Influence of hardwood, softwoodand fractionated pulp in a stratifiedthree-layered fine paper : Lövved, barrved och fraktionerad massa ochdess inverkan på ett treskiktat finpapper

Four different trials of stratified three-layered fine paper, of sulphate pulp, were performed to investigate if stratified fine fraction or fibres from birch can improve the properties of a paper compared to a reference sheet. All trials had five different scenarios and each scenario was calendered with different linear load. All sheets had a grammage of 80 g/m2.In the first trial, the paper contained birch, pine and filler of calciumcarbonate (marble), and was manufactured with the pilot paper machine XPM and the stratified headbox Formator at RCF (Stora Enso Research Center in Falun). The furnish consisted of 75% birch and 25% pine.The second trial contained coated sheets with paper from trial one as the base paper. The coating slip contained calciumcarbonate and clay and the amount was approximately 10-12 g/m2.The third trial, also with birch and pine but without filler, was performed at STFI (Skogsindustrins Tekniska Forskningsinstitut in Stockholm) with the laboratory scaled paper machine StratEx and the stratified headbox AQ-vanes. The furnish consisted of 75% birch and 25% pine, except for one scenario which contained of 75% pine and 25% birch.The last trial contained fractionated pulp of birch and pine and was performed at STFI. 50% was fine fraction and 50% was coarse fraction.This test does not show any clear benefits of making stratified sheets of birch and pine when it comes to properties such as bending stiffness, tensile index and surface smoothness. The retention can be improved with birch in the surface plies. It is possible that the formation can be improved with birch in the surface plies and pine in the middle ply. It is also possible that fine fraction in the surface plies and coarse fraction in the middle ply can improve both surface smoothness and bending stiffness. The results in this test are shown with confidence intervals which points out the difficulties of analysing sheets manufactured with a pilot paper machine or a laboratory scaled paper machine.

Undersökning av steady state och utvärdering av valskraft och friktion vid kallvalsning av aluminium

The purpose with this thesis was to examine the cold rolling mill located at Högskolan Dalarna and to stabilize the rolling process, to achieve steady state. Experiments with cold rolling of an aluminium strip have given results for rolling force, friction, reduction, strip tension and strain hardening. Results show that steady state has been found for the experiments with roll force and strain hardening, and not been found for the experiments with friction and reduction. Results show that increased strip tension gives lower roll forces. The roll force equation of Stone shows comparable results with reality for dry contact with reductions up to 30 %, but starts being incomparable with higher reductions. The roll force equation of Stone shows a bit higher roll forces than reality gave, but was comparable within reductions from 13 to 50 %. Experiments have shown that the aluminium strip has gone through strain hardening. Experiments show how the set roll gap did not yield the desired thickness reduction, there for the elastic spring constant for the rolling mill was examined and determined to be 417 N / mm for the specific alloy band. The influence of tension strip for roll force was examined and Results confirm the theory about how the roll force is decreased by increasing tension strip. The work rolls started to slip against the alumina strip as high tension strip; 70 N/mm2, gave low roll force; < 15kN.