Characterization of conducting polymer coated fabrics at microwave frequencies

Purpose – The purpose of this paper is to investigate microwave reflection, transmission, and complex permittivity of p-toluene-2-sulfonic acid doped conducting polypyrrole coated nylon-lycra textiles in the 1-18?GHz frequency with a view to potential applications in the interaction of electromagnetic radiation with such coated fabrics.

Design/methodology/approach – The chemical polymerization of pyrrole is achieved by an oxidant, ferric chloride and doped with p-toluene sulfonic acid (pTSA) to enhance the conductivity and improve stability. Permittivity of the conducting textile substrates is performed using a free space transmission method accompanied by a mathematical diffraction reduction method.

Findings – The real part of permittivity increases with polymerization time and dopant concentration, reaching a plateau at certain dopant concentration and polymerization time. The imaginary part of permittivity shows a frequency dependent change throughout the test range. All the samples have higher values of absorption than reflection. The total electromagnetic shielding effectiveness exceeds 80 percent for the highly pTSA doped samples coated for 3?h.

Originality/value – A non-contact, non-destructive free space method thin flexible specimens to be tested with high accuracy across large frequency range. The non-destructive nature of the experiments enables investigation of the stability of the microwave transmission, reflection, absorption and complex permittivity values. Moreover, mathematical removal of the diffraction enables higher accuracy.

Short-term heating tests on doped polypyrrole-coated polyester fabrics

Polyethyleneterephtalate–polypyrrole (PET–PPy) textile complexes incorporating different anionic dopants have been heat treated at 60 °C, 80 °C, 105 °C, 125 °C and 150 °C to investigate effects of short-term heating on conductivity and stability. In most cases heat treatments below 80 °C did not significantly change the final resistance of the conducting textiles. Only the anionic dye-dopant Indigo Carmine acted in a heat-stabilizing manner during treatment at 150 °C, while all samples containing other anionic dopant underwent some degradation. A treatment temperature of 125 °C was the most effective for lowering the final resistance, with sulphonic group containing dopants being particularly effective in improving conductivity and stability. A 29% decrease in the final resistance of a PET–PPy/para-toluene-2-sulphonic acid (pTSA) sample was achievable after 900 s at 125 °C.

The influence of polymerization time and dopant concentration on the absorption of microwave radiation in conducting polypyrrole coated textiles

Temperature changes in conducting polypyrrole/para-toluene-2-sulphonic acid (PPy/pTSA) coated nylon textiles due to microwave absorption in the 8–9 GHz and 15–16 GHz frequency ranges were obtained by a thermography station during simultaneous irradiation of the samples. The temperature values are compared and related to the amounts of reflection, transmission and absorption obtained with a non-contact free space transmission technique, indicating a relationship between microwave absorption and temperature increase. Non-conductive samples showed no temperature increase upon irradiation irrespective of frequency range. The maximum temperature difference of around 4 °C in the conducting fabrics relative to ambient temperature was observed in samples having 48% absorption and 26.5 ± 4% reflection. Samples polymerized for 60 or 120 min with a dopant concentration of 0.018 mol/l or polymerized for 180 min with a dopant concentration of 0.009 mol/l yielded optimum absorption levels. As the surface resistivity decreased and the reflection levels increased, the temperature increase upon irradiation reduced.

Reverse microemulsion-mediated synthesis of SiO2-coated ZnO composite nanoparticles : multiple cores with tunable shell thickness

Monodispersed SiO₂-shell/ZnO-core composite nanospheres have been prepared in an oil-in-water microemulsion system. By using cyclohexane as the oil phase and Triton X-100 as the surfactant, composite nanospheres with high core loading levels and tunable shell thickness were obtained. Utilization of PVP capping agent on ZnO allowed the synthesis of composite nanospheres without forming any coreless SiO2 spheres or shell-less ZnO particles. The photoactivity of ZnO nanoparticles was greatly reduced by SiO2-coating, which enables their applications as durable, safe, and nonreactive UV blockers in plastics, coating, and other products.

Superhydrophobic modification of polyimide films based on gold-coated porous silver nanostructures and self-assembled monolayers

We present a facile and effective method for controlling the surface hydrophobicity of polyimide films from sticky to superhydrophobic properties by tailoring their topographies. Nanostructured silver layers were produced on polyimide films by treatment with aqueous KOH and AgNO3, followed by thermal treatment at 200 degrees C or higher temperatures. Further modification of the gold-coated silver layers with n-dodecanethiol led to hydrophobic surfaces. Different morphologies of the silver layers at the micro- and nano-meter scales, which result in the variety of hydrophobicity, can be tailored by controlling the thermal treatment temperature. Surfaces prepared at 320 degrees C showed a sticky property that water drops did not slide off even when the sample was held upside down. Superhydrophobic surfaces were obtained when the temperature was above 340 degrees C. A remarkable superhydrophobicity, as evidenced by a very large water contact angle of 162 degrees and a very small sliding angle of 7 degrees, was achieved by heating the modified polyimide films at 360 degrees C. This is also the first example for superhydrophobic modification of polyimide films.

Endothelialisation and cell retention on gelation-chitosan coated electrospun polyurethane, poly (lactide-co-glycolide) and collagen-coated pericardium

Arterial bypass and heart valve replacements are two of the most common surgical treatments in cardiovascular surgery today. Currently, artificial materials are used as substitute for these cardiac tissues. However, these foreign materials do not have the ability to grow, repair or remodel and are thrombogenic, leading to stenosis. With the aid of tissue engineering, it is possible to develop functional identical copies of healthy heart valves and arteries, which are biocompatible. Although much effort has been made into this area, there are still inconsistencies with respect to
endothelialisation and cell retention on synthetic biological grafts. These variations may be attributed to differences in factors such as cell seeding density, incubation periods and effects of shear stress. In this study, we have compared the endothelialisation and cell retention between gelain chitosan-coated electrospun polyurethane (PU), poly (lactide co-glycolide) (PGA/PLA) and collagen-coated pericardium. Endothelial cells adhered to all of the materials as early as 1–day post seeding. After 7-day of seeding, the coverage on PU was almost 45% and that on PGA/PLA was about 25% and the least was on collagen-coated pericardium of approximately 15%. It was observed that the PU showed superior cell coverage and cell retention in comparison to the PGA/PLA and collagen-coated pericardium.

Characterization and application of conducting polymer coated textiles

This paper reports on some physical properties of a conducting polymer, polypyrrole, coated textiles. Polypyrrole was coated on textiles chemically through in-situ solution or vapor polymerisation to produce conducting textiles. The effects of the conductive coating on the physical and mechanical properties of the fibrous materials are presented. The coating durability and conductivity of the textiles have also been examined.

An investigation of polypyrrole coated conductive textiles

This research first clarified a possible chemical reaction between a dispersing dye and the conducting polymer polypyrrole. Then, the effect of acidic dyes as dopants on the colours, conductivity and thermal stability of polypyrrole were measured. Finally, the polypyrrole nanoparticles were prepared by a microemulsion polymerisation technique.

Novel conducting polymer films and coated textiles

This research developed non-hazardous methods for coating wool with conductive polymers for thermal and anti-static clothing. Conductive polymers are black in colour, thus the synthesis of new conductive polymers was required to produce coloured or fluorescent conductive textile. Cross-linked conductive polymers were also synthesised to increase their durability.

Experimental analysis of friction in forming automotive coated steels

The thesis addressed and answered a number of key issues in the experimental analysis of friction in sheet forming operations. Conventional friction theories were linked with the properties of sheet coatings and the process geometries. Newly derived mathematical models extended the analysis of friction in sheet metal forming applications.

Press forming performance of galvanneal coated steel

This project quantified the press formability of galvanneal coated steel. A coil of galvanneal coated steel was produced containing various coating structures. Using different lubricants, the powdering, friction and forming properties were determined. It was found that optimum formability was obtained by effective lubrication while galvanneal coating structure controlled powdering resistance.

Silicone coated metal oxide particles

A process for applying a silicone coating to metal oxide particles is described. The process comprises the steps of: preparing a mixture of an aqueous suspension of metal oxide particles and an aqueous solution of water-soluble organosilicon monomers; and, adding a pH-lowering agent to the mixture so as to initiate polymerisation of the water-soluble organosilicon monomers and form silicone coated metal oxide particles. The process does not require the use of an organic solvent.

PEDOT-coated counter electrodes for dye-sensitized solar cells

Poly(3,4-ethylenedioxythiophene) (PEDOT)-coated counter electrodes for dye-sensitized solar cells have been prepared at ambient temperature and without the use of iron-based oxidants, using an ionic liquid for the synthesis of the PEDOT. These electrodes show comparable electrocatalytic performance with conventional Pt-coated counter electrodes (solar cell efficiencies >7.5%).