The competition between metastable and equilibrium S (Al2CuMg) phase during the decomposition of AlCuMg alloys

Abstract The decomposition sequence of the supersaturated solid solution leading to the formation of the equilibrium S (Al2CuMg) phase in AlCuMg alloys has long been the subject of ambiguity and debate. Recent high-resolution synchrotron powder diffraction experiments have shown that the decomposition sequence does involve a metastable variant of the S phase (denoted S1), which has lattice parameters that are distinctly different to those of the equilibrium S phase (denoted S2). In this paper, the difference between these two phases is resolved using high-resolution synchrotron and neutron powder diffraction and atom probe tomography, and the transformation from S1 to S2 is characterised in detail by in situ synchrotron powder diffraction. The results of these experiments confirm that there are no significant differences between the crystal structures of S1 and S2, however, the powder diffraction and atom probe measurements both indicate that the S1 phase forms with a slight deficiency in Cu. The in situ isothermal aging experiments show that S1 forms rapidly, reaching its maximum concentration in only a few minutes at high temperatures, while complete conversion to the S2 phase can take thousands of hours at low temperature. The kinetics of S phase precipitation have been quantitatively analysed for the first time and it is shown that S1 phase forms with an average activation energy of 75 kJ/mol, which is much lower than the activation energy for Cu and Mg diffusion in an Al matrix (136 kJ/mol and 131 kJ/mol, respectively). The mechanism of the replacement of S1 with the equilibrium S2 phase is discussed.

Chip formation mechanism and machinability of wrought duplex stainless steel alloys

This paper investigates the chip formation mechanism and machinability of two-phase materials, such as, wrought duplex stainless steel alloys SAF 2205 and SAF 2507. SEM and optical microscopic details of the frozen cutting zone and chips revealed that the harder austenite phase dissipates in the advancement of the cutting tool, being effectively squeezed out of the softer ferrite phase. Microhardness profiles reveal correlation in hardness from the workpiece material transitioning to the chip. The tool wear (TiAIN + TiN coated solid carbide twist drill) and machining forces were investigated. Tool wear, was dominantly due to the adhesion process which developed from built-up edge formation, is highly detrimental to the flank face. Flute damage was also observed as a major issue in the drilling of duplex alloys leading to premature tool failure. Duplex 2507 shows higher sensitivity to cutting speed during machining and strain hardening at higher velocity and less machinability due to presence of higher percentage of Ni, Mo and Cr.

Nanoscale variation in energy dissipation in austenitic shape memory alloys in ultimate loading cycles

Wavy behaviours of hysteresis energy variation in nanoscale bulk of thermomechanical austenitic NiTi shape memory alloy are reported in ultimate nanoindentation loading cycles. One sharp and two spherical tips were used while two loading-unloading rates were applied. For comparison, another austenitic copper-based shape memory alloy, CuAlNi shape memory alloy, and a metal with no phase transition, elastoplastic Cu, were investigated. In shape memory alloys, the hysteresis energy variation ultimately undergoes a linear decrease with internal wavy fluctuations and no stabilisation was observed. The internal energy fluctuation in these alloys was found dissimilar depending on the loading-unloading rate and the indentation tip geometry. In contrast, there was an absence of both overall and internal variations in hysteresis energy for Cu after the second loading cycle. The underlying physics of these variations is discussed and found to be attributed to both the created dislocations and ratcheting thermal-mechanical behaviour of the phase-transformed volume in shape memory alloys.

Precipitation processes in Al-Cu-Mg-Sn and Al-Cu-Mg-Sn-Ag

Microalloying trace elements into aluminum alloys have been shown to improve mechanical properties by altering the precipitation process. Here, trace amounts of Sn and (Sn + Ag) have been added to Al-1.1Cu-1.7Mg (at.%) and the effects have been investigated by a combination of hardness testing and transmission electron microscopy (TEM). Hardness testing shows that the addition of Sn increases the hardness throughout the ageing process, and in combination with Ag, further increases the hardness and shortens the time to reach the peak hardness. The increase in hardness via Sn microalloying is attributed to the homogeneous distribution of S phase (Al2CuMg) precipitates. In the alloy microalloyed with both Sn and Ag, the microstructure is dominated by homogeneously distributed Ω phase (Al2Cu) precipitates in the peak strengthened condition. Given that neither spherical β-Sn precipitates, nor any other obvious nucleation sites for the Ω phase precipitates were observed using TEM, the mechanism for development of such homogeneous precipitation remains to be determined.

Study of direct laser fabricated high entropy alloys

This work analysed the microstructure-property correlations and solidification behavior of high entropy alloys (based on 5 principal elements: Al,Co, Cr, Fe, Ni). The novel outcome of the work is the effect of dislocation activities, texture and phase distribution on the tension-compression asymmetry of FCC, BCC and dual phase high entropy alloys.