Mässingslegeringar med låg blyhalt för svarvade komponenter ämnade för dricksvatten

This thesis is about brass alloys with low lead levels for manufacturing of turned components destined for human consumption. Is it technically possible, economically viable and environmentally necessary to produce lead-free brass alloys? Turning tests and leaching tests has been carried out in low-lead brass. The result of the tests carried out show that it is technically possible to produce faucets in low-leaded brass, but since these alloys are harder and less ductile, it takes more power and more cooling when it is processed. There should be more reality-based tests in regular machines that belong in the line of manufacturing. Tests is needed to find out which tool materials, cutting angles, cooling, etc. which are needed to manufacture products with the right surface, dimensions, durability, etc. One thing that no one knows today is the lifetime of a faucet made of low-lead brass. If these faucet’s do not have a higher life than that made in CW 602 N, it is a major strain on nature to produce these in low-lead brass, then to maintain production of the faucets as it is today. No information has come from the Boverket of tougher requirements for lead content in brass. This makes it difficult to know how much effort that is needed to replace lead. A legal requirement or to lose market areas is otherwise a good motivation to move forward.

Evaluation of galling resistance for some selected combinations of tool steels/stainless steel sheet materials/lubricants using pin-on-disc testing

Stainless steels are well known to be prone to cold welding and material transfer in sliding contacts and therefore difficult to cold form unless certain precautions as discussed in this paper are taken. In the present study different combinations of tool steels/stainless steels/lubricants has been evaluated with respect to their galling resistance using pin-on-disc testing. The results show that a high galling resistance is favored by a high stainless steel sheet hardness and a blasted stainless steel sheet surface topography. The effect of type of lubricant was found to be more complex. For example, the chlorinated lubricants failed to prevent metal-to-metal contact on a brushed sheet surface but succeeded on a blasted sheet surface of the same stainless steel material. This is believed to be due to a protective tribofilm which is able to form on the blasted surface, but not on the brushed surface.

Wear of coated and uncoated PCBN cutting tool used in turning and milling

This licentiate thesis has the main focus on evaluation of the wear of coated and uncoated polycrystalline cubic boron nitride cutting tool used in cutting operations against hardened steel. And to exam the surface finish and integrity of the work material used. Harder work material, higher cutting speed and cost reductions result in the development of harder and more wear resistance cutting tools. Although PCBN cutting tools have been used in over 30 years, little work have been done on PVD coated PCBN cutting tools. Therefore hard turning and hard milling experiments with PVD coated and uncoated cutting tools have been performed and evaluated. The coatings used in the present study are TiSiN and TiAlN. The wear scar and surface integrity have been examined with help of several different characterization techniques, for example scanning electron microscopy and Auger electron spectroscopy.   The results showed that the PCBN cutting tools used displayed crater wear, flank wear and edge micro chipping. While the influence of the coating on the crater and flank wear was very small and the coating showed a high tendency to spalling. Scratch testing of coated PCBN showed that, the TiAlN coating resulted in major adhesive fractures. This displays the importance of understanding the effect of different types of lapping/grinding processes in the pre-treatment of hard and super hard substrate materials and the amount and type of damage that they can create. For the cutting tools used in turning, patches of a adhered layer, mainly consisting of FexOy were shown at both the crater and flank. And for the cutting tools used in milling a tribofilm consisting of SixOy covered the crater. A combination of tribochemical reactions, adhesive wear and mild abrasive wear is believed to control the flank and crater wear of the PCBN cutting tools. On a microscopic scale the difference phases of the PCBN cutting tool used in turning showed different wear characteristics. The machined surface of the work material showed a smooth surface with a Ra-value in the range of 100-200 nm for the turned surface and 100-150 nm for the milled surface. With increasing crater and flank wear in combination with edge chipping the machined surface becomes rougher and showed a higher Ra-value. For the cutting tools used in milling the tendency to micro edge chipping was significant higher when milling the tools steels showing a higher hard phase content and a lower heat conductivity resulting in higher mechanical and thermal stresses at the cutting edge.