A study of slag corrosion of oxides and oxide-carbon refractories during steel refining

The use of ceramic material as refractories in the manufacturing industry is a common practice worldwide. During usage, for example in the production of steel, these materials do experience severe working conditions including high temperatures, low pressures and corrosive environments. This results in lowered service lives and high consumptions of these materials. This, in turn, affects the productivity of the whole steel plant and thereby the cost. In order to investigate how the service life can be improved, studies have been carried out for refractories used in the inner lining of the steel ladles. More specifically, from the slag zone, where the corrosion is most severe. By combining thermodynamic simulations, plant trails and post-mortem studies of the refractories after service, vital information about the behaviour of the slagline refractories during steel refining and the causes of the accelerated wear in this ladle area has been achieved. The results from these studies show that the wear of the slagline refractories of the ladle is initiated at the preheating station, through reduction-oxidation reactions. The degree of the decarburization process is mostly dependent on the preheating fuel or the environment. For refractories without antioxidants, refractory decarburization is slower when coal gas is used in ladle preheating than when a mixture of oil and air is used. In addition, ladle preheating of the refractories without antioxidants leads to direct wear of the slagline refractories. This is due to the total loss of the matrix strength, which results in a sand-like product. Thermal chemical changes that take place in the slagline refractories are due to the MgO-C reaction as well as the formation of liquid phases from impurity oxides. In addition, the decrease in the system pressure during steel refining makes the MgO-C reaction take place at the steel refining temperatures. This reduces the refractory’s resistance to corrosion. This is a serious problem for both the magnesia-carbon and dolomite-carbon refractories. The studies of the reactions between the slagline refractories and the different slag compositions showed that slags rich in iron oxide lead mostly to the oxidation of carbon/graphite in the carbon-containing refractories. This leads to an increased porosity and wettability and therefore an enhanced penetration of slag into the refractory structure. If the slag contains high contents of alumina and or silica (such as the steel refining slag), reactions between the slag components and the dolomite-carbon refractory are promoted. This leads to the formation of low-temperature melting phases such as calcium-aluminates and silicates. The state of these reaction products during steel refining leads to an accelerated wear of the dolomite-carbon refractory. The main products of the reactions between the magnesia-carbon refractory and the steel refining slag are MgAl2O4 spinels, and calcium-aluminates, and silicates. Due to the good refractory properties of MgAl2O4 spinels, the slag corrosion resistance of the magnesiacarbon refractory is promoted.

English-medium instruction in Sweden : Perspectives and practices in two upper secondary schools

This thesis presents English-medium instruction (EMI) in the Swedish context, focusing on perspectives and practices in two schools. The research question is as follows: How and why is EMI offered, chosen, and practiced in the Swedish upper secondary school today? The aim is to explore the status of the educational option, the reasons for offering EMI to stakeholders, the stakeholders’ beliefs about and goals of EMI, and the implementation of EMI in the classroom. A survey of all upper secondary schools in Sweden was conducted to ascertain the spread of content teaching through a foreign language. The educational context was studied from an ecological perspective using methods based in linguistic ethnography. Language alternation, academic language, and language hierarchy were all considered. Interviews were analysed for content; and classroom language use was analysed for language choice and function. The concepts of affordance and scaffolding together with translanguaging were key. The de facto policies of the micro contexts of the schools were examined in light of the declared national policy of the macro context of Sweden. The results indicate that the option in Swedish schools has not increased, and also tends to only be EMI—not Content and Language Integrated Learning (CLIL) or instruction through other languages. EMI is offered for prestige, an international profile, marketing potential and personal interest. EMI students are academically motivated and confident, and see the option as “fun”. 100% EMI in the lessons is not the goal or the practice. Translanguaging is abundant, but how language alternation is perceived as an affordance or not differs in the two schools. One focuses on how the languages are used while the other focuses on how much each language is used. In conclusion, the analysis suggests that a development of definitions and practices of EMI in Sweden is needed, especially in relation to language policy and language hierarchy.