Reprint of: photostability of wool fabrics coated with pure and modified TiO2 colloids

The surface of wool fabrics was coated with TiO2 and TiO2-based nanocomposite colloids and the impact of this coating on the photostability of wool was investigated. TiO2 along with TiO2/Metal and TiO2/Metal/SiO2 sols were synthesized through a low-temperature sol-gel method and applied to fabrics. Composite colloids were synthesized through integrating the silica and three noble metals of silver (Ag), gold (Au) and platinum (Pt) into the synthesis process of sols. Four different molar ratios of Metal to TiO2 (0.01%, 0.1%, 0.5% and 1%) were used to elucidate the role of metal type and amount on the obtained features. Photostability and UV protection features of fabrics were evaluated through measuring the photo-induced chemiluminescence (PICL), photoyellowing rate and ultraviolet protection factor (UPF) of fabrics. PICL and photoyellowing tests were carried out under UVA and UVC light sources, respectively. PICL profiles demonstrated that the presence of pure and modified TiO2 nanoparticles on fabrics reduced the intensity of PICL peak indicating a lower amount of polymer free radicals in coated wool, compared to that of pristine fabric. Moreover, a higher PICL peak intensity as well as photoyellowing rate was observed on fabrics coated with modified colloids in comparison with pure TiO2. The surface morphology of fabrics was further characterized using FESEM images.

Titanium in biomedical applications—properties and fabrication: a review

Ti and Ti-based alloys have unique properties such as high strength, low density and excellent corrosion resistance. These properties are essential for the manufacture of lightweight and high strength components for biomedical applications. In this paper, Ti properties such as metallurgy, mechanical properties, surface modification, corrosion resistance, biocompatibility and osseointegration in biomedical applications have been discussed. This paper also analyses the advantages and disadvantages of various Ti manufacturing processes for biomedical applications such as casting, powder metallurgy, cold and hot working, machining, laser engineering net shaping (LEN), superplastic forming, forging and ring rolling. The contributions of this research are twofold, firstly scrutinizing the behaviour of Ti and Ti-based alloys in-vivo and in-vitro experiments in biomedical applications to determine the factors leading to failure, and secondly strategies to achieve desired properties essential to improving the quality of patient outcomes after receiving surgical implants. Future research will be directed toward manufacturing of Ti for medical applications by improving the production process, for example using optimal design approaches in additive manufacturing and investigating alloys containing other materials in order to obtain better medical and mechanical characteristics.

Enhanced photocatalytic activities of TiO2-SiO2 nanohybrids immobilized on cement-based materials for dye degradation

Using cement-based material as a matrix for photocatalytic hybrids is an important development for the large-scale application of photocatalytic technologies. In this work, photocatalytic activity of nanosized hybrids of TiO2/SiO2 (nano-TiO2-SiO2) for degradation of some organic dyes on cementitious materials was highlighted. For this purpose, an optimal inorganic sol-gel precursor was firstly applied to prepare the composites of nano-TiO2-SiO2 which was characterized by XRD, SEM and UV-Vis. Then, a thin layer was successfully coated on white Portland cement (WPC) blocks using a dipping process in a nano-TiO2-SiO2 solution. The effect of nano-TiO2-SiO2-coated WPC blocks on photocatalytic decomposition of three dyes, including Malachite green oxalate (MG), Methylene blue (MB) and Methyl orange (MO) were studied under UV irradiation and monitored by chemical oxygen demand tests. The results showed an increase in photocatalytic effects which depends on the structure and pH of the applied cement.