Effect of twinning on microstructural evolution during dynamic recrystallisation of hot deformed as-cast austenitic stainless steel

An as-cast austenitic stainless steel was hot deformed at 1173 K, 1223 K, and 1373 K (900 °C, 950 °C, and 1100 °C) to a strain of 1 with a strain rate of 0.5 or 5 s⁻¹. The recrystallised fraction is observed to be dependent on dynamic recrystallisation (DRX). DRX grains nucleated at the initial stages of recrystallization have similar orientation to that of the deformed grains. With increasing deformation, Cube texture dominates, mainly due to multiple twinning and grain rotation during deformation.

Protocol for the Hall Technique study: A trial to measure clinical effectiveness and cost-effectiveness of stainless steel crowns for dental caries restoration in primary molars in young children

BACKGROUND: The Hall Technique (HT) is a carious primary molar treatment that does not require local analgesia, carious tissue removal or tooth preparation. The carious lesions in carefully selected teeth are sealed with a stainless steel crown (preformed metal crown). The study aims are to determine the clinical effectiveness, acceptability and cost-effectiveness of the HT for management of carious lesions in young dental patients. METHODS/DESIGN: Children, aged 3-7years, with a primary molar tooth with a carious lesion extending no further than the middle third of dentine, with no signs or symptoms of pulp inflammation or infection, and attending one of three community agencies are recruited. Target sample size is 220. A control tooth with an intra-coronal restoration is sourced from the same mouth. The primary outcome is the period of time free from further treatment. The assessments are scheduled at 6, 12 and 24months. In addition to the clinical assessment, acceptability of the HT will be assessed via questionnaires among patients and their primary carers at baseline, 6, 12 and 24months. Cost-outcome description and cost-effectiveness analysis from healthcare provider and societal perspective will be conducted. DISCUSSION: The clinical effectiveness, acceptability and cost-effectiveness of the HT in the community dental setting will be evaluated. The results of this study will determine the implementation of HT in the management of dental caries in young children.

Microstructure and hardness characterisation of laser coatings produced with a mixture of AISI 420 stainless steel and Fe-C-Cr-Nb-B-Mo steel alloy powders

Fe-C-Cr-Nb-B-Mo alloy powder and AISI 420 SS powder are deposited using laser cladding to increase the hardness for wear resistant applications. Mixtures from 0 to 100 wt.% were evaluated to understand the effect on the elemental composition, microstructure, phases, and microhardness. The mixture of carbon, boron and niobium in the Fe-C-Cr-Nb-B-Mo alloy powder introduces complex carbides into a Fe-based matrix of AISI 420 SS which increases its hardness. Hardness increased linearly with increasing Fe-C-Cr-Nb-B-Mo alloy, but substantial micro-cracking was observed in the clad layer at additions of 60 wt.% and above; related to a transition from a hypoeutectic alloy containing α-Fe/α' dendrites with an (Fe,Cr)2B and γ-Fe eutectic to primary and continuous carbo-borides M2B (where M represents Fe and Cr) and M23(B,C)6 carbides (where M represents Fe, Cr, Mo) with MC particles (where M represents Nb and Mo). The highest average hardness, for an alloy without micro-cracking, of 952 HV was observed in a 40 wt.% alloy. High stress abrasive scratch testing was conducted on all alloys at various loads (500, 1500, 2500 N). Alloy content was found to have a strong effect on the wear mode and the abrasive wear rate, and the presence of micro-cracks was detrimental to abrasive wear resistance.

Microstructural and surface texture analysis due to machining in Super Austenitic Stainless Steel

Inferior surface quality is a significant problem faced by machinist. The purpose of this study is to present a surface texture analysis undertaken as part of machinability assessment of Super Austenitic Stainless Steel alloy-AL6XN. The surface texture analysis includes measuring the surface roughness and investigating the microstructural behaviour of the machined surfaces. Eight milling trials were conducted using combination of cutting parameters under wet machining. An optical profilometer (non-contact), was used to evaluate the surface texture at three positions. The surface texture was represented using the parameter, average surface roughness. Scanning Electron Microscope was utilised to inspect the machined surface microstructure and co relate with the surface roughness results. Results showed that maximum roughness values recorded at the three positions in the longitudinal direction (perpendicular to the machining grooves) were 1.21 μm (trial 1), 1.63 μm (trial 6) and 1.68 μm (trial 7) respectively whereas the roughness values were greatly reduced in the lateral direction. Also, results showed that the feed rate parameter significantly influences the roughness values compared to the other cutting parameters. The microstructure of the machined surfaces was distorted by the existence of cracks, deformed edges and bands and wear deposition due to machining process.

Impacts of wear and geometry response of the cutting tool on machinability of super austenitic stainless steel

This paper presents a study of tool wear and geometry response whenmachinability tests were applied under milling operations onthe Super Austenitic Stainless Steel alloy AL-6XN. Eight milling trials were executed under two cutting speeds, two feed rates, andtwo depths of cuts. Cutting edge profile measurements were performed to reveal response of cutting edge geometry to the cuttingparameters and wear. A scanning electron microscope (SEM) was used to inspect the cutting edges. Results showed the presenceof various types of wear such as adhesion wear and abrasion wear on the tool rake and flank faces. Adhesion wear represents theformation of the built-up edge, crater wear, and chipping, whereas abrasion wear represents flank wear.Thecommonly formed wearwas crater wear. Therefore, the optimum tool life among the executed cutting trails was identified according to minimum lengthand depth of the crater wear.The profile measurements showed the formation of new geometries for the worn cutting edges due toadhesion and abrasion wear and the cutting parameters.The formation of the built-up edge was observed on the rake face of thecutting tool. The microstructure of the built-up edge was investigated using SEM. The built-up edge was found to have the austeniteshear lamellar structure which is identical to the formed shear lamellae of the produced chip.

New insights into the mechanism of low-temperature active-screen plasma nitriding of austenitic stainless steel

Low-temperature active-screen plasma nitriding is an effective surface engineering technology to improve the wear and corrosion resistance of austenitic stainless steel through the formation of expanded austenite. The material sputtered from the active screen and redeposited on the specimens has been suggested to play an important role in the nitriding mechanism involved. This paper reports a patterned deposition layer, which is in correlation with the grain orientation of polycrystalline specimens. This has provided new insights into the nitriding mechanism. © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Dry sliding wear of active screen plasma carburised austenitic stainless steel

Low temperature diffusion treatments with nitrogen and carbon have been widely used to increase the tribological performance of austenitic stainless steels. These processes produce a layer of supersaturated austenite, usually called expanded austenite or S-phase, which exhibits good corrosion and wear resistance. The novel active screen technology is said to provide benefits over the conventional DC plasma technology. The improvements result from the reduction in the electric potential applied to the treated components, and the elimination of such defects and processing instabilities as edge effects, hollow cathode effects and arcing. In this study, AISI 316 coupon samples were plasma carburised in DC and active screen plasma furnaces. The respective layers of carbon expanded austenite were characterised and their tribological performance was studied and compared. Detailed post-test examinations included SEM observations of the wear tracks and of the wear debris, EDX mapping of the wear track, EBSD crystal orientation mapping of the cross sections of the wear tracks, and cross-sectional TEM. Based on the results of wear tests and post-test examinations, the wear mechanisms involved are discussed.

Corrosion behaviour of direct current and active screen plasma carburised AISI 316 stainless steel in boiling sulphuric acid solutions

Active screen plasma is a recently developed plasma surface alloying technique, which has shown potential for addressing some drawbacks associated with conventional direct current plasma processes. In this study, the corrosion performance of untreated, direct current and active screen plasma carburised AISI 316 was investigated by immersion in a boiling solution of sulphuric acid. The experimental results show that the corrosion behaviour of expanded austenite produced by low temperature plasma carburising is controlled by the type and density of surface defects; the corrosion properties of the active screen plasma carburised material are superior to that produced by direct current plasma because of the significantly reduced edge effect and surface defects; and the bias level used in the active screen carburising treatment has a profound effect on the corrosion performance of the material. Based on the experimental results, the corrosion mechanisms involved are discussed.

Study of active screen plasma processing conditions for carburising and nitriding austenitic stainless steel

Active screen (AS) is an advanced technology for plasma surface engineering, which offers some advantages over conventional direct current (DC) plasma treatments. Such surface defects and process instabilities as arcing, edge and hollow cathode effects can be minimised or completely eliminated by the AS technique, with consequent improvements in surface quality and material properties. However, the lack of information and thorough understanding of the process mechanisms generate scepticism in industrial practitioners. In this project, AISI 316 specimens were plasma carburised and plasma nitrided at low temperature in AS and DC furnaces, and the treated samples were comparatively analysed. Two diagnostic techniques were used to study the plasma: optical fibre assisted optical emission spectroscopy, and a planar electrostatic probe. Optimum windows of treatment conditions for AS plasma nitriding and AS plasma carburising of austenitic stainless steel were identified and some evidence was obtained on the working principles of AS furnaces. These include the sputtering of material from the cathodic mesh and its deposition on the worktable, the generation of additional active species, and the electrostatic confinement of the plasma within the operative volume of the furnace.

Experimental and finite element analysis of machinability of AL-6XN super austenitic stainless steel

This paper presents a finite element cutting modelbased on physical microstructure to investigate the thermomechanicalbehaviour of AL-6XN Super AusteniticStainless Steel in the primary shear zone. Frozen chip rootsamples were created under dry turning operation to observethe plasticity behaviour occurring in the shear zones to comparewith the model for analysis. Chip samples were generatedunder cutting velocities at 65 and 94 m/min, feed rate at0.2 mm/rev and depth of cut at 1 mm. Temperature on thecutting zone was recorded by infrared thermal camera.Secondary and backscatter electron detectors were used toinvestigate the deformed microstructure and to calculate theplastic strain. Experimental results showed the formation ofmicrocracks (build-up edge triggers) at the chip root stagnationzone of both samples. The austenite phase patterns wereevident against the cutting tool tip in the stagnation zone of thechip root fabricated at 65 m/min. The movement of thesepatterns caused the formation of the slip lines within thegrains. The backscatter diffraction maps showed the formationof special grain boundaries within the slip lines, workhardeninglayer and in the chip region. Strain measurementsin the microstructures of the chip roots fabricated at 94 and65 m/min showed high values of 6.5 and 5.7 (mm/mm) respectively.The finite element model was used to measure thestress, strain, temperature and chip morphology. Numericalresults were compared to the outcomes of the experimentalwork to validate the finite element model. The model validatingprocess showed good agreement between theexperimental and numerical results, and the error values werecalculated. For a 94- and 65-m/min cutting speeds, 7.5 and5.2% were the errors in the strain, 3 and 2.5% were the error inthe temperature and 4.7 and 6.8% were the error in the shearplane angles.

Evolution of recrystallization during and following hot deformation

Recrystallization of austenite during and following hot deformation has been studied in detail in a type 304 austenitic stainless steel. Furthermore, the effect of second phase on the softening process of austenite has been investigated using a 2205 duplex stainless steel. The mechanical and microstructural features have been compared for dynamic and post deformation recrystallization.

Effect of δ-ferrite co-existence on hot deformation and recrystallization of austenite

This work evaluates the effect of co-existence of a large volume fraction of δ-ferrite on the hot deformation and dynamic recrystallization (DRX) of austenite using comparative hot torsion tests on AISI 304 austenitic and 2205 duplex stainless steels. The comparison was performed under similar deformation conditions (i.e. temperature and strain rate) and also under similar Zener-Hollomon, Z, values. The torsion data were combined with electron backscatter diffraction (EBSD) analysis to study the microstructure development. The results imply a considerable difference between DRX mechanisms, austenite grain sizes and also DRX kinetics of two steels. Whereas austenitic stainless steel shows the start of DRX at very low strains and then development of that microstructure based on the necklace structure, the DRX phenomena in the austenite phase of duplex structure does not proceed to a very high fraction. Also, the DRX kinetics in the austenitic steel are much higher than the austenite phase of the duplex steel. The results suggest that at a similar deformation condition the DRX grain size of austenitic steel is almost three times larger than the DRX grains of austenite phase in duplex steel. Similarly, the ratio of DRX grain size in the austenitic to the duplex structure at the same Z values is about 1.5.