Collagen type-I leads to in vivo matrix mineralization and secondary stabilization of Mg-Zr-Ca alloy implants

Biodegradable magnesium-zirconia-calcium (Mg-Zr-Ca) alloy implants were coated with Collagen type-I (Coll-I) and assessed for their rate and efficacy of bone mineralization and implant stabilization. The phases, microstructure and mechanical properties of these alloys were analyzed using X-ray diffraction (XRD), optical microscopy and compression test, respectively, and the corrosion behavior was established by their hydrogen production rate in simulated body fluid (SBF). Coll-I extracted from rat tail, and characterized using fourier transform infrared (FT-IR) spectroscopy, was used for dip-coating the Mg-based alloys. The coated alloys were implanted into the femur bones of male New Zealand white rabbits. In vivo bone formation around the implants was quantified by measuring the bone mineral content/density (BMC/BMD) using dual-energy X-ray absorptiometry (DXA). Osseointegration of the implant and new bone mineralization was visualized by histological and immunohistochemical analysis. Upon surface coating with Coll-I, these alloys demonstrated high surface energy showing enhanced performance as an implant material that is suitable for rapid and efficient new bone tissue induction with optimal mineral content and cellular properties. The results demonstrate that Coll-I coated Mg-Zr-Ca alloys have a tendency to form superior trabecular bone structure with better osteoinduction around the implants and higher implant secondary stabilization, through the phenomenon of contact osteogenesis, compared to the control and uncoated ones in shorter periods of implantation. Hence, Coll-I surface coating of Mg-Zr-Ca alloys is a promising method for expediting new bone formation in vivo and enhancing osseointegration in load bearing implant applications.

The effect of high yttrium solute concentration on the twinning behaviour of magnesium alloys

The deformation behaviour of two single phase binary alloys, Mg-5Y and Mg-10Y, have been examined. In compression, two twin types were observed, the common {101¯2} twin as well as the less common {112¯1} extension twin. It is shown that the {112¯1} twin is much less sensitive to solute concentration than the {101¯2} twin, and it is suggested that the simple atomic shuffle of the {112¯1} twin reduces the solute strengthening imparted by Y additions. The common {101¯2} twin showed significant hardening as a result of alloying with Y. An analysis of solute behaviour has indicated that of the four chemical parameters investigated, i.e. atomic size, shear modulus, electronegativity and solute distribution, it appears to be the larger atomic radius of Y compared to Mg that increases the stress required to activate the {101¯2} twin. It is suggested that the large atomic radius inhibits the atomic shuffling process which accompanies the twinning shear in this twin type.

A potential anti-corrosive ionic liquid coating for MG alloy AZ31 in simulated body fluids

Magnesium alloys are attractive materials for biomedical applications, due to their excellent biocompatibility. However, these alloys show fast corrosion rates in the body that limits their clinical applications. Low-toxic ionic liquid (IL) trimethyl(butyl)phosphonium diphenyl phosphate P1444dpp has been investigated to provide corrosion protection for magnesium alloy AZ31 in simulated body fluids (SBFs). This work reports a preliminary exploration of the influence of different treatment temperatures on the corrosion protection properties of IL films for the magnesium alloy AZ31 in SBFs. Results show that the IL treatment at room temperature did not bring significant improvement in the corrosion performance of the AZ31 in SBF. However, when the treatment temperature was increased to 75°C, the IL treatment resulted in a substantial reduction of the corrosion, in particular the reduction of localized pitting corrosion. The influence of ionic liquid treatment on the corrosion performance of the magnesium alloys AZ31 in SBFs has been investigated by electrochemical impedance spectroscopy (EIS) tests and immersion tests.

Biocompatible magnesium alloys for hard tissue engineering

 Novel Mg-Zr-Sr and Mg-1Zr-2Sr-xDy/yHo alloys have recently been developed for use as biodegradable implant materials. These alloys are recommended to be promising biodegradable implant materials as they have enhanced corrosion resistance and excellent biocompatibility.

The competition between metastable and equilibrium S (Al2CuMg) phase during the decomposition of AlCuMg alloys

Abstract The decomposition sequence of the supersaturated solid solution leading to the formation of the equilibrium S (Al2CuMg) phase in AlCuMg alloys has long been the subject of ambiguity and debate. Recent high-resolution synchrotron powder diffraction experiments have shown that the decomposition sequence does involve a metastable variant of the S phase (denoted S1), which has lattice parameters that are distinctly different to those of the equilibrium S phase (denoted S2). In this paper, the difference between these two phases is resolved using high-resolution synchrotron and neutron powder diffraction and atom probe tomography, and the transformation from S1 to S2 is characterised in detail by in situ synchrotron powder diffraction. The results of these experiments confirm that there are no significant differences between the crystal structures of S1 and S2, however, the powder diffraction and atom probe measurements both indicate that the S1 phase forms with a slight deficiency in Cu. The in situ isothermal aging experiments show that S1 forms rapidly, reaching its maximum concentration in only a few minutes at high temperatures, while complete conversion to the S2 phase can take thousands of hours at low temperature. The kinetics of S phase precipitation have been quantitatively analysed for the first time and it is shown that S1 phase forms with an average activation energy of 75 kJ/mol, which is much lower than the activation energy for Cu and Mg diffusion in an Al matrix (136 kJ/mol and 131 kJ/mol, respectively). The mechanism of the replacement of S1 with the equilibrium S2 phase is discussed.

The role of back stress caused by precipitates on {101-2} twinning in a Mg-6Zn alloy

In the present study, the effect of precipitate characteristics on {101-2} extension twinning have been studied in a Z6 magnesium alloy. A strongly textured Z6 alloy plate was mechanically tested in twinning dominated orientation in solution treated and aged states. Optical microscopy, transmission electron microscopy (TEM) and visco-plastic self consistent (VPSC) modelling are used to examine the effect of precipitate characteristics on twinning. The yield stress was observed to increase by ~80. MPa during ageing and it was estimated that CRSS for twinning increased by ~29. MPa based on VPSC simulations. The increment of twin system strengthening can be attributed to back stress generated by elastically deforming particles.

Precipitation processes in Al-Cu-Mg-Sn and Al-Cu-Mg-Sn-Ag

Microalloying trace elements into aluminum alloys have been shown to improve mechanical properties by altering the precipitation process. Here, trace amounts of Sn and (Sn + Ag) have been added to Al-1.1Cu-1.7Mg (at.%) and the effects have been investigated by a combination of hardness testing and transmission electron microscopy (TEM). Hardness testing shows that the addition of Sn increases the hardness throughout the ageing process, and in combination with Ag, further increases the hardness and shortens the time to reach the peak hardness. The increase in hardness via Sn microalloying is attributed to the homogeneous distribution of S phase (Al2CuMg) precipitates. In the alloy microalloyed with both Sn and Ag, the microstructure is dominated by homogeneously distributed Ω phase (Al2Cu) precipitates in the peak strengthened condition. Given that neither spherical β-Sn precipitates, nor any other obvious nucleation sites for the Ω phase precipitates were observed using TEM, the mechanism for development of such homogeneous precipitation remains to be determined.

Enhancement of properties in cast Mg-Y-Zn rod processed by severe plastic deformation

Ternary Mg-Y-Zn alloys have attracted considerable attention from researchers due to their excellent mechanical properties and unique microstructures, particularly from the presence of long-period stacking-order (LPSO) phases. Microstructural variations and the resulting mechanical properties can be affected by various processing routes, particularly those involving severe plastic deformation of a cast billet. The approach used in this work was based on subjecting cast Mg92Y4Zn4 (composition in wt%) billet to severe plastic deformation by three different routes, namely equal channel angular pressing (ECAP), high pressure torsion (HPT) and ECAP followed by HPT, with the aim of refining the microstructure and improving mechanical properties. Samples processed by ECAP were annealed by post-processing and tested in compression and tension. The effect of the processing route and the process parameters on the microstructure and the hardness of the Mg-Y-Zn alloy is reported. An overall positive effect of annealing treatment on the mechanical properties of ECAP-processed alloy is demonstrated. © 2014 Elsevier B.V.

Structure and mechanical property variations in Mg-Gd-Y-Zn-Zr alloy depending on its composition and processing conditions

An effect of alloying element content on mechanical properties and precipitate formation in Mg-RE alloys was studied for Mg-8Gd-4Y- 1Zn-0.4Zr (wt%) and Mg-10Gd-5Y-1.8Zn-0.4Zr (wt%). It is shown that small variations in the alloying element concentration can be used to manipulate the alloy microstructure and precipitate formation towards eliminating the asymmetry (tension/compression) and anisotropy of yield stress.

Structural evolution of spark plasma sintered AlFeCuCrMgx (x = 0, 0.5, 1, 1.7) high entropy alloys

The present paper reports synthesis of novel AlFeCuCrMgx (x = 0, 0.5, 1, 1.7 mol) high entropy alloys (HEAs) by mechanical alloying (MA) followed by spark plasma sintering (SPS). Phase evolution, microstructure and phase transformation study of the sintered alloy were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). XRD of the sintered alloys revealed the formation of two BCC phases in the AlFeCuCr alloy and more complex structures in AlFeCuCrMgx (x = 0.5, 1, 1.7) alloys containing AlFe type, BCC, and Cu2Mg type phases. TEM bright field image and selected area diffraction pattern (SAED) revealed the formation of tetragonal closed packed Cr precipitates within the Cu2Mg phase of AlFeCuCrMgx alloys (x = 0.5, 1, 1.7). DSC study of the alloys revealed no substantial phase change up to 1000 °C for AlFeCuCr alloy. Although, for x = 0.5, 1 & 1.7 phase transformation occurs at 818 °C, 885 °C & 483 °C respectively. Mg content had a significant effect on hardness, increasing to a peak hardness of 853 HVN for AlFeCuCrMg0.5 alloy before decreasing to 533 HVN for the AlFeCuCrMg1.7 alloy. The phase evolution in these alloys has been considered using thermodynamic parameters, and the structure-property relationship has also been proposed by conventional strengthening mechanisms.