Microstructural evolution of ultrafine grained structure in plain carbon steels through single pass rolling

In the present study, the effect of nominal equivalent strain (between 0 and 1.2), deformation temperature (790– 750°C) and carbon content (0.06 – 0.35%C) was investigated on ferrite grain refinement through dynamic strain induced transformation (DSIT) in plain carbon steels in single pass rolling. The microstructural evolution of the transformation of austenite to ferrite has been evaluated through the thickness of the strip. The results showed a number of important microstructural features as a function of strain, which could be classified into three regions; no DSIT region, DSIT region, and ultrafine ferrite (UFF) grain region. Hence, two critical strains; dynamic strain induced transformation (εC, DSIT) and ultrafine ferrite formation (εC, UFF) were determined. These strains were increased significantly with an increase in carbon content. The critical strain for UFF formation reduced with decrease in deformation temperature. The UFF microstructure consisted of ultrafine, equiaxed ferrite grains (<2 μm) with very fine cementite particles. In the centre of the rolled strip, there was a conventional ferrite– pearlite microstructure, although ferrite grain refinement and the volume fraction of ferrite increased with increase in the nominal equivalent strain.

Formation of ultrafine grained structure in plain carbon steels through thermomechanical processing

In the present study, wedge-shaped samples were used to determine the effect of nominal equivalent strain (between 0 and 1.2) and carbon content (0.06--0.35%C) on ferrite grain refinement through dynamic strain-induced transformation (DSIT) in plain carbon steels using single-pass rolling. The microstructural evolution of the transformation of austenite to ferrite has been evaluated through the thickness of the strip. The results showed a number of important microstructural features as a function of strain which could be classified into three regions; no DSIT region, DSIT region and the ultrafine ferrite (UFF) grain region. Also, the extent of these regions was strongly influenced by the carbon content. The UFF microstructure consisted of ultrafine, equiaxed ferrite grains (<2 μ$m) with very fine cementite particles. In the centre of the rolled strip, there was a conventional ferrite-pearlite microstructure, although ferrite grain refinement and the volume fraction of ferrite increased with an increase in the nominal equivalent strain.

The formation of ultrafine ferrite through static transformation in low carbon steels

A novel approach was used to produce an ultrafine grain structure in low carbon steels with a wide range of hardenability. This included warm deformation of supercooled austenite followed by reheating in the austenite region and cooling (RHA). The ultrafine ferrite structure was independent of steel composition. However, the mechanism of ferrite refinement hanged with the steel quench hardenability. In a relatively low hardenable steel, the ultrafine structure was produced through dynamic strain-induced transformation, whereas the ferrite refinement was formed by static transformation in steels with high quench hardenability. The use of a model Ni–30Fe austenitic alloy revealed that the deformation temperature has a strong effect on the nature of the intragranular defects. There was a transition temperature below which the cell dislocation structure changed to laminar microbands. It appears that the extreme refinement of ferrite is due to the formation of extensive high angle intragranular defects at these low deformation temperatures that then act as sites for static transformation.

Effect of silicon and prior deformation of austenite on isothermal transformation in low carbon steels

Isothermal transformation (TTT) behavior of the low carbon steels with two Si contents (0.50 wt pct and 1.35 wt pct) was investigated with and without the prior deformation. The results show that Si and the prior deformation of the austenite have significant effiects on the transformation of the ferrite and bainite. The addition of Si refines the ferrite grains, accelerates the polygonal ferrite transformation and the formation of M/A constituents, leading to the improvement of the strength. The ferrite grains formed under the prior deformation of the austenite become more homogeneous and refined. However, the influence of deformation on the tensile strength of both steels is dependent on the isothermal temperatures. Thermodynamic calculation indicates that Si and prior deformation reduce the incubation time of both ferrite and bainite transformation, but the effiect is weakened by the decrease of the isothermal temperatures.

Transformation behavior of low carbon steels containing two different Si contents

Continuous cooling transformation behaviors of low carbon steels with two Si contents (0.50% and 1. 35%) were investigated under undeformed and deformed conditions. Effects of Si contents, deformation, and cooling rates on y transformation start temperature (A,_r3), phase microstructures, and hardness were studied. The results show that, in the case of the deformation with the true strain of 0. 4, the length of bainitic ferrite laths is significantly decreased in low Si steel, whereas, the M/A constituent becomes more uniform in high Si steel. An increase in cooling rates lowers the A,_r3 greatly. The steel with higher level of Si exhibits higher A,_r3, and higher hardness both under undeformed and deformed conditions compared with the steel with a lower Si content. Especially, the influence of Si on A_r3 is dependent on deformation. Such effects are more significant under the undeformed condition. The hardness of both steels increases with the increase of cooling rates, whereas, the deformation involved in both steels reduces the hardness.

The formation of ultrafine ferrite through static transformation in low carbon steels

A novel approach was used to produce an ultrafine grain structure in low carbon steels with a wide range of hardenability. This included warm deformation of supercooled austenite followed by reheating in the austenite region and cooling (RHA). The ultrafine ferrite structure was independent of steel composition. However, the mechanism of ferrite refinement changed with the steel quench hardenability. In a relatively low hardenable steel, the ultrafine structure was produced through dynamic strain induced transformation, whereas the ferrite refinement was formed by static transformation in steels with high quench hardenability. The use of a model Ni-30Fe austenitic alloy revealed that the deformation temperature has a strong effect on the nature of the intragranular defects. There was a transition temperature below which the cell dislocation structure changed to laminar microbands. It appears that the extreme refinement of ferrite is due to the formation of extensive high angle intragranular defects at these low deformation temperature that then act as sites for static transformation. © 2008 World Scientific Publishing Company.

Symmetric and asymmetric rolling of low carbon steels

 In this study, it is shown that a close to ideal shear texture can be formed throughout the thickness of a rolled sheet. Such rotation of rolling texture not only leads to the enhancement in grain refinement but also the secondary processing as compared to the symmetric rolling.

Hardenability reduction in VN microalloyed eutectoid steels

By dilatometry, it is shown that vanadium microalloying additions to eutectoid carbon steels, which also contain an increased level of nitrogen, cause a marked decrease in hardenability when transforming from fine grained austenite.

Warm deformation and annealing behaviour of iron-silicon-(carbon) steel sheets

Single pass warm rolling and compression experiments were carried out from ambient to 800°C for ultra-low carbon (ULC) steel with ∼100 ppm carbon and interstitial free (IF) steels, both with two levels of silicon. Subsequently, annealing was done in order to recrystallize the deformed specimens. The main purpose of this study was to understand the effects of rolling temperature and silicon on stress responses and textures. This study comprises two main themes: flow stress and strain rate sensitivity during compression and shear banding and textures in warm rolled specimens. The effects of deformation temperature on in-grain shear bands were different between ULC-Si and IF-Si steels. As in previous work with more conventional steels, in-grain shear bands in the IF grade had low sensitivity to rolling temperature, while those in the ULC grade depended significantly on the deformation temperature. However, the temperature profile of shear banding in the ULC grade was approximately 150°C higher than in previous work. Deformation and recrystallisation textures for both IF and ULC grades depended on their rolling temperatures. The variation of both grain size and texture after annealing can be explained by the rise and fall of in-grain shear banding activity which is related to the strain rate sensitivity.

Formation of ultrafine grained microstructures in steel through strain induced transformation during single pass hot rolling

In the present study, wedge-shape samples were used to study the effect of strain induced transformation on the formation of ultrafine grained structures in steel by single pass rolling. The results showed two different transition strains for bainite formation and ultrafine ferrite (UFF) formation in the surface layer of strip at reductions of 40% and 70%, respectively, in a plain carbon steel. The bainitic microstructure formed by strain induced bainitic transformation during single pass rolling was also very fine. The evolution of UFF formation in the surface layer showed that ferrite coarsening is significantly reduced through strain induced transformation combined with rapid cooling in comparison with the centre of the strip. In the surface, the ferrite coarsening mostly occurred for intragranular nucleated grains (IG) rather than grain boundary (GB) ferrite grains. The results suggest that normal grain growth occurred during overall transformation in the GB ferrite grains. In the centre of the strip, there was significantly more coarsening of ferrite grains nucleated on the prior austenite grain boundaries.

Formation of ultra-fine ferrite in hot rolled strip: potential mechanisms for grain refinement

A novel single-pass hot strip rolling process has been developed in which ultra-fine (<2 μm) ferrite grains form at the surface of hot rolled strip in two low carbon steels with average austenite grain sizes above 200 μm. Two experiments were performed on strip that had been re-heated to 1250°C for 300 s and air-cooled to the rolling temperatures. The first involved hot rolling a sample of 0.09 wt.%C–1.68Mn–0.22Si–0.27Mo steel (steel A) at 800°C, which was just above the Ar3 of this sample, while the second involved hot rolling a sample of 0.11C–1.68Mn–0.22Si steel (steel B) at 675°C, which is just below the Ar3 temperature of the sample. After air cooling, the surface regions of strip of both steel A and B consisted of ultra-fine ferrite grains which had formed within the large austenite grains, while the central regions consisted of a bainitic microstructure. In the case of steel B, a network of allotriomorphic ferrite delineated the prior-austenite grain boundaries throughout the strip cross-section. Based on results from optical microscopy and scanning/transmission electron microscopy, as well as bulk X-ray texture analysis and microtextural analysis using Electron Back-Scattered Diffraction (EBSD), it is shown that the ultra-fine ferrite most likely forms by a process of rapid intragranular nucleation during, or immediately after, deformation. This process of inducing intragranular nucleation of ferrite by deformation is referred to as strain-induced transformation.

Recrystallization kinetic behavior of copper-bearing strip cast steel

In the present study, copper-bearing low carbon steels were produced by direct strip casting (DSC) method on a pilot scale. The effects of copper on mechanical, microstructural, and recrystallization behavior were investigated. As-cast microstructure mainly consists of polygonal ferrite and Widmanstatten ferrite. The increase in Cu increases the amount of Widmanstatten ferrite and induces the formation of bainite in the as-cast condition. It was found that copper increases strength and hardness by solid solution strengthening, grain refinement, and precipitation hardening and the increment is significant above 1% Cu in as-cast condition. Six different compositions were selected for recrystallization study. All the samples were cold rolled to 70% reduction and annealed at three different temperatures, 600, 650, and 700°C for various times. Recrystallization responses were strongly dependent on initial microstructure and Cu content and the effect is dramatic between 1 and 2% Cu. Recrystallization time and temperature were found to be increased with increase in copper content.

Yielding behaviour of martensite in steel

Although martensite is recognised as a very strong phase in carbon steels, its initial yielding commences at low stresses and the tensile stress-strain curve shows a smooth, rounded form. Evidence is presented from x-ray diffraction to show that this behaviour is due to the presence of intra-granular stresses that are residues after the shear transformation from austenite to martensite. These internal stresses are reduced in magnitude by plastic deformation and also by tempering. Reduction of internal stress due to plasticity is shown by a decrease in XRD line broadening after deformation. A simple model is presented in which the stress-strain behaviour is controlled by relaxation of the internal stresses almost up to the point of the ultimate tensile strength. It demonstrates that only a very small fraction of the material remaining in a purely elastic state provides a large stabilising effect resisting necking. A corollary of this is that the uniform elongation of martensitic steel actually increases with increase in the strength level. Effects of heat treatment are also reproduced in the model, including the increase in conventional yield stress (Rp0.2) that occurs after low temperature tempering.