Effects of Si on microstructural evolution and mechanical properties of hot-rolled ferrite and bainite dual-phase steels

Based on the thermo-mechanical controlled process, the effects of Si on microstructural evolution, tensile properties, impact toughness, and stretch-flangeability of ferrite and bainite dual-phase (FBDP) steels were systematically investigated. The addition of Si from 0 to 0.95% promoted the formation of fine and equiaxed ferrite grains, and high Si (0.95%) also resulted in the formation of blocky martensite islands and retained austenite. Yield and tensile strengths, and uniform and total elongations all increased with increasing Si content. Therefore, the tensile strength and ductility balance was improved by Si addition due to the increasing strain-hardening rate. The fractured morphologies after hole-expansion showed that the excellent stretch-flangeability of FBDP steels was associated with the micro-cracks propagating through in ferrite phase as well as the elongated ferrite grains along the direction perpendicular to the crack. 0.95% Si steel had a similar high combination of tensile strength and impact toughness to 0.55% Si steel, and especially 0.95% Si steel exhibited an excellent combination of tensile strength and stretch-flangeability.

A uniaxial tensile stage with tracking capabilities for micro X-ray diffraction applications

First results are presented for a uniaxial tensile stage designed to operate on a scanning micro X-ray diffraction synchrotron beamline. The new tensile stage allows experiments at typical loading cycles used in standard engineering stress–strain tests. Several key features have been implemented to support in situ loading experiments at the intragranular length scale. The physical size and weight of the load cell were minimized to maintain the correct working distance for the X-ray focusing optics and to avoid overloading the high-resolution raster scan translation stages. A high-magnification optical microscope and image correlation code were implemented to enable automated online tracking capabilities during macroscopic elongation of the sample. Preliminary in situ tensile loading experiments conducted on beamline 12.3.2 at the Advanced Light Source using a polycrystalline commercial-purity Ti test piece showed that the elastic–plastic response of individual grains could be measured with submicrometre spatial resolution. The experiments highlight the unique instrumentation capabilities of the tensile stage for direct measurement of deviatoric strain and observation of dislocation patterning on an intragranular length scale as a function of applied load.

Effect of tensile pre-strain on bending and unloading of automotive steels

In recent years, advanced high strength steels (AHSS) have been used in a wide range of automotive applications; they may have property variations through the thickness and the properties may also be dependent of prior processing including pre-straining. In order to model forming processes precisely using, for example, finite element analysis, it is important that material input data should adequately reflect these effects. It is known that shape defects in roll forming are related to small strains in material that has undergone prior deformation in a different strain path. Much research has already been performed on the change in the Young’s Modulus once a steel sheet has been plastically deformed,however many of these tests have only been conducted using tensile testing, and therefore may not take into account differences in compressive and tensile unloading. This research investigates the effect of tensile pre-straining on bending behaviour for various types of material;in bending, one half of the sheet will load and unload in compression and hence experience deformation under a reversed stress. Four different materials were pre-strained in tension with 1%, 3%, 7%, 11% and 25% elongation. Using a free bending test, moment curvature diagrams were obtained for bending and unloading. The results showed that the characteristics of the moment curvature diagram depended on the degree of pre-straining; more highly strained samples showed an earlier elastic-plastic transformation and a decreased Young's Modulus during unloading. This was compared to previous literature results using only tensile tests. Our results could influence the modeling of springback in low tension sheet operations, such as roll forming.

Asymmetric rolling of interstitial-free steel using differential roll diameters. Part II : microstructure and annealing effects

The effects of annealing on the microstructure, texture, tensile properties, and R value evolution of an IF steel sheet after room-temperature symmetric and asymmetric rolling were examined. Simulations were carried out to obtain R values from the experimental textures using the viscoplastic self-consistent polycrystal plasticity model. The investigation revealed the variations in the textures due to annealing and symmetric/asymmetric rolling and showed that the R values correlate strongly with the evolution of the texture. An optimum heat treatment for the balance of strength, ductility, and deep drawability was found to be at 873 K (600 _C) for 30 minutes.

Surface wrinkling of the twinning induced plasticity steel during the tensile and torsion tests

'Heterogeneous twinning' is defined as plastic deformation due to the formation and progress of twins resulting in surface wrinkles on the deforming part when the initial grain size is relatively large compared to the typical size of the part. In the case of a Twinning Induced Plasticity (TWIP) steel with an initial grain size of ~160. m, the heterogeneous twinning generated visible wrinkles, an orange peel effect, under medium uni-axial strains. The heterogeneous twinning did not occur in the material subjected to high shear strains. The complications resulting from this phenomenon on strain hardening characterization of the TWIP steels using two commonly used mechanical tests, tensile and torsion are discussed along with some experimental aspects of heterogeneous twinning. © 2014.

Effect of temperature on mechanical behaviour of high manganese TWIP steel

The aim of the present study was to investigate the role of deformation temperature on the active deformation mechanisms in a 0.6C-18Mn-1.5Al (wt%) TWIP steel. The tensile testing was performed at different temperatures, ranging from ambient to 400°C at a constant strain rate of 10-3 S-1. The microstructure characterization was carried out using a scanning electron microscopy. The deformation temperature revealed a significant effect on the active deformation mechanisms (i.e. slip versus twinning), resulting in different microstructure evolution and mechanical properties. At the room temperature, the mechanical twinning was the dominant deformation mechanism, enhancing both the strength and ductility. Dynamic strain aging (DSA) effect was observed at different deformation temperatures, though it was more pronounced at higher temperatures. The volume fraction of deformation twins significantly reduced with an increase in the deformation temperature, deteriorating the mechanical behavior. There was a transition temperature (~300°C), above which the mechanical twinning was hardly observed in the microstructure even at fracture, resulting in low ductility and strength. The current observation can be explained through the change in the stacking fault energy with the deformation temperature. © (2014) Trans Tech Publications, Switzerland.