Impact of grain microstructure on the heterogeneity of precipitation strengthening in an Al-Li-Cu alloy

The effect of grain microstructure on the age-hardening behavior is investigated on recrystallized and un-recrystallized Al-Cu-Li alloys by combining electron-backscatter-diffraction and micro-hardness mapping. The spatial heterogeneity of micro-hardness is found to be strongly dependent on the grain microstructure. Controlled experiments are carried out to change the pre-strain before artificial ageing. These experiments lead to an evaluation of the range of local strain induced by pre-stretching as a function of the grain microstructure and results in heterogeneous formation of the hardening T1 precipitates.

Anisotropic behavior in plasticity and ductile fracture of an aluminum alloy

Anisotropic mechanical behavior is investigated for an aluminum alloy of 6K21-IH T4 both in plastic deformation and ductile fracture. Anisotropic plastic deformation is characterized by uniaxial tensile tests of dog-bone specimens, while anisotropy in ductile fracture is illustrated with specimens with a central hole, notched specimens and shear specimens. All these specimens are cut off at every 15º from the rolling direction. The r-values and uniaxial tensile yield stresses are measured from the tensile tests of dog-bone specimens. Then the anisotropic plasticity is modeled by a newly proposed J2-J3 criterion under non-associate flow rule (non-AFR). The testing processes of specimens for ductile fracture analysis are simulated to extract the maximum plastic strain at fracture strokes as well as the evolution of the stress triaxiality and the Lode parameter in different testing directions. The measured fracture behavior is described by a shear-controlled ductile fracture criterion proposed by Lou et al. (2014. Modeling of shear ductile fracture considering a changeable cut-off value for stress triaxiality. Int. J. Plasticity 54, 56-80) for different loading directions. It is demonstrated that the anisotropic plastic deformation is described by the J2-J3 criterion with high accuracy in various loading conditions including shear, uniaxial tension and plane strain tension. Moreover, the anisotropy in ductile fracture is not negligible and cannot be modeled by isotropic ductile fracture criteria. Thus, an anisotropic model must be proposed to accurately illustrate the directionality in ductile fracture.

The evolution of microbands and their interaction with NbC precipitates during hot deformation of a Fe-30Ni-Nb model austenitic steel

The present work has investigated the evolution of microbands (MBs) and their interaction with strain-induced NbC precipitates during uniaxial compression of a model austenitic Fe-30Ni-Nb steel at 925 °C. The (1 1 0) fibre grains, both without and with copious amounts of precipitates, contained up to large strains crystallographic MBs aligned close to the highly stressed {1 1 1} slip planes having large Schmid factors. The MBs thus maintained their crystallographic character during straining, through continuously rearranging themselves, and did not follow the macroscopically imposed rigid body rotation. During double-pass deformation, fine NbC particles formed at short inter-pass holding remained strongly pinned at small reloading strains and appeared to be dragged by rearranging MB walls. With increasing reloading strain, the fine precipitates became progressively released from the above walls. During reloading after increased holding time, the coarsened particles tended with their increased size to become increasingly detached from the MB walls already at a small strain. The precipitate-free MB wall segments rearranged during straining to maintain their crystallographic alignment, while the detached precipitates followed the sample shape change and rotated towards the compression plane. The MB wall rearrangement generally occurred through cooperative migration of the corresponding dislocation networks.

β-Ti grain refinement via α-Precipitation

The present work explores the impact of α precipitates on β recrystallization following hot deformation of Ti-5Al-5Mo-5V-3Cr with grains larger than 1 mm. A single hot rolling pass of 36 pct reduction was conducted on an aged microstructure containing α precipitates at a temperature well below the β transus temperature. After annealing, a uniformly recrystallized structure with a grain size of ~100 µm is formed. The prior β grain boundaries can be readily identified and it is seen that the primary β grains have been replaced by grains displaying a spread of correlated misorientation angles extending up to the highest allowable values. The annealing comprises two stages. The first stage involves normal β subgrain growth limited by the Zener pinning force of the unstable α precipitates. The second stage corresponds to the onset of β recrystallization at the point where the Zener pinning force drops due to dissolution of the α precipitates. This leads to a uniform distribution of site saturated recrystallization nuclei.