Behaviour of Surface Defects in Wire Rod Rolling

Defects are often present in rolled products, such as wire rod. The markets demand for wire rod without any defects has increased. In the final wire rod products, defects originating from the steel making, casting, pre-rolling of billets and during the wire rod rolling can appear. In this work, artificial V-shaped longitudinal surface cracks has been analysed experimentally and by means of FEM. The results indicate that the experiments and FEM calculations show the same tendency except in two cases, where instability due to a fairly “round” false round bars disturbed the experiment. FE studies in combination with practical experiments are necessary in order to understand the behaviour of the material flows in the groove and to explain whether the crack will open up as a V-shape or if it will be closed as an I-shape.

Evolution of artificial defects during shape rolling

Very often defects are present in rolled products. For wire rods, defects are very deleterious since the wire rods are generally used directly in various applications. For this reason, the market nowadays requires wire rods to be completely defect-free. Any wire with defects must be rejected as scrap which is very costly for the production mill. Thus, it is very important to study the formation and evolution of defects during wire rod rolling in order to better understand and minimize the problem, at the same time improving quality of the wire rods and reducing production costs. The present work is focused on the evolution of artificial defects during rolling. Longitudinal surface defects are studied during shape rolling of an AISI M2 high speed steel and a longitudinal central inner defect is studied in an AISI 304L austenitic stainless steel during ultra-high-speed wire rod rolling. Experimental studies are carried out by rolling short rods prepared with arteficial defects. The evolution of the defects is characterised and compared to numerical analyses. The comparison shows that surface defects generally reduce quicker in the experiments than predicted by the simulations whereas a good agreement is generally obtained for the central defect.

Influence of grinding operations on surface integrity and chloride induced stress corrosion cracking of stainless steels

Stainless steels were developed in the early 20th century and are used where both the mechanical properties of steels and corrosion resistance are required. There is continuous research to allow stainless steel components to be produced in a more economical way and be used in more harsh environments. A necessary component in this effort is to correlate the service performance with the production processes. The central theme of this thesis is the mechanical grinding process.  This is commonly used for producing stainless steel components, and results in varied surface properties that will strongly affect their service life. The influence of grinding parameters including abrasive grit size, machine power and grinding lubricant were studied for 304L austenitic stainless steel (Paper II) and 2304 duplex stainless steel (Paper I). Surface integrity was proved to vary significantly with different grinding parameters. Abrasive grit size was found to have the largest influence. Surface defects (deep grooves, smearing, adhesive/cold welding chips and indentations), a highly deformed surface layer up to a few microns in thickness and the generation of high level tensile residual stresses in the surface layer along the grinding direction were observed as the main types of damage when grinding stainless steels. A large degree of residual stress anisotropy is interpreted as being due to mechanical effects dominating over thermal effects. The effect of grinding on stress corrosion cracking behaviour of 304L austenitic stainless steel in a chloride environment was also investigated (Paper III). Depending on the surface conditions, the actual loading by four-point bend was found to deviate from the calculated value using the formula according to ASTM G39 by different amounts. Grinding-induced surface tensile residual stress was suggested as the main factor to cause micro-cracks initiation on the ground surfaces. Grinding along the loading direction was proved to increase the susceptibility to chloride-induced SCC, while grinding perpendicular to the loading direction improved SCC resistance. The knowledge obtained from this work can provide a reference for choosing appropriate grinding parameters when fabricating stainless steel components; and can also be used to help understanding the failure mechanism of ground stainless steel components during service.

Induktiv provning av ferritiskt rostfritt stå

The report examines the factors which may be a contributing cause to the problems that are present when ferritic stainless steel are eddy current tested in a warm condition. The work is carried out at Fagersta Stainless AB in Fagersta which manufactures stainless steel wire. In the rolling mill there is an eddy current equipment for detection of surface defects on the wire. The ferritic stainless steels cause a noise when testing and this noise complicates the detection of defects.Because of this, a study was made of how the noise related to factors such as steel grade, temperature, size and velocity. By observing the signal and with the possibilities to change the equipment settings the capability to let a signal filter reduce the noise level were evaluated. Theories about the material's physical properties have also been included, mainly the magnetic properties, electrical conductivity and the material's tendency to oxidize.Results from the tests show that a number of factors do not affect the inductive test significantly and to use a filter to reduce the noise level does not seem to be a viable option. The level of noise does not relate to the presence of superficial particles in form of oxides.The ferritic stainless steels showed some difference in noise level. Which noise level there was did match well with the steels probability for a precipitation of a second phase, and precipitation of austenite may in this case contribute to noise when using an eddy current instrument.The noise is probably due to some physical material property that varies within the thread.