Experimental study of strain fields during shearing of medium and high-strength steel sheet

There is a shortage of experimentally determined strains during sheet metal shearing. These kinds of data are a requisite to validate shearing models and to simulate the shearing process. In this work, strain fields were continuously measured during shearing of a medium and a high strength steel sheet, using digital image correlation. Preliminary studies based on finite element simulations, suggested that the effective surface strains are a good approximation of the bulk strains below the surface. The experiments were performed in a symmetric set-up with large stiffness and stable tool clearances, using various combinations of tool clearance and clamping configuration. Due to large deformations, strains were measured from images captured in a series of steps from shearing start to final fracture. Both the Cauchy and Hencky strain measures were considered, but the difference between these were found negligible with the number of increments used (about 20 to 50). Force-displacement curves were also determined for the various experimental conditions. The measured strain fields displayed a thin band of large strain between the tool edges. Shearing with two clamps resulted in a symmetric strain band whereas there was an extended area with large strains around the tool at the unclamped side when shearing with one clamp. Furthermore, one or two cracks were visible on most of the samples close to the tool edges well before final fracture. The fracture strain was larger for the medium strength material compared with the high-strength material and increased with increasing clearance.

3D roll-forming of hat-profile with variable depth and width

The use of roll-formed products in automotive, furniture, buildings etc. increases every year due to the low part-production cost and the complicated cross-sections that can be produced. The limitation with roll-forming until recent years is that one could only produce profiles with a constant cross-section in the longitudinal direction. About eight years ago ORTIC AB [1] developed a machine in which it was possible to produce profiles with a variable width (“3D roll-forming”) for the building industry. Experimental equipment was recently built for research and prototyping of profiles with variable cross-section in both width and depth for the automotive industry. The objective with the current study is to investigate the new tooling concept that makes it possible to roll-form hat-profiles, made of ultra high strength steel, with variable cross-section in depth and width. The result shows that it is possible to produce 3D roll-formed profiles with close tolerances.

Evaluation of galling resistance for some selected combinations of tool steels/stainless steel sheet materials/lubricants using pin-on-disc testing

Stainless steels are well known to be prone to cold welding and material transfer in sliding contacts and therefore difficult to cold form unless certain precautions as discussed in this paper are taken. In the present study different combinations of tool steels/stainless steels/lubricants has been evaluated with respect to their galling resistance using pin-on-disc testing. The results show that a high galling resistance is favored by a high stainless steel sheet hardness and a blasted stainless steel sheet surface topography. The effect of type of lubricant was found to be more complex. For example, the chlorinated lubricants failed to prevent metal-to-metal contact on a brushed sheet surface but succeeded on a blasted sheet surface of the same stainless steel material. This is believed to be due to a protective tribofilm which is able to form on the blasted surface, but not on the brushed surface.

Evolution of artificial defects during shape rolling

Very often defects are present in rolled products. For wire rods, defects are very deleterious since the wire rods are generally used directly in various applications. For this reason, the market nowadays requires wire rods to be completely defect-free. Any wire with defects must be rejected as scrap which is very costly for the production mill. Thus, it is very important to study the formation and evolution of defects during wire rod rolling in order to better understand and minimize the problem, at the same time improving quality of the wire rods and reducing production costs. The present work is focused on the evolution of artificial defects during rolling. Longitudinal surface defects are studied during shape rolling of an AISI M2 high speed steel and a longitudinal central inner defect is studied in an AISI 304L austenitic stainless steel during ultra-high-speed wire rod rolling. Experimental studies are carried out by rolling short rods prepared with arteficial defects. The evolution of the defects is characterised and compared to numerical analyses. The comparison shows that surface defects generally reduce quicker in the experiments than predicted by the simulations whereas a good agreement is generally obtained for the central defect.

An investigation of worn work roll materials used in the finishing stands of the hot strip mill for steel rolling

The surface failure characteristics of different work roll materials, i.e. High Speed Steel, High Chromium Iron and Indefinite Chill Iron, used in the finishing stands of a hot strip mill have been investigated using stereo microscopy, 3D optical profilometry, scanning electron microscopy and energy dispersive X-ray spectroscopy. The results show that the surface failure mechanisms of work rolls for hot rolling are very complex, involving plastic deformation, abrasive wear, adhesive wear, mechanical and thermal induced cracking, material transfer and oxidation. Despite the differences in chemical composition and microstructure, the tribological response of the different work roll materials was found to be strongly dependent on the material microstructure and especially the presence and distribution of microstructural constituents, such as the different carbide phases and graphite (in the case of Indefinite Chill Iron). Cracking and chipping of the work roll surfaces, both having a negative impact on work roll wear, are strongly influenced by the presence of carbides, carbide networks and graphite in the work roll surface. Consequently, the amount of carbide forming elements as well as the manufacturing process must be controlled in order to obtain an optimised microstructure and a predictable wear rate.