The first preparation of beta-lactones by radical cyclization

beta-Lactones have, for the first time, been prepared by 4-exo-trig radical cyclization. Thus, alpha-ethenoyloxy radicals react in the presence of tributylstannane in a photothermal process to give beta-lactones. Highest yields were obtained when groups capable of stabilizing a carboncentered radical were present at the 3-position of the alkenoate acceptor.

Viability of Salmonella enterica subsp. enterica during the preparation and cold storage of Egyptian soft cheeses and ice-cream

Changes occurring in the viability of Salmonella enterica subsp. enterica during the preparation and cold storage of Domiati cheese, Kariesh cheese and ice-cream were examined. A significant decrease in numbers was observed after whey drainage during the manufacture of Domiati cheese, but Salmonella remained viable for 13 weeks in cheeses prepared from milks with between 60 and 100 g/L NaCl; the viability declined in Domiati cheese made from highly salted milk during the later stages of storage. The method of coagulation used in the preparation of Kariesh cheese affected the survival time of the pathogen, and it varied from 2 to 3 weeks in cheeses made with a slow-acid coagulation method to 4-5 weeks for an acid-rennet coagulation method. This difference was attributed to the higher salt-in-moisture levels and lower pH values of Kariesh cheese prepared by the slow-acid coagulation method. A slight decrease in the numbers of Salmonella resulted from ageing ice-cream mix for 24 h at 0degreesC, but a greater reduction was evident after one day of frozen storage at -20degreesC. The pathogen survived further frozen storage for four months without any substantial change in numbers.

Preparation and magnetic properties of La–Mn and La–Co doped barium hexaferrites prepared via an improved co-precipitation/molten salt method

LaMn and LaCo doped barium hexaferrites of formula Ba(1-x)LaxFe(12-x)MxO19 (M=Mn, Co) (x=0.05 to 0.40) were prepared with an improved co-precipitation/molten salt method. For the synthesis, aqueous solutions of the appropriate metal chlorides were prepared in the ratio required except that the initial mole ratio of Fe and dopants to Ba was chosen to be 11:1, and then mixed with excess Na2CO3. The solutions were then cooled, filtered off, dried, then mixed with KCl flux, and heated at 450 degrees C and for 2 h. The temperature was then raised to 950 degrees C and kept for 4 h, then cooled. This new synthesis method, which employs a lower temperature and shorter reaction time, gives products with improved crystallinity and purity while the saturation magnetization and coercivity values are comparable with those synthesized via the high temperature method.

Efficiency and purity control in the preparation of pure and/or aluminum-doped barium ferrites by hydrothermal methods using ferrous ions as reactants

The synthesis of hexagonal barium ferrite (BaFe12O19) was studied under hydrothermal conditions by a method in which a significant amount of ferrous chloride was introduced along side ferric chloride among the starting materials. Though all of the Fe2+ ions in the starting material were converted to Fe3+ ions in the final product, Fe2+ was confirmed to participate differently from the Fe3+ used in the conventional method in the mechanism of forming barium ferrite. Indeed the efficiency of the synthesis and the quality of the product and the lack of impurities such as Fe2O3 and BaFe2O4 were improved when Fe2+ was included. However, the amount of ferrous ions that could be included to obtain the desired product was limited with an optimum ratio of 2:8 for FeCl2/FeCl3 when only 2h of reaction time were needed. It was also found that the role of trivalent Fe3+ could be successfully replaced by Al3+. Up to 50% of their on could be replaced by Al3+ in the reactants to produce Al- doped products. It was also found that the ratio of Fe2+/M3+ could be increased in the presence of Al3+ to produce high quality barium ferrite.

Preparation and magnetic properties of barium ferrites substituted with manganese, cobalt, and tin

Barium ferrites substituted by Mn–Sn, Co–Sn, and Mn–Co–Sn with general formulae BaFe12−2xMnxSnxO19 (x=0.2–1.0), BaFe12−2xCoxSnxO19 (x=0.2–0.8), and BaFe12−2xCox/2Mnx/2SnxO19 (x=0.1–0.6), respectively, have been prepared by a previously reported co-precipitation method. The efficiency of the method was refined by lowering the reaction temperature and shortening the required reaction time, due to which crystallinity improved and the value of saturated magnetization increased as well. Low coercivity temperature coefficients, which are adjustable by doping, were achieved by Mn–Sn and Mn–Co–Sn doping. Synthesis efficiency and the effect of doping are discussed taking into account accumulated data concerning the synthesis and crystal structure of ferrites.