described in this paper is believed to be a novel and versatile method that has the potential to further improve the ability to study complex polymer blends where one polymer contains an aromatic ring.