Stability of oxide films formed on mild steel in turbulent flow conditions of alkaline solutions at elevated temperatures

In the industries involving alkaline solutions in different process streams, the nature and stability of oxide films formed on the metallic surfaces determine the rates of erosion–corrosion of the equipment. In the present study the characteristics of the oxide films formed on AISI 1020 steel in a 2.75 M sodium hydroxide solution at temperatures up to 175°C, have been investigated by employing electrochemical techniques of cyclic voltammetry and chronoamperometry. The experiments were carried out in an autoclave system based upon a ‘rotating cylinder electrode’ geometry to determine the effects of turbulence on the stability of the films. The results suggest that little protection is afforded in the active region (at about −0.8 V_SHE). In the passive region at low potentials (−0.6 V to −0.4 V_SHE), it appears the films are compact and more stable, and therefore provide good protection. At higher potentials (>−0.4 V_SHE) in the passive region, the results suggest that film formation and dissolution occur simultaneously and the increase in temperature and turbulence causes a breakdown of the passive film resulting in a situation similar to nonprotective magnetite growth.

Strain rate effects for strength of geopolymer concrete

The effects of strain rate on compressive and tensile strength of fly ash based geopolymer concrete were investigated experimentally. Four mixes of geopolymer concrete using different alkaline solutions and under vary curing conditions were prepared. One mix of ordinary Portland cement (OPC) concrete was prepared for comparison. Both Quasi-Static tests using standard MTS and dynamic tests using Split-Hopkinson pressures bar (SHPB) were conducted, which were giving varying strain rate loadings from 10‾⁷ to 103 per second. The strain rate effect is presented as the ratio of dynamic compressive strength to static compressive strength (DIF). Results show that DIFs of geopolymer concrete are generally higher than those of OPC concrete at strain range of 187/s to 346/s (compression tests) and 7/s to 13/s (splitting tensile tests), respectively. This tendency is independent on loading regimes (compression or tension). This suggests that geopolymer concrete can be used as an alternative construction material to OPC concrete for the structures which has a high risk of being subjected to impact loadings.

Cobalt carbonate hydroxide nanowire array on ti mesh: an efficient and robust 3D catalyst for on-demand hydrogen generation from alkaline naBH4 solution.

In this work, for the first time, a cobalt carbonate hydroxide (Co(CO3 )0.5 (OH)⋅0.11 H2 O) nanowire array on Ti mesh (CHNA/Ti) was applied to drive the dehydrogenation of alkaline NaBH4 solution for on-demand hydrogen production. Compared with other nanostructured Co-based catalyst systems, CHNA/Ti can be activated more quickly and separated easily from fuel solutions. This self-supported cobalt salt nanowire array catalyst works as an efficient and robust 3D catalyst for the hydrolysis reaction of NaBH4 with a hydrogen generation rate of 4000 mL min(-1)  gCo (-1) and a low apparent activation energy of 39.78 kJ mol(-1) and offers an attractive system for on-demand hydrogen generation.