Comparative study on thermodynamical and electrochemical behavior of Al88Ni6La6 and Al86Ni6La6Cu2 amorphous alloys

Two amorphous ribbons with the compositions of Al₈₈Ni₆La₆ and Al₈₆Ni₆La₆Cu₂ were made using the meltspun method, and their thermal response and electrochemical behavior were studied comparatively. Differential scanning calorimetry (DSC) and electrochemical polarization measurements indicated that Al₈₆Ni₆La₆Cu₂ exhibited slightly higher crystallization temperature (T_x), lower melting point (T₁) and better corrosion resistance in 0.01 mol · L⁻¹ NaCl alkaline solution. These results demonstrated that Cu (2%) addition could slightly promote the glass forming ability, but it could greatly improve the corrosion resistance of Al₈₈Ni₆La₆ alloy in 0.01 mol · L⁻¹ NaCl alkaline solution.

The microstructure evolution and mechanical properties of cryorolled Al alloys

A solutionized Al2024 alloy was subjected to rolling at liquid nitrogen temperature (cryorolling) resulting in an ultra-fine stmcture. The material was also subjected to recovery annealing at 160°C. The ultrafine structured material demonstrated increased strength but very low ductility. The uniform elongation of the material after recovery annealing increased without any sacrifice of strength.

Method for determining reaction rate of mild steel containers during melting of magnesium-aluminium alloys and effect of aluminium content on directionally solidified microstructures

A magnesium alloy of eutectic composition (33 wt-'%Al) was directionally solidified in mild steel tubes at two growth rates, 32 and 580 mum s(-1,) in a temperature gradient between 10 and 20 K mm(-1). After directional solidification, the composition of each specimen varied dramatically, from 32'%Al in the region that had remained solid to 18%Al (32 mum s(-1) specimen) and 13%Al (580 mum s(-1) specimen) at the plane that had been quenched from the eutectic temperature. As the aluminium content decreased, the microstructure contained an increasing volume fraction of primary magnesium dendrites and the eutectic morphology gradually changed from lamellar to partially divorced. The reduction in aluminium content was caused by the growth of an Al-Fe phase ahead of the Mg-Al growth front. Most of the growth of the Al-Fe phase occurred during the remelting period before directional solidification. The thickness of the Al-Fe phase increased with increased temperature and time of contact with the molten Mg-Al alloy. (C) 2003 Maney Publishing.

Twinning and the ductility of magnesium alloys Part I: “Tension” twins

Magnesium and its alloys do not in general undergo the same extended range of plasticity as their competitor structural metals. The present work is part I of a study that examines some of the roles deformation twinning might play in the phenomenon. A series of tensile test results are reported for the common wrought alloy AZ31. These data are employed in conjunction with a simple constitutive model to argue that View the MathML source twinning (which gives extension along the c-axis) can increase the uniform elongation in tensile tests. This effect appears to be similar to that seen in Ti, Zr and Cu–Si and in the so called TWIP phenomenon in steel.

A criterion for conventional dynamic recrystallization: Application to magnesium alloys

An analytical approximation for the steady state dynamic recrystallized grain size is combined with a simple nucleation criterion to assess the propensity for dynamic recrystallization. In line with observation, the criterion predicts dynamic recrystallization in 99.9995% pure Al but not in material 99.5% pure. It also agrees with the observation that zone refined ferrite can display dynamic recrystallization at high temperatures and low strain rates but not at lower hot working temperatures. The criterion is applied here to common wrought magnesium alloys to argue that conventional dynamic recrystallization is expected under "normal" hot working conditions.

Solidification of cast magnesium alloys

A description of the key solidification steps in the formation of the as-cast microstructure of magnesium alloys is presented. The focus is on the two common magnesium alloy groups: Mg-Al alloys and Mg-Zn-rare earth alloys. The key elements described are: nucleation (including grain refinement), growth of the primary phase and the formation of the eutectic phases. In addition the effect of casting process (e.g. high-pressure diecasting and sand casting) on the outcomes from solidification are discussed. This includes consideration of the formation of banded defects during solidification in the dynamic environment of high pressure die casting.