Effect of pre-straining and bake hardening on the microstructure and mechanical properties of CMnSi trip steels

The effects of pre-straining and bake hardening on the mechanical behaviour and microstructural changes were studied in two CMnSi TRansformation-Induced Plasticity (TRIP) steels with different microstructures after intercritical annealing. The TRIP steels before and after pre-straining and bake hardening were characterised by X-ray diffraction, optical microscopy, transmission electron microscopy, three dimensional atom probe and tensile tests. Both steels exhibited discontinuous yielding behaviour and a significant strength increase with some reduction in ductility after pre-straining and bake hardening treatment. The following main microstructural changes are responsible for the observed mechanical behaviours: a decrease in the volume fl:action of retained austenite, a increase in the dislocation density and the formation of cell substructure in the polygonal ferrite, higher localized dislocation density in the polygonal ferrite regions adjacent to martensite or retained austenite, and the precipitation of fine iron carbides in bainite and martensite. The mechanism for the observed yield point phenomenon in both steels after treatment was analysed.

Crystallographic analysis of nano-structured bainitic steels

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200 and 350°C bainitic transformation temperatures. The microstructure was consisted of bainitic ferrite lath and retained austenite for both heat treatment conditions. The crystallographic analysis revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with their parent austenite. The isothermal bainite transformation temperature has a significant effect on the retained austenite characteristics and the variant selection of the bainitic ferrite laths. In general, a decrease in the isothennal bainite transformation temperature refined the bainitic structure and weakened the variant selection.

A study of the strengthening mechanism in the thermomechanically processed TRIP/TWIP steel

The strengthening mechanism responsible for the unique combination of ultimate tensile strength and elongation in a multiphase Fe-0.2C-1.5Mn-1.2Si-0.3Mo-0.6Al-0.02Nb (wt%) steel was studied. The microstructures with different volume fraction of polygonal fenite, bainite and retained austenite were simulated by controlled thermomechanical processing. The interupted tensile test was used to study the bainitic ferrite, retained austenite and polygonal ferrite behavior as a function of plastic strain. X-ray analysis was used to characterize the volume fraction and carbon content of retained austenite. TEM and heat-tinting were utilized to analyze the effect of bainitic fenite morphology on the strain induced transformation of retained austenite and retained austenite twinning as a function of strain in the bulk material. The study has shown that the austenite twinning mechanism is more preferable than the transformation induced plasticity mechanism during the early stages of deformation for a microstructure containing I5% polygonal ferrite, while the transformation induced plasticity effect is the main mechanism in when there is 50% of polygonal ferrite in the microstructure. The baillitic fenite morphology affects the deformation mode of retained austenite during straining. The polygonal fenite behavior during straining depends on dislocation substructure tonned due to the deformation and the additional mobile dislocations caused by the TRIP effect. TRIP and TWIP effects depend not only on the chemical and mechanical stability of retained austenite, but also on the interaction of the phases during straining.

Electron backscattering diffraction analysis of an ancient wootz steel blade from central India

The electron backscattering diffraction technique was used to analyse the nature of carbides present in an ancient wootz steel blade. Bulky carbides, pro-eutectoid carbide along the prior austenite grain boundaries and fine spheroidized carbides were detected. Electron backscattering diffraction was employed to understand the texture of these carbides. The orientations of the cementite frequently occur in clusters, which points to a common origin of the members of the cluster. For the bands of coarse cementite, the origin is probably large coarse particles formed during the original cooling of the wootz cake. Pearlite formed earlier in the forging process has led to groups of similarly oriented fine cementite particles. The crystallographic texture of the cementite is sharp whereas that of the ferrite is weak. The sharp cementite textures point to the longevity of the coarse cementite throughout the repeated forging steps and to the influence of existing textured cementite on the nucleation of new cementite during cooling.

Study of the effect of grain size on the dynamic mechanical properties of microalloyed steels

In the present paper the effect of grain refinement on the dynamic response of ultra fine-grained (UFG) structures for C–Mn and HSLA steels is investigated. A physically based flow stress model (Khan-Huang-Liang, KHL) was used to predict the mechanical response of steel structures over a wide range of strain rates and grain sizes. However, the comparison was restricted to the bcc ferrite structures. In previous work [K. Muszka, P.D. Hodgson, J. Majta, A physical based modeling approach for the dynamic behavior of ultra fine-grained structures, J. Mater. Process. Technol. 177 (2006) 456–460] it was shown that the KHL model has better accuracy for structures with a higher level of refinement (below 1 μm) compared to other flow stress models (e.g. Zerrili-Armstrong model). In the present paper, simulation results using the KHL model were compared with experiments. To provide a wide range of the experimental data, a complex thermomechanical processing was applied. The mechanical behavior of the steels was examined utilizing quasi-static tension and dynamic compression tests. The application of the different deformation histories enabled to obtain complex microstructure evolution that was reflected in the level of ferrite refinement.

Crystallographic analysis of nanobainitic steels

Electron back-scattered diffraction in conjunction with transmission electron microscopy was employed to investigate the crystallographic nature of bainitic laths formed at relatively low transformation temperatures where a nanostructured bainite forms. It was revealed that the bainitic ferrite laths are close to the Nishiyama–Wasserman orientation relationship with the parent austenite. Furthermore, the temperature showed a significant effect on the retained austenite characteristics and the variant selection of the bainitic ferrite laths. A decrease in temperature generally refined the bainitic structure and weakened the variant selection.

Cyclic deformation of advanced high-strength steels : mechanical behavior and microstructural analysis

The fatigue properties of multiphase steels are an important consideration in the automotive industry. The different microstructural phases present in these steels can influence the strain life and cyclic stabilized strength of the material due to the way in which these phases accommodate the applied cyclic strain. Fully reversed strain-controlled low-cycle fatigue tests have been used to determine the mechanical fatigue performance of a dual-phase (DP) 590 and transformation-induced plasticity (TRIP) 780 steel, with transmission electron microscopy (TEM) used to examine the deformed microstructures. It is shown that the higher strain life and cyclic stabilized strength of the TRIP steel can be attributed to an increased yield strength. Despite the presence of significant levels of retained austenite in the TRIP steel, both steels exhibited similar cyclic softening behavior at a range of strain amplitudes due to comparable ferrite volume fractions and yielding characteristics. Both steels formed low-energy dislocation structures in the ferrite during cyclic straining.

Refinement of microstructure in steels through thermomechanical processing

The refinement of microstructure is the most generally accepted approach to simultaneously improve the strength and toughness in steels. In the current study, the role of dynamic/static phase transformation on the ferrite grain refinement was investigated using different thermomechanical processing routes. A Ni-30Fe austenitic model alloy was also used to investigate the substructure character formed during deformation. It was revealed that the microstructure of steel could further be refined to the nanoscale through both the control of processing route and steel composition design.

Microstructure and mechanical properties of thermomechanically processed TRIP steel

The strengthening mechanism responsible for the unique combination of ultimate tensile strength and elongation in a multiphase Fe-0.2C-1.5Mn-1.2Si-0.3Mo-0.6Al-0.02Nb (wt%) steel was studied. The microstructures with different volume fractions of polygonal ferrite, bainite and retained austenite were simulated by controlled thermomechanical processing. The interrupted tensile test was used to study the bainitic ferrite, retained austenite and polygonal ferrite behaviour as a function of plastic strain. X-ray analysis was used to characterise the volume fraction and carbon content of retained austenite. Transmission electron microscopy was utilised to analyse the effect of bainitic ferrite morphology on the strain induced transformation of retained austenite and retained austenite twinning as a function of strain in the bulk material. The study has shown that the austenite twinning mechanism is more preferable than the transformation induced plasticity (TRIP) mechanism during the early stages of deformation for a microstructure containing 15% polygonal ferrite, while the transformation induced plasticity effect is the main mechanism when there is 50% of polygonal ferrite in the microstructure. The bainitic ferrite morphology affects the deformation mode of retained austenite during straining. The polygonal ferrite behaviour during straining depends on dislocation substructure formed due to the deformation and the additional mobile dislocations caused by the TRIP effect. Operation of TRIP or twinning mechanisms depends not only on the chemical and mechanical stability of retained austenite, but also on the interaction of the phases during straining.

Softening mechanisms in two duplex stainless steels deformed in hot torsion

The aim of the present work was to undertake a detailed investigation of the softening mechanisms during hot deformation of a 21Cr-10Ni-3Mo (steel A) and a 21Cr-8Ni-3Mo (steel B) austenite/ferrite duplex stainless steels containing about 60% and 30% of austenite, respectively. The steels were subjected to hot deformation in torsion performed at 900 ºC and 1200 ºC using a strain rate of 0.7 s-1 to several strain levels. Quantitative optical and transmission electron microscopy were used in the investigation. Austenite was observed to soften via dynamic recovery (DRV) and dynamic recrystallisation (DRX) accompanied by DRV for the deformation temperatures of 900 °C and 1200 °C, respectively, for the both steels studied. DRX of austenite largely occurred through strain-induced grain boundary migration, complemented by (multiple) twinning, and developed significantly faster in steel A than in steel B, indicating that considerably larger strains partitioned into austenite in the former steel during deformation at 1200 °C. The above softening mechanism was accompanied by the formation of DRX grains from subgrains along the austenite/ferrite interface and by large-scale subgrain coalescence. At 900°C, stressassisted phase transitions between austenite and ferrite were observed, characterised by dissolution of the primary austenite, formation of Widmanstätten secondary austenite and gradual globularisation of the microstructure with increasing strain. These processes appeared to be significantly more widespread in steel B. The softening mechanism within ferrite for the both steels studied was classified as “continuous DRX”, characterised by a gradual increase in misorientations between neighbouring subgrains with strain, for the both deformation temperatures.

EBSD investigation of the microstructure and texture characteristics of hot deformed duplex stainless steel

The microstructure and crystallographic texture characteristics were studied in a 22Cr-6Ni-3Mo duplex stainless steel subjected to plastic deformation in torsion at a temperature of 1000 °C using a strain rate of 1 s⁻¹. High-resolution EBSD was successfully used for precise phase and substructural characterization of this steel. The austenite/ferrite ratio and phase morphology as well as the crystallographic texture, subgrain size, misorientation angles and misorientation gradients corresponding to each phase were determined over large sample areas. The deformation mechanisms in each phase and the interrelationship between the two are discussed.

Effect of pre-straining and bake hardening on the microstructure and mechanical properties of CMnSi trip steels

The effects of pre-straining and bake hardening on the mechanical behaviour and microstructural changes were studied in two CMnSi TRansformation-Induced Plasticity (TRIP) steels with different microstructures after intercritical annealing. The TRIP steels before and after pre-straining and bake hardening were characterised by X-ray diffraction, optical microscopy, transmission electron microscopy, three dimensional atom probe and tensile tests. Both steels exhibited discontinuous yielding behaviour and a significant strength increase with some reduction in ductility after pre-straining and bake hardening treatment. The following main microstructural changes are responsible for the observed mechanical behaviours: a decrease in the volume fraction of retained austenite, an increase in the dislocation density and the formation of cell substructure in the polygonal ferrite, higher localized dislocation density in the polygonal ferrite regions adjacent to martensite or retained austenite, and the precipitation of fine iron carbides in bainite and martensite. The mechanism for the observed yield point phenomenon in both steels after treatment was analysed.

Mechanisms of dynamic strain induced transformation and post-deformation evolution

In this study, a novel experimental approach was applied to study the mechanism of the equiaxed shape retention in dynamic strain induced ferrite during deformation. The post-deformation ferrite evolution in both static and dynamic transformation was studied. The refinement potential and the origin of their differences in both mechanisms were analysed.

Characterization of the bake-hardening behavior of transformation induced plasticity and dual-phase steels using advanced analytical techniques

The bake-hardening (BH) behavior of TRansformation Induced Plasticity (TRIP) and Dual-Phase (DP) steels after intercritical annealing (IA) has been studied using transmission electron microscopy, X-ray diffraction and three dimensional atom probe tomography. It was found for the DP steel that carbon can segregate to dislocations in the ferrite plastic deformation zones where there is a high dislocation density around the "asquenched" martensite. The carbon pinning of these dislocations, in turn, increases the yield strength after aging. It was shown that bake-hardening also leads to rearrangement of carbon in the martensite leading to the formation of rod-like low temperature carbides in the DP steel. Segregation of carbon to microtwins in retained austenite of the TRIP steel was also evident. These factors, in combination with the dislocation rearrangement in ferrite through the formation of cells and microbands in the TRIP steel after pre-straining, lead to the different bake-hardening responses of the two steels.

Microstructure and properties of a C-Mn steel subjected to heavy plastic deformation

In the present paper an effect of severe plastic deformation (SPD) on the microstructural evolution and properties of a plain C-Mn steel was investigated. The SPD was accomplished by the MaxStrain system which deforms material along two perpendicular axes while the deformation along the third axis is fully constrained. The applied amounts of true strains were 5 and 20 in total. Deformation was conducted at room and 500°C temperatures. Some samples deformed at room temperature were subsequently annealed at 500°C. A microstructural analysis by SEM/EBSD was used for recognition the low- and high-angle grain boundaries. It was found that the collective effect of severe plastic deformation (true strain of 20) and further annealing promotes the formation of high-angle grain boundaries and uniform fine grained microstructure. The refinement of ferrite microstructure results in a significant increase in strength and hardness.