Carbon nanotubes reinforced electrospun polymer nanofibres

With the rapid development in nanoscience and nanotechnology, there is an ever increasing demand for polymer fibres of diameters down to a nanometre scale having multiple functionalities. Electrospinning, as a simple and efficient nanofibre-making technology, has been used to produce polymer nanofibres for diverse applications. Electrospun nanofibres
based on polymer/carbon nanotube (CNT) composites are very attractive multifunctional nanomaterials because they combine the remarkable mechanical and electronic properties of CNTs and the confinement-enhanced CNTs alignment within the nanofibre structure, which could greatly improve the fibre mechanical, electrical and thermal properties. In this chapter, we summarise recent research progress on electrospun CNTs/polymer nanofibres, with an emphasis on fibre mechanical properties and structure-property attributes. Outlook towards the challenge and future directions in this field is also presented.

Properties of a carbon-fibre composite modified by electrospun poly (vinylidene fluoride)

The interlaminar toughening of a carbon-fibre reinforced composite by incorporation of electrospun polyvinylidene fluoride (PVDF) nanofibrous membranes was explored in this work. The nanofibres were electrospun directly onto commercial pre-impregnated carbon fibre materials under optimised conditions and PVDF was found to primarily crystallise in its β phase polymorphic form. There is strong evidence from DMTA analysis to suggest that a partial miscibility between the amorphous phases of the PVDF nanofibres and the epoxy exists. The improved plastic deformation at the crack tip after inclusion of the nanofibres was directly translated to a 57% increase in the mode II interlaminar fracture toughness (in-plane shear failure). Conversely, the fracture toughness in mode I (opening failure) was slightly lower than the reference by approximately 20%, and the results were interpreted from the complex micromechanisms of failure arising from the changes in polymorphism of the PVDF.

Modelling the side impact of carbon fiber tubes

Metallic tubes have been extensively studied for their crashworthiness as they closely resemble automotive crash rails. Recently, the demand to improve fuel economy and reduce vehicle emissions has led automobile manufacturers to explore the crash properties of light weight materials such as fibre reinforced polymer composites, metallic foams and sandwich structures in order to use them as crash barriers. This paper discusses the response of carbon fibre reinforced polymer (CFRP) tubes and their failure mechanisms during side impact. The energy absorption of CFRP tubes is compared to similar Aluminium tubes. The response of the CFRP tubes during impact was modelled using Abaqus finite element software with a composite fabric material model. The material inputs were given based on standard tension and compression test results and the in-plane damage was defined based on cyclic shear tests. The failure modes and energy absorption observed during the tests were well represented by the finite element model.

The indentation behaviour of carbon fibre composite tubes-experiments & modelling

Metallic tubes have been extensively studied for their crashworthiness as they closely resemble automotive crash rails. Recently, the demand to produce lighter weight, yet safer vehicles has led to the need to understand the crash behaviour of novel materials, such as fibre reinforced polymer composites, metallic foams and sandwich structures. This paper discusses the static indentation response of Carbon Fibre Reinforced Polymer (CFRP) tubes. The side impact on a CFRP tube involves various failure mechanisms. This paper highlights these mechanisms and compares the energy absorption of CFRP tubes with similar Aluminium tubes. The response of the CFRP tubes during bending was modelled using ABAQUS finite element software with a composite fabric material model. The material inputs were given based on standard tension and compression test results and the in-plane damage was defined based on cyclic shear tests. The failure modes and energy absorption observed during the tests were well represented by the finite element model.

Single-walled carbon nanotubes with DNA recognition

Two methods for attaching DNA to oxidized single-walled carbon nanotubes either in organic solvent or aqueous solution are described. The sites of DNA attachment to the nanotubes have been verified by binding gold nanoparticles modified with DNA of complementary sequence to the DNA-modified nanotubes, and imaging with TEM. The gold nanoparticles appear on the tips of the nanotubes, and at isolated positions (defects) on the sidewalls. The methods provide versatility for the modification of nanotubes with DNA for their directed assembly, or for their composites with gold nanoparticles, into nanoscale devices.

Characterisation of an out-of-autoclave resin film infusion process for textile composites

A new method to manufacture damage tolerant textile composites, which combines Resin Film Infusion with a fast and cost·efficient curing technology QuickstepTM, was investigated. The effect of process parameters on resin flow through carbon fibre preforms was analysed and model-based parameter optimisation resulted in considerable improvement of resin flow properties.

Toughening of a carbon-fibre composite using electrospun poly(Hydroxyether of Bisphenol A) nanofibrous membranes through inverse phase separation and inter-domain etherification

The interlaminar toughening of a carbon fibre reinforced composite by interleaving a thin layer (~20 microns) of poly(hydroxyether of bisphenol A) (phenoxy) nanofibres was explored in this work. Nanofibres, free of defect and averaging several hundred nanometres, were produced by electrospinning directly onto a pre-impregnated carbon fibre material (Toray G83C) at various concentrations between 0.5 wt % and 2 wt %. During curing at 150 °C, phenoxy diffuses through the epoxy resin to form a semi interpenetrating network with an inverse phase type of morphology where the epoxy became the co-continuous phase with a nodular morphology. This type of morphology improved the fracture toughness in mode I (opening failure) and mode II (in-plane shear failure) by up to 150% and 30%, respectively. Interlaminar shear stress test results showed that the interleaving did not negatively affect the effective in-plane strength of the composites. Furthermore, there was some evidence from DMTA and FT-IR analysis to suggest that inter-domain etherification between the residual epoxide groups with the pendant hydroxyl groups of the phenoxy occurred, also leading to an increase in glass transition temperature (~7.5 °C).

Practical amine functionalization of multi-walled carbon nanotubes for effective interfacial bonding

 Improved methods of functionalizing the surfaces of multi-walled carbon nanotubes (MWCNTs) have been investigated. It is shown that a level of primary amines of 2.3%, higher than previously reported for any nitrogen-containing gas plasma treatment, can be achieved using a mixture of N2 and H2, which is preferable to using NH3. Even higher levels (3.5%) of primary amines can be achieved by coating the MWCNTs with a thin layer of plasma polymerized heptylamine. In both cases, the highest levels were achieved using a combined continuous plus pulsed plasma mode which was superior to either continuous wave or pulsed wave alone. The integrity of the MWCNT structure is maintained by the plasma treatments, and the functionalized surface improves the dispersion of the MWCNTs and their interfacial bonding with epoxy, giving superior nanoindentation performance of the composites.

Glass/carbon fibre hybrid composite laminates for structural applications in automotive vehicles

Light-weight structure is one of the keys to improve the fuel efficiency and reduce the environmental buden of transport vehicles (automotive and rail). While fibreglass composites have been increasingly used to replace steel in automotive industry, the adoption rate for carbon fibre composites which are much lighter, stronger and stiffere than glass fibre composites, remains low. The main reason is the high cost of carbon fibres. To further reduce vehicle weight without excessive cost increase, one technique is to incorporate carbon fibre reinforcement into glass fibre composites and innovative design by selectively reinforcing along the main load path. Glass/carbon woven fabrics with epoxy resin matrix were utilised for preparing hybrid composite laminates. The in-plane mechanical properties such as tensile and three-point-bending flexural properties were investigated for laminates with different carbon fibre volume and lay-up scheme. It is shown that hybrid composite laminates with 50% carbon fibre reinforcement provide the best flexural properties when the carbon layers are at the exterior, while the alternating carbon/glass lay-up provides the highest compressive strength.

Objective surface evaluation of fiber reinforced polymer composites

The mechanical properties of advanced composites are essential for their structural performance, but the surface finish on exterior composite panels is of critical importance for customer satisfaction. This paper describes the application of wavelet texture analysis (WTA) to the task of automatically classifying the surface finish properties of two fiber reinforced polymer (FRP) composite construction types (clear resin and gel-coat) into three quality grades. Samples were imaged and wavelet multi-scale decomposition was used to create a visual texture representation of the sample, capturing image features at different scales and orientations. Principal components analysis was used to reduce the dimensionality of the texture feature vector, permitting successful classification of the samples using only the first principal component. This work extends and further validates the feasibility of this approach as the basis for automated non-contact classification of composite surface finish using image analysis.

Effect of manufacturing method and aging environment on painted automotive carbon fibre composite surfaces

In this paper, the effect of various aging environments on the painted surface finish of unidirectional carbon fibre composite laminates, manufactured by autoclave and a novel out-of-autoclave technique was investigated. Laminates were exposed to water immersion, 95 % relative humidity and cyclic environments for 552 h and the surface finish was evaluated using visual and wave-scan distinctness of image (DOI) techniques. It was found that the laminate surface finish was dependent on the amount of moisture in the aging test. Minor surface waviness occurred on the laminates exposed to the cyclic test, whereas, surface waviness, print through and DOI values were all significantly higher as the laminates absorbed larger quantities of moisture from the hygrothermal and hydrothermal tests. The water immersion test, which was the most detrimental to the surface finish of the painted laminates, produced dense blistering on the autoclave manufactured laminate surface whereas the out-of-autoclave laminate surface produced only a few. It was found that the out-of-autoclave laminate had high substrate surface roughness which resulted in improved paint adhesion and, therefore, prevented the formation of surface blistering with aging. © 2012 Springer Science+Business Media Dordrecht.