The effect of Nb, Mo, and A1 additions on the transformation behaviour and mechanical properties of thermomechanically processed C-Si-Mn trip steel

The effect of additions of Nb, A1 and Mo to Fe-C-Mn-Si TRIP steels on the final microstructure and mechanical properties after simulated thermomechanical processing (TMP) has been studied. Laboratory simulations of continuous cooling during TMP were performed using a quench deformation dilatometer, while laboratory simulations of discontinuous cooling during TMP were performed using a hot rolling mill. From this a comprehensive understanding of the structural and kinetic aspects of the bainite transformation in these types of TRIP steels has been developed. All samples were characterised using optical microscopy and XRD. The relationships between the morphology of bainitic structure, volume fraction, stability of RA and mechanical properties were investigated.

The production of ultrafine ferrite in low-carbon steel by strain-Induced transformation

An investigation into the production of ultrafine (1 µm) equiaxed ferrite (UFF) grains in low-carbon steel was made using laboratory rolling, compression dilatometry, and hot torsion techniques. It was found that the hot rolling of thin strip, with a combination of high shear strain and high undercooling, provided the conditions most suitable for the formation of this type of microstructure. Although high strains could be applied in compression and torsion experiments, large volume fractions of UFF were not observed in those samples, possibly due to the lower level of undercooling achieved. It is thought that ferrite refinement was due to a strain-induced transformation process, and that ferrite grains nucleated on parallel and linear deformation bands that traversed austenite grains. These bands formed during the deformation process, and the undercooling provided by the contact between the strip and the work rolls was sufficient to drive the transformation to homogeneous UFF grains.

Numerical investigation of austenite grain size distribution in square-diamond pass hot bar rolling

In this study, the austenite grain size (AGS) for hot bar rolling of AISI4135 steel was predicted based on two different AGS evolution models available in the literature. In order to predict the AGS more accurately, both models were integrated with a three-dimensional non-isothermal finite element program by implementing a modified additivity rule. The predicted results based on two models for the square-diamond (S-D) and round-oval (R-O) pass bar rolling processes were compared with the experimental data available in the literature. Then, numerical predictions depending on various process parameters such as interpass time, temperature, and roll speed were made to compare both models and investigate the effect of these parameters on the AGS distributions. Such numerical results were found to be beneficial to understand the effect of the microstructure evolution model on the rolling processes better and control the processes more accurately.

Effect of process variables on formation of dynamic strain induced ultrafine ferrite during hot torsion testing

Ultrafine grain sizes were produced using hot torsion testing of a 0.11C-1.68Mn-0.20Si (wt-%) steel, with ultrafine ferrite (<1 µm) nucleating intragranularly during testing by dynamic strain induced transformation. A systematic study was made of the effect of isothermal deformation temperature, strain level, strain rate, and accelerated cooling during deformation on the formation of ultrafine ferrite by this process. Decreasing the isothermal testing temperature below the Ae₃ temperature led to a greater driving force for ferrite nucleation and thus more extensive nucleation during testing; the formation of Widmanstätten ferrite prior to, or early during, deformation imposed a lower temperature limit. Increasing the strain above that where ferrite first began 0.8 at 675C and a strain rate of 3 s¯¹ increased the intragranular nucleation of ferrite. Strain rate appeared to have little effect on the amount of ferrite formed. However, slower strain rates led to extensive polygonisation of the ferrite formed because more time was available for ferrite recovery. Accelerated cooling during deformation followed by air cooling to room temperature led to a uniform microstructure consisting of very fine ferrite grains and fine spherical carbides located in the grain boundaries regions. Air cooling after isothermal testing led to carbide bands and a larger ferrite grain size.

Conversion of the hot torsion test results into flow curve with multiple regimes of hardening

The method of Fields and Backofen has been commonly used to reduce the data obtained by hot torsion test into flow curves. The method, however, is most suitable for materials with monotonic strain hardening behaviour. Other methods such as Stüwe’s method, tubular specimens, differential testing and the inverse method, each suffer from similar drawbacks. It is shown in the current work that for materials with multiple regimes of hardening any method based on an assumption of constant hardening indices introduces some errors into the flow curve obtained from the hot torsion test. Therefore such methods do not enable accurate prediction of onset of recrystallisation where slow softening occurs. A new method to convert results from the hot torsion test into flow curves by taking into account the variation of constitutive parameters during deformation is presented. The method represents the torque twist data by a parametric linear least square model in which Euler and hyperbolic coefficients are used as the parameters. A closed form relationship obtained from the mathematical representation of the data is employed next for flow stress determination. Two different solution strategies, the method of normal equations and singular value decomposition, were used for parametric modelling of the data with hyperbolic basis functions. The performance of both methods is compared. Experimental data obtained by FHTTM, a flexible hot torsion test machine developed at IROST, for a C–Mn austenitic steel was used to demonstrate the method. The results were compared with those obtained using constant strain and strain rate hardening characteristics.

Characterization on ferrite microstructure evolution during large strain warm torsion testing of plain low carbon steel

Ferrite grain/subgrain structures evolution during the extended dynamic softening of a plain low carbon steel was investigated throughout the large strain warm deformation by hot torsion. Microstructural analysis with electron back-scattering diffraction (EBSD) scanning electron microscope (FEG/SEM) was carried out on the ferrite microstructural parameters. The results showed that the warm flow stress–strain curves are similar to those affected only by dynamic softening and an extended warm flow softening is seen during large strain deformation up to 30. Furthermore, with an increase in strain up to ~ vert, similar1 the grain size of ferrite, misorientation angle and fraction of high-angle boundaries gradually decrease and fraction of low-angle boundaries increases. With a further increase in the strain beyond ~, vert, similar2, these parameters remain approximately unchanged. No evidence of discontinuous dynamic recrystallisation involving nucleation and growth of new grains was found within ferrite. Therefore, the dynamic softening mechanism observed during large strain ferritic deformation is explained by continuous dynamic recrystallization (CDRX).

Correlation between the deformation and post-deformation softening behaviours in hot worked Austenite

The relation between the deformation and post-deformation softening behaviours of austenite is examined in a 304 stainless steel. This correlation has been exploited in the modelling of hot rolling and it is argued here that the key to this understanding lies in the deformation structure. The latter is characterized in the present work by the fraction of dynamic recrystallization. The value of this fraction at the peak in the flow stress curve is found to decrease with increasing stress (i.e. with decreasing temperature and increasing strain rate). By contrast, the fraction of dynamic  recrystallization at the strain corresponding to the point where  post-deformation softening becomes strain independent is found to be constant. These observations are used to explain the nature of the important difference between the flow curve peak and the onset of strain independent post-deformation softening.

Effect of grain size on deformation twinning behaviour of high MN steel

The effect of grain size on the mechanical properties and deformation twinning behaviour in high manganese steel was investigated. In order to generate different grain sizes, the samples were subjected to hot rolling, cold rolling and annealing. Room temperature tensile testing of the steel with different grain sizes (5-50 µm) indicated the occurrence of twinning induced plasticity (TWIP) in all the samples. Also, changes in work-hardening behaviour accompanied changes in the grain size. The results are discussed in terms of the enhanced sensitivity of twinning to the grain size.

Electron back scattered diffraction (EBSD) characterization of warm rolled and accumulative roll bonding (ARB) processed ferrite

An interstitial free (IF) steel was severely deformed using accumulative roll bonding (ARB) process and warm rolling. The maximum equivalent strains for ARB and warm rolling were 4.8 and 4.0, respectively. The microstructure and micro-texture were studied using optical microscopy and scanning electron microscopy equipped with electron back scattered diffraction (EBSD). The grain size and misorientation obtained by both methods are in the same range. The microstructure in the ARB samples after 6 cycles is homogeneous, although a grain size gradient is observed at the layers close to the surface. The through thickness texture gradient in the ARB samples is different from the warm rolled samples. While a shear texture (⟨110⟩//rolling plane normal direction (ND)) at the surface and rolling texture at the center region is developed in the ARB  samples, the overall texture is weak. The warm rolled samples display a sharp rolling texture through the thickness with increasing the sharpness toward the center. These differences are attributed to the fact that the central region of ARB strip is comprised of material that was once at the surface. The ARB process  can suppress the formation of shear bands which are conventional at warm rolled IF steels. EBSD study on the sample with 6th cycle of ARB following the annealing at 750 ◦C verified a texture gradient through the thickness of the sheet. The shear orientations at the surface and at the quarter thickness layers can be identified even after annealing. The overall weak texture and existence of shear orientations make ARB processed samples unfavorable for sheet metal forming in compare with warm rolled samples.

Softening mechanisms in two duplex stainless steels deformed in hot torsion

The aim of the present work was to undertake a detailed investigation of the softening mechanisms during hot deformation of a 21Cr-10Ni-3Mo (steel A) and a 21Cr-8Ni-3Mo (steel B) austenite/ferrite duplex stainless steels containing about 60% and 30% of austenite, respectively. The steels were subjected to hot deformation in torsion performed at 900 ºC and 1200 ºC using a strain rate of 0.7 s-1 to several strain levels. Quantitative optical and transmission electron microscopy were used in the investigation. Austenite was observed to soften via dynamic recovery (DRV) and dynamic recrystallisation (DRX) accompanied by DRV for the deformation temperatures of 900 °C and 1200 °C, respectively, for the both steels studied. DRX of austenite largely occurred through strain-induced grain boundary migration, complemented by (multiple) twinning, and developed significantly faster in steel A than in steel B, indicating that considerably larger strains partitioned into austenite in the former steel during deformation at 1200 °C. The above softening mechanism was accompanied by the formation of DRX grains from subgrains along the austenite/ferrite interface and by large-scale subgrain coalescence. At 900°C, stressassisted phase transitions between austenite and ferrite were observed, characterised by dissolution of the primary austenite, formation of Widmanstätten secondary austenite and gradual globularisation of the microstructure with increasing strain. These processes appeared to be significantly more widespread in steel B. The softening mechanism within ferrite for the both steels studied was classified as “continuous DRX”, characterised by a gradual increase in misorientations between neighbouring subgrains with strain, for the both deformation temperatures.

Fine structure of shear bands formed during hot deformation of two austenitic steels

Shear bands formed during both cold and hot plastic deformation have been linked with several proposed mechanisms for the formation of ultrafine grains. The aim of the present work was to undertake a detailed investigation of the microstructural and crystallographic characteristics of the shear bands formed during hot deformation of a 22Cr-19Ni-3Mo (mass%) austenitic stainless steel and a Fe-30 mass%Ni based austenitic model alloy. These alloys were subjected to deformation in torsion and plane strain compression (PSC), respectively, at temperatures of 900°C and 950°C and strain rates of 0.7s_-1 and 10s_-1, respectively. Transmission electron microscopy and electron backscatter diffraction in conjunction with scanning electron microscopy were employed in the investigation. It has been observed that shear bands already started to form at moderate strains in a matrix of pre-existing microbands and were composed of fine, slightly elongated subgrains (fragments). These bands propagated along a similar macroscopic path and the subgrains, present within their substructure, were rotated relative to the surrounding matrix about axes approximately parallel to the sample radial and transverse directions for deformation in torsion and PSC, respectively. The subgrain boundaries were largely observed to be non-crystallographic, suggesting that the subgrains generally formed via multiple slip processes. Shear bands appeared to form through a co-operative nucleation of originally isolated subgrains that gradually interconnected with the others to form long, thin bands that subsequently thickened via the formation of new subgrains. The observed small dimensions of the subgrains present within shear bands and their large misorientations clearly indicate that these subgrains can serve as potent nucleation sites for the formation of ultrafine grain structures during both subsequent recrystallisation, as observed during the present PSC experiments, and phase transformation.

Evolution of recrystallization during and following hot deformation

Recrystallization of austenite during and following hot deformation has been studied in detail in a type 304 austenitic stainless steel. Furthermore, the effect of second phase on the softening process of austenite has been investigated using a 2205 duplex stainless steel. The mechanical and microstructural features have been compared for dynamic and post deformation recrystallization.

Mechanical properties and blow forming of rolled AZ31 Mg alloy sheet

Rolling was conducted at 373-673 K for AZ31 Mg alloy; mechanical properties of the rolled Mg alloy were investigated by tensile and blow forming tests. The grain sizes of all the rolled specimens were smaller than that of the specimen prior to rolling. At tensile temperatures under 373 K, the rolled specimens showed much higher 0.2% proof stresses than the non-rolled specimens due to their fine-grained microstructure. However, the strength of the rolled specimens decreased significantly at 473 K. Superplastic behavior was obtained at 573-723 K for the specimens rolled at 498 K. Blow forming tests demonstrated that specimens rolled at 498 K exhibited a high degree of formability at 723 K.

Microstructure evolution modeling during and after deformation in 304 austenitic stainless steel through cellular automaton approach

A 2D cellular automation approach was used to simulate microstructure evolution during and after hot deformation. Initial properties of the microstructure and dislocation density were used as input data to the cellular automation model. The flow curve and final grain size were the output data for the dynamic recrystallization simulation, and softening kinetics curves were the output data of static and metadynamic recrystallization simulations. The model proposed in this work considered the effect of thermomechanical parameters (e.g., temperature and strain rate) on the nucleation and growth kinetics during dynamic recrystallization. The dynamic recrystallized microstructures at different strains, temperatures, and strain rates were used as input data for static and metadynamic recrystallization simulations. It was shown that the cellular automation approach can model the final microstructure and flow curve successfully in dynamic recrystallization conditions. The postdeformation simulation results showed that the time for 50% recrystallization decreases with increasing strain for a given initial grain size and that dynamic recrystallization slows the postdeformation recrystallization kinetics compared to a model without dynamic recrystallization.

Microscale modelling of AISI 304 behaviour during hot deformation

This project aimed to model the microstructure evolution during and following hot deformation using a cellular automaton approach. The flow curves, softening kinetics and final microstructures were used as the input data for the post-deformation simulation to elucidate the effect of dynamic recrystallization on the post-deformation softening.