Cerium acetylacetonates—new aspects, including the lamellar clathrate [Ce(acac)4]·10H2O

Reactions of CeCl₃·7H₂O and Ce(NO₃)₃·6H₂O with Naacac or NH₄acac in aqueous solution at 21 and 45 °C yielded the trihydrate [Ce(acac)₃(H₂O)₂]·H₂O and the dihydrate [Ce(acac)₃(H₂O)₂], respectively, whereas similar treatment of (NH₄)₂[Ce(NO₃)₆] gave the trihydrate at both temperatures. Desiccation of the hydrates over silica gel left the dihydrate unchanged, whereas the trihydrate underwent decomposition rather than dehydration. Aerial oxidation of [Ce(acac)₃(H₂O)₂] in CH₂Cl₂ and toluene yielded α-[Ce(acac)₄] and β-[Ce(acac)₄], respectively, the structure of the former being re-determined with improved precision. Careful treatment of aqueous (NH₄)₄[Ce(SO₄)₄] and Hacac (initially pH 1–2) with aqueous ammonia to pH 5 precipitated hydrated [Ce(acac)₄], from which [Ce(acac)₄]·10H₂O was isolated as unstable, light-sensitive single crystals, and the structure was determined. The complex is a laminar clathrate containing layers of Ce(acac)₄ molecules sandwiched between extensive hydrogen-bonded layers of water molecules which do not interact with the metal. Electrochemical experiments confirmed the unstable nature of hydrated Ce^III(acac)₃, while the reduction of [Ce(acac)₄] yielded well-defined cyclic voltammograms in acetonitrile and acetone, corresponding to a quasi-reversible process. For the [Ce^IV(acac)₄]/[Ce^III(acac)₄]⁻redox couple, a calculated reversible potential of 0.22±0.02 V versus SHE was obtained in acetone or acetonitrile (0.1 M Bu₄NPF₆) at both gold and glassy carbon electrodes. This potential is consistent with the ease of both oxidation and reduction of cerium acetylacetonate complexes as found in the synthetic studies.

The nature of the surface film on steel treated with cerium and lanthanum cinnamate based corrosion inhibitors

The corrosion inhibition mechanisms of new cerium and lanthanum cinnamate based compounds have been investigated through the surface characterisation of the steel exposed to NaCl solution of neutral pH. Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) spectroscopy was used to identify the nature of the deposits on the metal surface and demonstrated that after accelerated tests the corrosion product commonly observed on steel (i.e. lepidocrocite, γ-FeOOH) is absent. The cinnamate species were clearly present on the steel surface upon exposure to NaCl solution for short periods and appeared to coordinate through the iron. At longer times the Rare Earth Metal (REM) oxyhydroxide species are proposed to form as identified through the bands in the 1400–1500 cm⁻¹ region. These latter bands have been previously assigned to carbonate species adsorbed onto REM oxyhydroxide surfaces. The protection mechanism appears to involve the adsorption of the REM–cinnamate complex followed by the hydrolysis of the REM to form a barrier oxide on the steel surface.

ATR characterisation of synergistic corrosion inhibition of mild steel surfaces by cerium salicylate

The nature of deposits on mild steel surfaces formed by exposure to corrosive and inhibiting solutions has been examined by attenuated total reflectance spectroscopy. For cerium-based inhibitors, e.g. CeCl₃ the formation of cerium-containing coatings was detected whilst the cerium carboxylate Ce(sal)₃ (sal=salicylate), which combines the Ce³⁺ with the known organic inhibitor sal⁻, was shown to involve substantial deposition of both cerium and a salicylate species. These results, combined with corrosion inhibition data for the respective inhibitor compounds clearly indicate a synergistic corrosion mechanism for Ce(sal)₃ which underpins the improved performance of this corrosion inhibitor in comparison to the individual components (i.e. Na(sal) or CeCl₃).

Corrosion inhibition of 7000 series aluminium alloys with cerium diphenyl phosphate

Cerium diphenyl phosphate (Ce(dpp)3) has previously been shown to be a strong corrosion inhibitor for aluminium-copper magnesium alloy AA2024-T3 and AA7075 in chloride solutions. Surface characterisation including SEM and ToF-SIMS coupled with electrochemical impedance spectroscopy (EIS) measurements are used to propose a mechanism of corrosion inhibition which appears to involve the formation of a complex oxide film of aluminium and cerium also incorporating the organophosphate component. The formation of a thin complex film consisting of hydrolysis products of the Ce(dpp)3 compound and aluminium oxide is proposed to lead to the observed inhibition. SEM analysis shows that some intermetallics favour the creation of thicker deposits predominantly containing cerium oxide compounds.

The corrosion inhibition of aluminium alloy 7075-T651 with cerium and Mischmetal di phenyl phosphate

Previous studies have shown that cerium diphenyl phosphate (Cedpp) 3 is a very effective inhibitor of corrosion of aluminium alloys in chloride solutions. This paper describes the results of further studies using electrochemical and constant immersion corrosion tests to compare the effectiveness of Ce(dpp) 3 and Mischmetal diphenyl phosphate Mm(dpp) 3 as inhibitors of corrosion pitting on AA7075-T651 aluminium alloy. The results shows that both Ce(dpp) 3 and Mm(dpp) 3 are excellent inhibitors of pitting corrosion of this alloy in very aggressive environments of continuously aerated 0.1M and 1.0M sodium chloride (NaCl) solutions. Polarisation tests indicate that these compounds act as a cathodic inhibitors by reducing the rate of the oxygen reduction reaction, which results in a decreased corrosion current density and a separation of the corrosion potential from the pitting potential. This inhibition is thought to be due to the formation of a surface film consisting of rare earth metal oxide, aluminium oxide and a cerium-aluminium organo-phosphate complex. Surface analysis data from scanning electron microscopy and X-ray Energy Dispersive Spectroscopy show the complex nature of this protective film. This work further develops our understanding about the mechanisms through which these complex films form, and how inhibition occurs in the presence of these compounds.

Effects of nano cerium (IV) oxide and zinc oxide particles on biogas production

With an increase in use of nanoparticles (NPs) in day to day products, these particles eventually enter the wastewater treatment plant and get removed from the effluent while getting accumulated in the sludge at ever increasing concentrations. These NPs have a potential for causing inhibition in sludge digestion processes. Therefore, this research focused on the effects of cerium (IV) oxide (CeO2) and zinc oxide (ZnO) NPs on biogas production from sludge. The inhibition effects were investigated by studying toxicity of the said NPs on Escherichia coli. The results showed that CeO2 and ZnO NPs showed some degree of inhibition in biogas production with 65.3% biogas reduction at ZnO NPs at 1000 mg/L concentration. Conversely, CeO2 at low concentration of 10 mg/L lead to an increase biogas generation by 11%. The tolerable exposure concentrations for ZnO were determined to be 100 and 500 mg/L, where the system could overcome the inhibition effect after 14 days of incubation. The bacterial toxicity test showed that both nanoparticles were toxic for bacteria leading to biogas reduction.

Tris(2,2'-bipyridyl)ruthenium(II) chemiluminescence enhanced by silver nanoparticles

Mixtures of silver(I) and citrate that are used to produce silver nanoparticles evoke intense chemiluminescence with tris(2,2'-bipyridyl)ruthenium(II) and cerium(IV), which can be exploited for the determination of citrate ions and other analytes over a wide concentration range.

Effect of oxidant type on the chemiluminescence intensity from the reaction of tris(2,2’-biyridyl)ruthenium(III) with various organic acids

An investigation into the chemiluminescence of fourteen organic acids and tris(2,2′-bipyridyl)ruthenium(II) was undertaken. Particular emphasis was placed upon the method of production of the reagent, tris(2,2′-bipyridyl)ruthenium(III), with cerium(IV) sulfate, potassium permanganate, lead dioxide and electrochemical generation. Analytically useful chemiluminescence was observed when Ce(IV) or potassium permanganate were employed as oxidants. The kinetics of analyte oxidation was related to the intensity of the chemiluminescence emission, which increased by three orders of magnitude for tartaric acid after 40 h of oxidation.