Continuous cooling transformation of deformed austenite in highly hole-expandable steels

The effects of Si and Mn contents on transformation temperature _r3, transformed microstructure and mechanical properties of three kinds of low-carbon steels during continuous cooling were investigated. A _r3 rises by 15-25°C when increasing Si content from 0.50% to 1.35%, and it drops by 30-50°C when increasing Mn content from 0.97% to 1.43%. The effect of Mn on A _r3 is more significant than Si. Si stimulates the precipitation of the high-temperature equiaxed ferrite to suppress the bainite transformation, but Mn not only provides the grain refining of transformed microstructure but also stimulates the forming of bainite. The homogeneous and grain refining diphase ferrite/bainite steel (w(Si)=0.56, w(Mn)=1.43) can be obtained after deformed at 850°C and cooled at the rate 30°C/s, of which the tensile strength is up to 654 MPa.

Effects of Si on microstructural evolution and mechanical properties of hot-rolled ferrite and bainite dual-phase steels

Based on the thermo-mechanical controlled process, the effects of Si on microstructural evolution, tensile properties, impact toughness, and stretch-flangeability of ferrite and bainite dual-phase (FBDP) steels were systematically investigated. The addition of Si from 0 to 0.95% promoted the formation of fine and equiaxed ferrite grains, and high Si (0.95%) also resulted in the formation of blocky martensite islands and retained austenite. Yield and tensile strengths, and uniform and total elongations all increased with increasing Si content. Therefore, the tensile strength and ductility balance was improved by Si addition due to the increasing strain-hardening rate. The fractured morphologies after hole-expansion showed that the excellent stretch-flangeability of FBDP steels was associated with the micro-cracks propagating through in ferrite phase as well as the elongated ferrite grains along the direction perpendicular to the crack. 0.95% Si steel had a similar high combination of tensile strength and impact toughness to 0.55% Si steel, and especially 0.95% Si steel exhibited an excellent combination of tensile strength and stretch-flangeability.

Comparative study of ni effect on the corrosion behavior of low alloy steels in FGD and acid rain environments

The alloying effect of a small amount of nickel on low alloy steel for application to flue gas desulfurization(FGD) systems was studied. The structural characteristics of the rust layer were investigated by scanning electron microscopy(SEM). The electrochemical properties were examined by means of potentiostatic polarization test, potentiodynamic polarization test, and electrochemical impedance spectroscopy(EIS) in a modified green death solution of 16.9 vol.% H2SO4+0.35 vol.% HC1 at 60°C and an acid rain solution of 6.25 X 10-5 M H2S04+5.5 X 10-3 M NaCl at room temperature. It was found that as the amount of nickel increased, the corrosion rate increased in the modified green death solution, which seemed to result from micro-galvanic corrosion between NiS and alloy matrix. In acid rain solution, the corrosion rate decreased as the amount of nickel increased due to the repulsive force of NiFe204 rust against Cl-ions by electronegativity.

Nanoscale precipitation in advanced high strength steels

Precipitation strenghthening is one of the most important approaches for enhancing the strenght of microalloyed steels. This study has made a significant contribution in understanding the nucleation and growth mechanism of nanoscale interphase precipitates in steel during commercial processes. Atom Probe Tomography revealed the existence of nanoscale clusters with precipitates that then dictate the final strength.

Characterization of nano-structured bainitic steel

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200°C for 10 days to produce a nano-structured bainitic steel. The microstructure consisted of nanobainitic ferrite laths with a high dislocation density and retained austenite films having extensive twins. The crystallographic analysis using TEM and EBSD revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with their parent austenite. There was only one type of packet identified in a given transformed austenite grain. Each packet consisted of two different blocks having variants with the same habit plane, but different crystallographic orientations. Atom Probe Tomography (APT) revealed that the carbon content of nanobainitic ferrite laths was much higher than expected from the para-equilibrium level. This was explained due to the long heat treatment time, which led to the formation of fine Fe-C clusters on areas with high dislocation densities in bainitic ferrite laths.

Fabrication, microstructure and mechanical properties of high performance ferrite-bainite steels

Low cost ferrite and bainite(FB) steels offer the prospect of high ultimate tensile strength combined with high hole expansion ratio. The enhanced strain hardening and formabilityof FB steels were primarily associated with the fine ferrite matrix, the low residual stresses and dislocation densityand compatible deformation between both phases.This overview describes the various techniques to produce FB steels, and comparestheresulting microstructure, tensile propertiesand tretchflangeabilitywith conventional HSLA and DP steels.A new generation of ultrafine ferrite and nano-scalebainiteautomotive steelsisunder development forthe futuredemands of extremely high strength and ductilitythroughthe fabricationtechnologiesinvolvingphase transformationsandplastic deformation.

Multiscale modelling of stress and strain partitioning in high strength dual phase steels

Multiscale modelling of stress and strain partitioning in DP steel was carried out using both realistic microstructure-based RVE models as well as stochastic microstructures generated by Monte Carlo method. The stochastic microstructure models were shown to resemble that of realistic microstructures, enabling research on the specific aspects of the microstructure that could be difficult to control and study during experimental work. One such feature of the realistic microstructures studied in this work was the grain size and microstructure morphology. The microstructures were generated with varying average grain sizes while all other parameters, such as boundary conditions, material properties and volume fractions of martensite and ferrite were kept constant. It is found that the effect of grain size is much more pronounced during the initial localisation of the plastic deformation at and around the interface of the phases. In addition, the decrease in ductility and increase in strength of the DP steels are directly related to the refinement of grain sizes of each phase and the stress-strain partitioning in between them.

Effect of tensile pre-strain on bending and unloading of automotive steels

In recent years, advanced high strength steels (AHSS) have been used in a wide range of automotive applications; they may have property variations through the thickness and the properties may also be dependent of prior processing including pre-straining. In order to model forming processes precisely using, for example, finite element analysis, it is important that material input data should adequately reflect these effects. It is known that shape defects in roll forming are related to small strains in material that has undergone prior deformation in a different strain path. Much research has already been performed on the change in the Young’s Modulus once a steel sheet has been plastically deformed,however many of these tests have only been conducted using tensile testing, and therefore may not take into account differences in compressive and tensile unloading. This research investigates the effect of tensile pre-straining on bending behaviour for various types of material;in bending, one half of the sheet will load and unload in compression and hence experience deformation under a reversed stress. Four different materials were pre-strained in tension with 1%, 3%, 7%, 11% and 25% elongation. Using a free bending test, moment curvature diagrams were obtained for bending and unloading. The results showed that the characteristics of the moment curvature diagram depended on the degree of pre-straining; more highly strained samples showed an earlier elastic-plastic transformation and a decreased Young's Modulus during unloading. This was compared to previous literature results using only tensile tests. Our results could influence the modeling of springback in low tension sheet operations, such as roll forming.

Development of boundary misorientations during grain growth in silicon steels

Changes in grain size, texture and misorientation distributions have been monitored during extensive normal grain growth in 3%Si steels. The boundary misorientation distributions deviate significantly from the Mackenzie relationship. Comparisons of correlated and uncorrelated distributions show large excesses of low angle boundaries. However, these are not a result of low energy boundaries being favoured during grain growth since the deviation diminishes as growth proceeds. The effect originates in the nucleation of grains in colonies of similar orientation during primary recrystallisation. A slight tendency for promotion of 60º boundaries may indicate some preference for the retention of lower energy twin boundaries during grain growth in silicon steel.