Strain-responsive polyurethane/PEDOT:PSS elastomeric composite fibers with high electrical conductivity

It is a challenge to retain the high stretchability of an elastomer when used in polymer composites. Likewise, the high conductivity of organic conductors is typically compromised when used as filler in composite systems. Here, it is possible to achieve elastomeric fiber composites with high electrical conductivity at relatively low loading of the conductor and, more importantly, to attain mechanical properties that are useful in strain-sensing applications. The preparation of homogenous composite formulations from polyurethane (PU) and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) that are also processable by fiber wet-spinning techniques are systematically evaluated. With increasing PEDOT:PSS loading in the fiber composites, the Young's modulus increases exponentially and the yield stress increases linearly. A model describing the effects of the reversible and irreversible deformations as a result of the re-arrangement of PEDOT:PSS filler networks within PU and how this relates to the electromechanical properties of the fibers during the tensile and cyclic stretching is presented. Conducting elastomeric fibers based on a composite of polyurethane (PU) and PEDOT:PSS, produced by a wet-spinning method, have high electrical conductivity and stretchability. These fibers can sense large strains by changes in resistance. The PU/PEDOT:PSS fiber is optimized to achieve the best strain sensing. PU/PEDOT:PSS fibers can be produced on a large scale and integrated into conventional textiles by weaving or knitting. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Achieving outstanding mechanical performance in reinforced elastomeric composite fibers using large sheets of graphene oxide

A simple fiber spinning method used to fabricate elastomeric composite fibers with outstanding mechanical performance is demonstrated. By taking advantage of the large size of as-prepared graphene oxide sheets (in the order of tens of micrometers) and their liquid crystalline behavior, elastomeric composite fibers with outstanding low strain properties have been fabricated without compromising their high strain properties. For example, the modulus and yield stress of the parent elastomer improved by 80- and 40-fold, respectively, while maintaining the high extensibility of ∼400% strain inherent to the parent elastomer. This outstanding mechanical performance was shown to be dependent upon the GO sheet size. Insights into how both the GO sheet size dimension and dispersion parameters influence the mechanical behavior at various applied strains are discussed.

Wireless sensor networks for heritage object deformation detection and tracking algorithm

Deformation is the direct cause of heritage object collapse. It is significant to monitor and signal the early warnings of the deformation of heritage objects. However, traditional heritage object monitoring methods only roughly monitor a simple-shaped heritage object as a whole, but cannot monitor complicated heritage objects, which may have a large number of surfaces inside and outside. Wireless sensor networks, comprising many small-sized, low-cost, low-power intelligent sensor nodes, are more useful to detect the deformation of every small part of the heritage objects. Wireless sensor networks need an effective mechanism to reduce both the communication costs and energy consumption in order to monitor the heritage objects in real time. In this paper, we provide an effective heritage object deformation detection and tracking method using wireless sensor networks (EffeHDDT). In EffeHDDT, we discover a connected core set of sensor nodes to reduce the communication cost for transmitting and collecting the data of the sensor networks. Particularly, we propose a heritage object boundary detecting and tracking mechanism. Both theoretical analysis and experimental results demonstrate that our EffeHDDT method outperforms the existing methods in terms of network traffic and the precision of the deformation detection.

Grain growth and β-Mg17Al12 intermetallic phase dissolution during heat treatment and its impact on deformation behavior of AZ80 Mg-alloy

Microstructure evolution after solutionizing and ageing treatment of cast AZ80 Mg alloy were investigated using optical and scanning electron microscopy. Effect of these treatments on grain size, β-Mg17Al12 intermetallic phase, mechanical behavior, and flow asymmetry were investigated. The initial continuous network of β-phase found to be reduced after solutionizing. The dissolution of β-phase and simultaneous grain growth are found to be interrelated. Mechanical properties including yield strength, maximum strength (ultimate compressive strength), and maximum strain attainable in compressive found almost twice than the corresponding values obtained in tension. The asymmetry in compressive and tensile properties is found to decrease with grain size at certain solutionizing duration. Particular heat treatment found to offer best combination of tensile compressive flow properties in AZ80 Mg alloy. Aging under certain conditions found to minimize the strength asymmetry. © ASM International.

Strain partitioning in dual-phase steels containing tempered martensite

Tempering has been used as a method to develop a range of dual phase steels with the same martensite morphology and volume fraction, but containing phases with different relative strengths. These steels were used to examine the strain partitioning between the two constituent phases experimentally through mechanical testing and numerically through finite element modelling. It was found that increasing the differential in strength between the two phases not only produces regions of high strain, but also regions of low strain. On average, a larger difference in strength between the phases increased the strain carried by the softer phase. There was no discernible preferential strain localisation to the ferrite/martensite interface, with the regions of strain localisation being determined by the morphology of the microstructure. A direct correlation between the average strain in the ferrite, and the measured ductility has been found. © 2014 Elsevier B.V.

The formation of complex microstructures after different deformation modes in advanced high-strength steels

The microstructure of transformation induced plasticity (TRIP) and dual phase (DP) multiphase steels after stamping of an industrial component at different strain levels was investigated using transmission electron microscopy. The TRIP steel microstructure showed a more complex dislocation substructure of ferrite at different strain levels than DP steel. The deformation microstructure of the stamped parts was compared to the deformation microstructure in these complex steels for different "equivalent" tensile strains. It was found that the microstructures are similar only at high levels of strain (>10 pct) for both steels. © 2014 The Minerals, Metals & Materials Society and ASM International.

Severe plastic deformation of TWIP steel

The severe plastic deformation of a Twinning Induced Plasticity (TWIP), 0.61C-22.3Mn-0.19Si-0.14Ni-0.27Cr (wt. %) steel by Equal Channel Angular Pressing (ECAP) at elevated temperatures was used to study the deformation mechanism as a function of accumulated strain and processing parameters. The relationship between the microstructures after different deformation schedules of ECAP at the temperatures of 200, 300 and 400oC, strain hardening behavior and mechanical properties was studied. The best balance between strength and ductility (1702 MPa and 24%) was found after 2 passes at 400oC and 300oC of ECAP. It was due to the formation of deformation microbands and twins in the microstructure. The twinning was observed after all deformation schedules except after 1 pass at 400oC. The important finding was the formation of twins in the ultrafine grains. Moreover, the stacking faults were observed in the subgrains with the size of 50nm. It is also worth mentioning the formation of nano- twins within the micro-twins at the same time. It was found that the deformation schedule affects the dislocation substructure with formation of deformation bands, cells, subgrains, two variants of twins that, in turn, influence the strain-hardening behavior and mechanical properties. Keywords: Twinning Induced Plasticity steels; Equal Channel Angular Pressing; mechanical properties; transmission electron microscopy; micro/nano twins; dislocation substructure.

The effect of deformation twinning on stress localization in a three dimensional TWIP steel microstructure

We present an investigation of the effect of deformation twinning on the visco-plastic response and stress localization in a low stacking fault energy twinning-induced plasticity (TWIP) steel under uniaxial tension loading. The three-dimensional full field response was simulated using the fast Fourier transform method. The initial microstructure was obtained from a three dimensional serial sectionusing electron backscatter diffraction. Twin volume fraction evolution upon strain was measured so the hardening parameters of the simple Voce model could be identified to fit both the stress-strain behavior and twinning activity. General trends of texture evolution were acceptably predicted including the typical sharpening and balance between the 1 1 1 fiber and the 1 0 0 fiber. Twinning was found to nucleate preferentially at grain boundaries although the predominant twin reorientation scheme did not allow spatial propagation to be captured. Hot spots in stress correlated with the boundaries of twinned voxel domains, which either impeded or enhanced twinning based on which deformation modes were active locally.

Microstructure and texture evolution during tensile deformation of symmetric/asymmetric-rolled low carbon microalloyed steel

The deformation and fracture mechanisms of a low carbon microalloyed steel processed by asymmetric rolling (AsR) and symmetric rolling (SR) were compared by microstructural and texture evolutions during uniaxial tensile deformation. A realistic microstructure-based micromechanical modeling was involved as well. AsR provides more effective grain refinement and beneficial shear textures, leading to higher ductility and extraordinary strain hardening with improved yield and ultimate tensile stresses as well as promoting the occurrence of ductile fracture. This was verified and further explained by means of the different fracture modes during quasi-static uniaxial deformation, the preferred void nucleation sites and crack propagation behavior, and the change in the dislocation density based on the kernel average misorientation (KAM) distribution. The equivalent strain/stress partitioning during tensile deformation of AsR and SR specimens was modeled based on a two-dimensional (2D) representative volume element (RVE) approach. The trend of strain/stress partitioning in the ferrite matrix agrees well with the experimental results.

The effect of low cycle fatigue, ratcheting and mean stress relaxation on stress-strain response and microstructural development in a dual phase steel

This study examines the cyclic plastic deformation behavior and microstructural development of a dual phase steel in both symmetric and asymmetric cycling in strain and stress control modes. The low-cycle fatigue (LCF) and mean stress relaxation (MSR) tests show very similar fatigue lifetimes. However, fatigue lifetimes reduce and prominent accumulation of directional strain was observed in ratcheting. A microstructural analysis has revealed that the type of cyclic test carried out has a noticeable impact on the substructural development, and this has been correlated with differences in accumulated tensile strain. Electron backscatter diffraction investigation has shown larger in-grain misorientation for ratcheting specimen in comparison with LCF and MSR specimens. The orientation of ferrite grains was found to have very little effect on their substructural development, and strain localization commonly occurred in the ferrite at the ferrite/martensite interface.

Warm deformation and annealing behaviour of iron-silicon-(carbon) steel sheets

Single pass warm rolling and compression experiments were carried out from ambient to 800°C for ultra-low carbon (ULC) steel with ∼100 ppm carbon and interstitial free (IF) steels, both with two levels of silicon. Subsequently, annealing was done in order to recrystallize the deformed specimens. The main purpose of this study was to understand the effects of rolling temperature and silicon on stress responses and textures. This study comprises two main themes: flow stress and strain rate sensitivity during compression and shear banding and textures in warm rolled specimens. The effects of deformation temperature on in-grain shear bands were different between ULC-Si and IF-Si steels. As in previous work with more conventional steels, in-grain shear bands in the IF grade had low sensitivity to rolling temperature, while those in the ULC grade depended significantly on the deformation temperature. However, the temperature profile of shear banding in the ULC grade was approximately 150°C higher than in previous work. Deformation and recrystallisation textures for both IF and ULC grades depended on their rolling temperatures. The variation of both grain size and texture after annealing can be explained by the rise and fall of in-grain shear banding activity which is related to the strain rate sensitivity.

Yielding behaviour of martensite in steel

Although martensite is recognised as a very strong phase in carbon steels, its initial yielding commences at low stresses and the tensile stress-strain curve shows a smooth, rounded form. Evidence is presented from x-ray diffraction to show that this behaviour is due to the presence of intra-granular stresses that are residues after the shear transformation from austenite to martensite. These internal stresses are reduced in magnitude by plastic deformation and also by tempering. Reduction of internal stress due to plasticity is shown by a decrease in XRD line broadening after deformation. A simple model is presented in which the stress-strain behaviour is controlled by relaxation of the internal stresses almost up to the point of the ultimate tensile strength. It demonstrates that only a very small fraction of the material remaining in a purely elastic state provides a large stabilising effect resisting necking. A corollary of this is that the uniform elongation of martensitic steel actually increases with increase in the strength level. Effects of heat treatment are also reproduced in the model, including the increase in conventional yield stress (Rp0.2) that occurs after low temperature tempering.

Constitutive analysis of hot deformation behavior of a Ti6Al4V alloy using physical based model

The effect of deformation parameters on the flow behavior of a Ti6Al4V alloy has been studied to understand the deformation mechanisms during hot compression. Cylindrical samples with partially equiaxed grains were deformed in the α+β phase region at different thermo-mechanical conditions. To develop components with tailored properties, the physically based Estrin and Mecking (EM) model for the work hardening/dynamic recovery combined with the Avrami equation for dynamic recrystallization was used to predict the flow stress at varying process conditions. The EM model revealed good predictability up to the peak strain, however, at strain rates below 0.01s^-1, a higher B value was observed due to the reduced density of dislocation tangles. In contrast, the flow softening model revealed higher value of constants a and b at high strain rates due to the reduction in the volume fraction of dynamic recrystallization and larger peak strain. The predicted flow stress using the combined EM+Avrami model revealed good agreement with the measured flow stress resulted in very low average absolute relative error value. The microstructural analysis of the samples suggests the formation of coarse equiaxed grains together with the increased β phase fraction at low strain rate leads to a higher flow softening.

Softening behavior of Ti6Al4V alloy during hot deformation

The effect of strain rate and strain on the hot compression behavior of Ti6Al4V has been analysed to understand the microstructural evolution and restoration behavior. Cylindrical samples with partially equiaxed grains were deformed in the α+β region at different thermo-mechanical conditions. EBSD has been used to study the microstructural evolution and the flow softening mechanisms. The microstructural evolution showed a complex restoration behaviour, where both fragmentation and nucleation of new grains have been observed. The volume fraction of the equiaxed grains increased with an increase in the strain, but decreased with the strain rate. At the same time, the average grain size of the equiaxed grains decreased with an increase in both the strain and strain rate. The measured activation energy for deformation revealed a good agreement with reported values in the literature.

Strain gradients in Cu-Fe thin films and multilayers during micropillar compression

Plastic strain gradients can influence the work-hardening behaviour of metals due to the accumulation of geometrically necessary discolations at the micron/submicron scale. A finite element model based on the conventional theory of mechanism-based strain-gradient plasticity has been developed to simulate the micropillar compression of Cu–Fe thin films and multilayers. The modelling results show that the geometric constraints lead to inhomogeneous deformation in the Cu layers, which agrees well with the bulging of Cu layers observed experimentally. Plastic strain gradients develop inside the individual layers, leading to extra work-hardening due to the accumulation of geometrically necessary dislocations. In the multilayer specimens, the Cu layers deform more severely than the Fe layers, resulting in the development of tensile stresses in the Fe layers. It is proposed that these tensile stresses are responsible for the development of micro-cracks in the Fe layers.