Texture selection mechanisms in uniaxially extruded magnesium alloys

Extrusion textures in magnesium alloys are of high interest due to their influence on yield asymmetry. This data supports work describing three mechanisms of texture selection that may play a role during extrusion. These mechanisms involve localized differences in deformation at the grain level, the change in local environment experienced by grain boundary bulges and shear banding. The work employs visco-plastic crystal plasticity and electron backscattering diffraction.

Deformation of magnesium alloys during laboratory scale in-situ x-ray diffraction

In this research work we developed a new laboratory based transmission X-ray diffraction technique to perform in-situ deformation studies on a far more regular basis that is not possible at large scale synchrotron and neutron facilities. We studied the deformation mechanisms in light weight magnesium alloys during in-situ tensile testing.

The effect of high yttrium solute concentration on the twinning behaviour of magnesium alloys

The deformation behaviour of two single phase binary alloys, Mg-5Y and Mg-10Y, have been examined. In compression, two twin types were observed, the common {101¯2} twin as well as the less common {112¯1} extension twin. It is shown that the {112¯1} twin is much less sensitive to solute concentration than the {101¯2} twin, and it is suggested that the simple atomic shuffle of the {112¯1} twin reduces the solute strengthening imparted by Y additions. The common {101¯2} twin showed significant hardening as a result of alloying with Y. An analysis of solute behaviour has indicated that of the four chemical parameters investigated, i.e. atomic size, shear modulus, electronegativity and solute distribution, it appears to be the larger atomic radius of Y compared to Mg that increases the stress required to activate the {101¯2} twin. It is suggested that the large atomic radius inhibits the atomic shuffling process which accompanies the twinning shear in this twin type.

Biocompatible magnesium alloys for hard tissue engineering

 Novel Mg-Zr-Sr and Mg-1Zr-2Sr-xDy/yHo alloys have recently been developed for use as biodegradable implant materials. These alloys are recommended to be promising biodegradable implant materials as they have enhanced corrosion resistance and excellent biocompatibility.

Advances in wrought magnesium alloys: Fundamentals of processing, properties and applications

This important book summarises the wealth of recent research on our understanding of process-property relationships in wrought magnesium alloys and the way this understanding can be used to develop a new generation of alloys for high-performance applications. After an introductory overview of current developments in wrought magnesium alloys, part one reviews fundamental aspects of deformation behaviour. These chapters are the building blocks for the optimisation of processing steps covered in part two, which discusses casting, extrusion, rolling and forging technologies. The concluding chapters cover applications of wrought magnesium alloys in automotive and biomedical engineering. With its distinguished editors, and drawing on the work of leading experts in the field, Advances in wrought magnesium alloys is a standard reference for those researching, manufacturing and using these alloys.

Theoretical study on the (1-012) deformation twinning and cracking in coarse-grained magnesium alloys

This paper theoretically and systematically investigates: (1) the effect of local transformed strains within deformation twinning on twin intersection; (2) the fracture mode based on type I co-zone tensile twin intersection in coarse-grained magnesium alloys, as well as the impacts of twin intersection and grain diameter on interfacial crack nucleation along twin boundaries; and (3) the influence of the local stresses arising from the encountered twin bands on crack growth. A novel dislocation-based strain nucleus model and a Green's function method, which are applicable to any material with local transformations in which elastic properties are reasonably approximated as isotropic, are specifically employed to model the concentrated transformed strain and calculate the local stress field resulting from deformation twinning and the stress intensity factors at crack tips in the magnesium alloys, respectively. In addition, an electron backscatter diffraction (EBSD) measurement is provided for crack nucleation originating from Type I co-zone tensile twin intersection. The theoretical modeling indicates: (i) the local strains within barrier twins strongly dictate the growth of incident twins and enhance the twin propagation stress; (ii) larger grains favor brittle fracture. More specifically, the dislocation reactions and pile-ups at the junctions between tensile twins can result in interfacial crack nucleation and growth along the twin boundaries, which is a brittle fracture mode based on lower twinning stress and stress concentration in the coarse-grained magnesium alloys; and (iii) the direction of crack propagation is easily changed by high-density twin bands and twin intersections owing to the local strains.

Hot working microstructure map for magnesium AZ31

A thermomechanical processing (TMP) structure map is proposed that plots the critical strains required for dynamic recrystallization along with the grain sizes that result. These maps are useful in identifying the limits to grain refinement and designing hot working processes. They are readily constructed for well studied alloys such as plain carbon steel. In light of the recent interest in the hot working of magnesium, initial steps are taken here to construct a TMP structure map for the most common wrought magnesium alloy, AZ31. The completion of dynamic recrystallization is estimated using a geometrical approach and a twinning region is identified.

Determination of lower-bound ductility for AZ31 magnesium alloy by use of the bulge specimens

Despite the high demand for industrial applications of magnesium, the forming technology for wrought magnesium alloys is not fully developed due to the limited ductility and high sensitivity to the processing parameters. The processing window for magnesium alloys could be significantly widened if the lower-bound ductility (LBD) for a range of stresses, temperature, and strain rates was known. LBD is the critical strain at the moment of fracture as a function of stress state and temperature. Measurements of LBD are normally performed by testing in a hyperbaric chamber, which is highly specialized, complex, and rare equipment. In this paper an alternative approach to determine LBD is demonstrated using wrought magnesium alloy AZ31 as an example. A series of compression tests of bulge specimens combined with finite element simulation of the tests were performed. The LBD diagram was then deduced by backward calculation.

Grain size in Mg alloys: recrystallization and mechanical consequences

The present paper examines the development of grain size during the recrystallization of magnesium alloys and the influence the grain size has on the mechanical response. In magnesium alloys grain refinement improves the strength-ductility balance. This simultaneous increase in both strength and ductility is ascribed to the impact the grain size has on deformation twinning. The mechanisms by which the grain size is established during hot working are shown to be conventional dynamic recrystallization followed by post-dynamic recrystallization. The role of alloying additionon both of these reactions is briefly considered.

Effect of solidification grain refinement on the development of wrought Mg alloys

A recent trial investigated the effect of solidification grain refinement of billet on the grain refinement and properties of alloy ZM20. It was found that even at levels of 0.4Mn, significant grain refinement could be obtained when 0.7Zr was added. At 0.2Mn grain sizes as low as 60μm were
obtained. Billets of Mg-2Zn-0.2Mn with four different grain sizes, due to different Zr and cooling rates were then cast via vertical direct chill casting and extruded conventionally. Benefits of grain refinement of the billet on extrusion were found to be a slight increase in the size of the operating
window, and a reduction of the grain size in the extrudate. However, the effect of the reduction in extrudate grain size due to refinement of the billet was small compared with the amount of grain refinement obtained due to recrystallisation on extrusion.

Construction of extrusion limit diagram for AZ31 magnesium alloy by FE simulation

The maximum speed at which magnesium can be extruded is considerably slower than that of many common aluminium extrusion alloys. This affects both the economies of production and the final mechanical behaviour. The present work quantifies the limiting extrusion speeds and ratios of magnesium alloy AZ31 as a function of billet temperature. This is done by combining hot compression test results, FE simulations and extrusion trials. Hot working stress–strain curves displayed a distinct dynamic recrystallisation peak. These data were used as a “look-up” table for the FE simulations in which the cracking limit was assumed to occur when the surface temperature reaches the incipient melting point. The maximum extrusion ratio predicted using FE analysis dropped from 90 to 40 when the extrusion ram speed was raised from 5 to 50 mm/s. The predicted limits agree well with the occurrence of cracking in both a laboratory and a commercial extrusion trial.

Effect of composition on the texture and deformation behaviour of wrought Mg alloys

The microstructure and mechanical response of three extruded magnesium alloys, Mg-3Al-1Zn (AZ31), Mg-1.5Mn (Ml) and Mg-lMn-0.4RE (ME10) are examined. The tensile yield strength of ME10 was nearly half that of AZ31 and Ml. The tensile elongations were 6%, 11% and 19% for Ml, AZ31 and ME10, respectively. This range of properties is large and is attributed to the unique extrusion texture produced in ME10, and the high density of fine particles in Ml.

Microstructure evolution in hot worked and Annealed Magnesium Alloy AZ31

The present work examines the microstructure that evolves during the annealing of hot worked magnesium alloy AZ31. First, the influences of deformation and annealing conditions on the microstructures are assessed. It is found that the annealing behaviour is consistent with what one would expect for a recrystallization type reaction. Whilst both the deformation and annealing conditions influence the time required to reach a stable annealed microstructure, the grain size attained is governed solely by the prior deformation conditions employed. At the highest temperature and strain rate examined, the rate of recrystallization is quite high and the grain size was found to be approximately double when annealed for only 1 s prior to quenching. Finally, semi-empirical equations are developed to predict the kinetics of recrystallization, as well as the evolution of grain size, during annealing.

The origin of "Rare Earth" texture development in extruded Mg-based alloys and its effect on tensile ductility

The extrusion behaviour, texture and tensile ductility of five binary Mg-based alloys have been examined and compared to pure Mg. The five alloying additions examined were Al, Sn, Ca, La and Gd. When these alloys are compared at equivalent grain size, the La- and Gd-containing alloys show the best ductilities. This has been attributed to a weaker extrusion texture. These two alloying additions, La and Gd, were found to also produce a new texture peak with View the MathML source parallel to the extrusion direction. This “rare earth texture” component was found to be suppressed at high extrusion temperatures. It is proposed that the View the MathML source texture component arises from oriented nucleation at shear bands.