Three-dimensional atom probe analysis of solute distribution in thermomechanically processed TRIP steels

Complex multiphase microstructures were obtained in transformation induced plasticity C–Mn–Si–(Nb–Al–Mo) steels by simulated controlled thermomechanical processing. These microstructures were characterized using transmission electron microscopy, X-ray diffraction and three-dimensional atom probe tomography (APT), which was used to determine the partitioning of elements between different phases and microconstituents. The measured carbon concentration (not, vert, similar0.25 at%) in the ferrite of carbide-free bainite was higher than expected from para-equilibrium between the austenite and ferrite, while the concentrations of substitutional elements were the same as in the parent austenite suggesting that incomplete bainite transformation occurred. In contrast, the distribution of substitutional elements between the ferrite lath and austenite in carbide-containing bainite indicated a complete bainite reaction. The average carbon content in the retained austenite (3.2 ± 1.6 at%) was somewhat higher than the T0 limit. On the basis of the APT measured composition, the calculated Ms temperatures for retained austenite were above room temperature, indicating its low chemical stability.

Effect of process variables on formation of dynamic strain induced ultrafine ferrite during hot torsion testing

Ultrafine grain sizes were produced using hot torsion testing of a 0.11C-1.68Mn-0.20Si (wt-%) steel, with ultrafine ferrite (<1 µm) nucleating intragranularly during testing by dynamic strain induced transformation. A systematic study was made of the effect of isothermal deformation temperature, strain level, strain rate, and accelerated cooling during deformation on the formation of ultrafine ferrite by this process. Decreasing the isothermal testing temperature below the Ae₃ temperature led to a greater driving force for ferrite nucleation and thus more extensive nucleation during testing; the formation of Widmanstätten ferrite prior to, or early during, deformation imposed a lower temperature limit. Increasing the strain above that where ferrite first began 0.8 at 675C and a strain rate of 3 s¯¹ increased the intragranular nucleation of ferrite. Strain rate appeared to have little effect on the amount of ferrite formed. However, slower strain rates led to extensive polygonisation of the ferrite formed because more time was available for ferrite recovery. Accelerated cooling during deformation followed by air cooling to room temperature led to a uniform microstructure consisting of very fine ferrite grains and fine spherical carbides located in the grain boundaries regions. Air cooling after isothermal testing led to carbide bands and a larger ferrite grain size.

Effect of alloying elements on the microstructure property relationship in thermomechanically processed C-Mn-Si TRIP steels

The effect of additions of Nb, Al and Mo to Fe-C-Mn-Si TRIP steel on the final microstructure and mechanical properties after simulated  thermomechanical processing (TMP) has been studied. The laboratory simulations of discontinuous cooling during TMP were performed using a hot rolling mill. All samples were characterised using optical microscopy and image analysis. The volume fraction of retained austenite was ascertained using a heat tinting technique and X-ray diffraction measurements. Room temperature mechanical properties were determined by a tensile test. From this a comprehensive understanding of the structural aspect of the bainite transformation in these types of TRIP steels has been developed. The  results have shown that the final microstructures of thermomechanically processed TRIP steels comprise 50 % of polygonal ferrite, 7 - 12 % of retained austenite, non-carbide bainitic structure and martensite. All steels exhibited a good combination of ultimate tensile strength and total elongation. The microstructure-property examination revealed the relationship between the composition of TRIP steels and their mechanical properties. It has been shown that the addition of Mo to the C-Si-Mn-Nb TRIP steel increases the ultimate tensile strength up to 1020 MPa. The stability of the retained austenite of the Nb-Mo steel was degraded, which led to a decrease in the elongation (24 %). The results have demonstrated that the addition of Al to C-Si-Mn-Nb steel leads to a good combination of strength (∼ 940 MPa) and elongation (∼ 30 %) due to the formation of refined acicular ferrite and granular bainite structure with ∼7 - 8 % of stable retained austenite. Furthermore, it has been found that the addition of Al increases the volume fraction of bainitic ferrite laths. The investigations have shown an interesting result that, in the Nb-Mo-Al steel, Al has a more pronounced effect on the microstructure in comparison with Mo. It has been found that the bainitic structure of the Nb-Mo-Al steel appears to be more granular than in the Nb-Mo steel. Moreover, the volume fraction of the retained austenite increased (12 %) with decreasing bainitic ferrite content. The results have demonstrated that this steel has the best mechanical properties (1100 MPa and 28 % elongation). It has been concluded that the combined effect of Nb, Mo, and Al addition on the dispersion of the bainite, martensite and retained austenite in the ferrite matrix and the morphology of these phases is different than effect of Nb, Mo and Al, separately.

Effect of alloying elements on the microstructure-property relationship in thermomechanically processed C-Mn-Si TRIP steels

The effect of additions of Nb, Al and Mo to Fe-C-Mn-Si TRIP steel on the final microstructure and mechanical properties after simulated thermomechanical processing (TMP) has been studied. The laboratory simulations of discontinuous cooling during TMP were performed using a hot rolling mill. All samples were characterised using optical microscopy and image analysis. The volume fraction of retained austenite was ascertained using a heat tinting technique and X-ray diffraction measurements. Room temperature mechanical properties were determined by a tensile test. From this a comprehensive understanding of the structural aspect of the bainite transformation in these types of TRIP steels has been developed. The results have shown that the final microstructures of thermomechanically processed TRIP steels comprise 50 % of polygonal ferrite, 7 - 12 % of retained austenite, non-carbide bainitic structure and martensite. All steels exhibited a good combination of ultimate tensile strength and total elongation. The microstructure-property examination revealed the relationship between the composition of TRIP steels and their mechanical properties. It has been shown that the addition of Mo to the C-Si-Mn-Nb TRIP steel increases the ultimate tensile strength up to 1020 MPa. The stability of the retained austenite of the Nb-Mo steel was degraded, which led to a decrease in the elongation (24 %). The results have demonstrated that the addition of Al to C-Si-Mn-Nb steel leads to a good combination of strength (∼ 940 MPa) and elongation (∼ 30 %) due to the formation of refined acicular ferrite and granular bainite structure with ∼7 - 8 % of stable retained austenite. Furthermore, it has been found that the addition of Al increases the volume fraction of bainitic ferrite laths. The investigations have shown an interesting result that, in the Nb-Mo-Al steel, Al has a more pronounced effect on the microstructure in comparison with Mo. It has been found that the bainitic structure of the Nb-Mo-Al steel appears to be more granular than in the Nb-Mo steel. Moreover, the volume fraction of the retained austenite increased (12 %) with decreasing bainitic ferrite content. The results have demonstrated that this steel has the best mechanical properties (1100 MPa and 28 % elongation). It has been concluded that the combined effect of Nb, Mo, and Al addition on the dispersion of the bainite, martensite and retained austenite in the ferrite matrix and the morphology of these phases is different than effect of Nb, Mo and Al, separately.

Patterned growth and cathodoluminescence of conical boron nitride nanorods

We demonstrate a simple and effective approach for growing large-scale, high-density, and well-patterned conical boron nitride nanorods. A catalyst layer of Fe(NO₃)₃ was patterned on a silicon substrate by using a copper grid as a mask. The nanorods were grown via annealing milled boron carbide powders at 1300 °C in a flow of nitrogen gas. The as-grown nanorods exhibit uniform morphology and the catalyst pattern precisely defines the position of nanorod deposition. Cathodoluminescence (CL) spectra of the nanorods show two broad emission bands centered at 3.75 and 1.85 eV. Panchromatic CL images reveal clear patterned structure

Conical boron nitride nanorods synthesized via the ball-milling and annealing method

A boron nitride (BN) nanostructure, conical BN nanorod, has been synthesized in a large quantity on Si substrates for the first time via the ball-milling and annealing method. Nitridation of milled boron carbide (B₄C) powders was performed in nitrogen gas at 1300°C on the surface of the substrates to form the BN nanorods. The highly crystallized nanorods consist of conical BN basal layers stacked along the nanorod axis. Ball milling of the B₄C powders can significantly enhance the nitridation of the powders and thus facilitate the formation of nanorods during the annealing process.

One-dimensional nanomaterials synthesized using high-energy ball milling and annealing process

One-dimensional (1D) nanomaterials including nanotubes, nanowires and nanorods have many new properties, functionalities and a large range of promising applications. A major challenge for these future industrial applications is the large-quantity production. We report that the ball milling and annealing process has the potential to achieve the mass production. Several examples including C, BN nanotubes and SiC, Zn nanowires are presented to demonstrate such capability. In addition, both size and structure of 1D nanomaterials can be controlled by varying processing conditions. New growth mechanisms involved in the process have been investigated and the high-energy ball milling has an important role in the formation of these 1D nanomaterials.

Electron backscattering diffraction analysis of an ancient wootz steel blade from central India

The electron backscattering diffraction technique was used to analyse the nature of carbides present in an ancient wootz steel blade. Bulky carbides, pro-eutectoid carbide along the prior austenite grain boundaries and fine spheroidized carbides were detected. Electron backscattering diffraction was employed to understand the texture of these carbides. The orientations of the cementite frequently occur in clusters, which points to a common origin of the members of the cluster. For the bands of coarse cementite, the origin is probably large coarse particles formed during the original cooling of the wootz cake. Pearlite formed earlier in the forging process has led to groups of similarly oriented fine cementite particles. The crystallographic texture of the cementite is sharp whereas that of the ferrite is weak. The sharp cementite textures point to the longevity of the coarse cementite throughout the repeated forging steps and to the influence of existing textured cementite on the nucleation of new cementite during cooling.

Effect of NbC and TiC precipitation on shape memory in an iron-based alloy

This paper examines the effects of TiC and NbC precipitation and prior cold rolling on the shape memory behaviour of an iron-based alloy. A precipitate-free alloy was used as a reference to investigate the relative contributions of prior-deformation and precipitation on shape memory. Heat treatment of the Nb- and Ti-containing alloys at 700 °C and 800 °C resulted in carbide precipitates between 120 nm and 220 nm in diameter. Bend testing of these samples showed a marginal increase in shape memory compared to the precipitate-free alloy. Under these conditions TiC precipitation exhibited slightly better shape memory than for NbC. However, this small increase was over-shadowed by the marked increase in shape memory that can be produced by subjecting the alloys to cold rolling followed by recovery annealing. When processed in this way, fine carbides are formed in the Ti- and Nb-containing alloys during the heat treatment. For particles >25 nm in diameter the shape memory is unaffected, but, it was found that small <5 nm particles have a detrimental effect on shape memory due to pinning of the martensite plates, thereby inhibiting their reversion to austenite. The optimum shape memory was observed in the precipitate-free alloy after cold rolling and recovery annealing.

Martensite/particle interactions and the shape memory effect in an Fe–Mn–Si-based alloy

The effect of carbide precipitates with a size range of 30–300 nm on the austenite to martensite transformation has been studied. Such particles are known to enhance shape memory, and it was the aim of this work to clarify how the particles exert a favourable effect on shape memory. Differential scanning calorimetry revealed that the presence of particles increases the amount of thermally induced martensite. X-ray diffraction showed that the presence of particles increases the amount of stress-induced martensite also. Surface-relief produced on a pre-polished surface by bending deformation showed that the particle-containing samples exhibited a more complex and highly tilted surface-relief indicative of the formation of a larger volume fraction of martensite. The reversion characteristics of the particle-containing and solution-treated samples were similar: both showed co-reversion of multiple variants of martensite within the same volume of microstructure. However, a higher volume fraction of martensite reverted for the particle-containing sample on recovery annealing. The increased density of nucleation sites for martensite formation and a higher volume fraction of stress-induced martensite for a given strain are therefore considered to be the main contributions of relatively coarse carbide particles to the improvement of shape memory performance.

Surface alloying of metals using fluid bed reactor

The use of fluidised bed reactors for surface alloying is reviewed. Research at Deakin has includes the use of chemical vapour deposition to form chromium rich layers on ferrous substrates, including stainless and tool steel grades. These layers can be modified to carbide or nitride if required by the end application. The deposition of aluminium and silicon has also been successfully achieved.

Evaluation of the thermal behaviour of bevelled cutting inserts using a numerical approach

The nose geometry of a hard and brittle metal cutting tool is generally modified in order to avoid the premature failure due to fracture under tensile stresses. While most research findings point to a favourable mechanical load pattern, the possible influence of the shape of the geometry on the thermal fields and the consequent changes in the stressed state of the tool seem to have attained less attention. The present work aims at establishing the thermal behaviour of bevelled tools under varying geometrical and process parameters. Data generated from statistically designed experiments and quick-stop chip samples are coupled to conduct numerical investigations using a mixed finite and boundary element solution to obtain the temperature distribution in bevelled carbide inserts. Due consideration is given to the presence of the stagnation zone and its size and shape. While the cutting forces and temperatures increased owing to the blunt shape of the tool, the possible absence of tensile stresses was found to be the likely effect of a more uniform temperature distribution resulting from a significant plastic contact on the principal flank and the consequent flank heat source. The characteristic low-temperature zones close to the nose of the conventional tool are taken over by the stagnation zone in bevelled tools. © IMechE 2007.

Machinability assessment and surface integrity characteristics of Austempered Ductile Iron (ADI) using ultra-hard cutting tools

The application of austempered ductile iron (ADI) is gaining an ever greater share of the worldwide ferrous product market, specifically centering on the aerospace, automotive and shipping industries. ADI is a heat treated cast iron, which exhibits remarkable mechanical properties and provides an attractive material for designers and engineers to displace conventional materials. Previous attempts, however, to machine ADI using carbide or ceramic cutting tools produced poor tool life characteristics due to the relatively poor machinability of the workpiece. This paper presents a research study that has applied the advanced technology of modern ultrahard cutting tools, in an attempt to achieve enhanced machinability performance. This performance was evaluated through the analysis of cutting forces, tool wear, surface finish and roundness.

Wear characteristics of ultra-hard cutting tools when machining austempered ductile iron

Nodularised Ductile Cast Iron, when subjected to heat treatment processes - austenitising and austempering produces Austempered Ductile Iron (ADI). The microstructure of ADI also known as "ausferrite" consists of ferrite, austenite and graphite nodules. Machining ADI using conventional techniques is often a problematic issue due to the microstructural phase transformation from austenite to martensite during machining. This paper evaluates the wear characteristics of ultra hard cutting tools when machining ADI and its effect on machinability. Machining trials consist of turning ADI (ASTMGrade3) using two sets of PCBN tools with 90% and 50% CBN content and two sets of ceramics tools; Aluminium Oxide Titanium Carbide and Silicon Carbide - whisker reinforced Ceramic. The cutting parameters chosen are categorized as roughing and finishing conditions; the roughing condition comprises of constant cutting speed (425 m/min) and depth of cut (2mm) combined with variable feed rates of 0.1, 0.2, 0.3 and 0.4mm/rev. The finishing condition comprises of constant cutting speed (700 m/min) and depth of cut (0.5mm) combined with variable feed rates of 0.1, 0.2, 0.3 and 0.4mm/rev. The benchmark condition to evaluate the performance of the cutting tools was tool wear evaluation, surface texture analysis and cutting force analysis. The paper analyses thermal softening of the workpiece by the tool and its effect on the shearing mechanism under rough and finish machining conditions in term of lower cutting forces and enhanced surface texture of the machined part.

Effect of aluminum on the corrosion resistance of low-alloy steel in 10wt% sulfuric acid solution

The aqueous corrosion behavior of low-alloy steel with aluminum contents was examined in a 10 wt% H₂SO₄ (pH 0.13) solution using electrochemical techniques and surface analyses. The corrosion resistance of the new alloy steel was evaluated in terms of electrochemical parameters, such as passive current density, film, and charge transfer resistances. The results showed that a high Al content in the steel imparted better passivation behavior resulting in a lower corrosion rate. It related to the enrichment of iron carbonate and hydrocarbon by the dissolution of the carbide phase.