Photochromic wool fabrics with enhanced durability and photochromic performance

In our previous work, we have produced a photochromic wool fabric by applying a thin layer of hybrid silica-photochromic dye onto the wool surface. The coating showed a very fast optical response, but had little influence on the fabric handle, however durability was low. In this context, we reported that durability of the hybrid layer can be improved by introducing epoxy groups into the silica matrix via co-hydrolysis and co-condensation of an alkyl trialkoxysilane (ATAS) and 3-glycidoxypropyltrimethoxysilane (GPTMS). The presence of epoxy groups in the silica enhanced both washing and abrasion durabilities. Also, the optical response speed was slightly increased as well. Effects of the type of alkyl silane and the GPTMS:alkyl silane ratio on the coating durability, fabric handle and optical response were examined.

Photochromic fabrics with improved durability and photochromic performance

Previously, we have reported a method for producing photochromic wool fabric by applying a thin layer of hybrid silica-photochromic dye onto the wool surface. While the photochromic coating showed a very fast optical response and had little influence on the fabric handle, its durability was poor. In this study, the durability of the photochromic coating layer was improved by introducing epoxy groups into the silica matrix via co-hydrolysis and co-condensation of an alkyl trialkoxysilane compound (ATAS) and 3-glycidoxypropyltrimethoxysilane (GPTMS). The presence of epoxy groups in the silica enhanced both washing and abrasion durability or fastness. In addition, the optical response speed was slightly increased as well. Effects of the type of alkyl silane and the GPTMS/alkyl silane ratio on the coating durability, fabric handle and optical response were examined.

Photostability and durability properties of photochromic organosilica coating on fabric

Photochromic fabrics were prepared by a dip-coating method using a silica sol-gel solution containing photochromic dyes. The coated fabric showed a rapid photochromic response. Three methods; incorporating a UV stabilizer in the coating layer, hydrophobic treatment of the porous surface, and covering the coating layer with an additional silica layer; were used to improve the photostability and durability. All three treatments improved the photostability without noticeably changing the photochromic response/fading speeds. Most of the treatments reduced the washing and abrasion durability. The extra coating layer increased the fabric rigidity.

Photochromic wool fabrics from a hybrid silica coating

In this work, a photochromic wool fabric has been prepared by applying a photochromic-dye hybrid silica sol-gel onto the surface of fabric. The photochromic fabric was found to have a very quick optical response. Two types of silica were used as the matrix material, and the type of silica had a small effect only on the photochromic performance, the fabric washing fastness, and water contact angle, but affected the fabric handle property considerably. The silica from a precursor containing a long alkyl chain showed very little influence on the fabric handle and better photochromic performance than that containing a phenyl group.

Excellent electrochemical performance of LiFe0.4Mn0.6PO4 microspheres produced using a double carbon coating process

Composite LiFe0.4Mn0.6PO4/C microspheres are considered advanced cathode materials for electric vehicles and other high-energy density applications due to their advantages of high energy density and excellent cycling stability. LiFe0.4Mn0.6PO4/C microspheres have been produced using a double carbon coating process employing traditional industrial techniques (ball milling, spray-drying and annealing). The obtained LiFe0.4Mn0.6PO4 microspheres exhibit a high discharge capacity of around 166 mA h g-1 at 0.1 C and excellent rate capabilities of 132, 103, and 72 mA h g-1 at 5, 10, and 20 C, respectively. A reversible capacity of about 152 mA h g-1 after 500 cycles at a current density of 1 C indicates an outstanding cycling stability. The excellent electrochemical performance is attributed to the micrometer-sized spheres of double carbon-coated LiFe0.4Mn0.6PO4 nanoparticles with improved electric conductivity and higher Li ion diffusion coefficients, ensuring full redox reactions of all nanoparticles. The results show that the advanced high-energy density cathode materials can be produced using existing industry techniques.

A superamphiphobic coating with an ammonia-triggered transition to superhydrophilic and superoleophobic for oil-water separation

Superhydrophilic and superoleophobic materials are very attractive for efficient and cost-effective oil-water separation, but also very challenging to prepare. Reported herein is a new superamphiphobic coating that turns superhydrophilic and superoleophobic upon ammonia exposure. The coating is prepared from a mixture of silica nanoparticles and heptadecafluorononanoic acid-modified TiO2 sol by a facile dip-coating method. Commonly used materials, including polyester fabric and polyurethane sponge, modified with this coating show unusual capabilities for controllable filtration of an oil-water mixture and selective removal of water from bulk oil. We anticipate that this novel coating may lead to the development of advanced oil-water separation techniques.

Photochromic coloration of wool fabric

A method has been developed for producing photochromic wool fabric by applying a layer of hybrid silica containing a photochromic dye onto wool fibres. A number of different hybrid silicas were prepared by the sol-gel technique involving co-hydrolysis and co-condensation of alkyltrialkoxysilanes together with 3-glycidoxypropyltrimethoxysilane. With the dye Photorome II, it was possible to obtain a photo chromic coating which showed fast optical response. The coating had only a slight effect on the fabric handle. The durability of the coating appeared to be acceptable, at least for fashion wear.

Photochromic fabrics from hybrid silica surface coatings

In this study, hybrid silica prepared by a sol-gel technique and doped with a photochromic dye was used to produce photochromic coatings on fabric surfaces. The coated fabrics showed a strong photochromic effect with very fast optical response speed. Good coating adhesion was obtained on wool fabrics. The photostability of the photochromic fabrics was improved by three different processes: adding a photo stabilizer, adjusting the surface wettability and sealing off the dye-containing pores with additional silica coating. Four UV stabilizers were added separately to the photochromic silica coatings to investigate their influence on the photostability and photochromic behaviour. The addition of UV stabilizers retarded the photochromic response and reduced photochromic absorption, but increased photochromic lifetime. Among the four UV stabilizers studied, the quencher resulted in the best improvement to the photostability with minimal reduction in the photochromic absorption. Increasing the hydrophobicity of the coating, and sealing-off the dye-containing pores were also found to improve photostability.